High Manganese Austenitic Steels for Cryogenic Applications

요약:

Martensitic high nitrogen stainless steels are particularly interesting because they typically exhibit high strength and ductility, good corrosion resistance and reduced grain boundary sensitization.
Nitrogen, when used as an additive in stainless steels can increase the austenitic phase range, decrease the formation of unwanted ferrite and at the same time help refine carbide to enhance strength.

As the name suggests, high-Mn steels are based on alloying Fe with a large amount of Mn (≥12 wt%). This makes the Fe-Mn equilibrium phase diagram an excellent starting point to understand their behavior. Figure 1 presents the equilibrium phase diagram of the Fe-Mn system. As can be seen, increasing Mn content significantly expands the austenite (γ) phase field. High temperature ferrite (δ) formation is suppressed by an addition of approximately 12-13 wt% Mn, indicating that alloys with this amount of manganese or more will exhibit fully austenitic solidification from high temperature. Another feature of interest in the Fe-Mn system is that the two phase region separating liquid (L) and austenite (γ) is quite narrow, suggesting that Mn does not segregate strongly during solidification. Estimating the partition ratio from the diagram itself gives a value of approximately 0.75. Although slightly outside of the data presented in Figure 1, a eutectoid reaction exists in the system at 255°C and 43 wt% Mn; γ→αFe+αMn. From a practical standpoint, the high-Mn alloys which are discussed here would not demonstrate any low temperature ferrite (αFe) formation during typical cooling conditions because of limited diffusion rates.



Figure 1: Fe-Mn equilibrium phase diagram

High manganese austenitic steels have been widely studied for their corresponding outstanding tensile strength and ductility. Certain high Mn austenitic steels have also been investigated for cryogenic applications. Koyama et al. studied the effects of temperature on the tensile properties of Fe-17Mn-0.6C steels and discovered that the uniform tensile elongation deteriorated as the deformation temperature decreased from room temperature to −100°C. The lower ductility was attributed to an increase in the amount of ε-martensite plates. This suggestion was supported by the observation that an addition of elements such as carbon, which suppressed the formation of ε-martensite, improved the cryogenic tensile ductility.

Therefore, it has been suggested that the reduction number of ε-martensite plates is a key factor for the cryogenic tensile ductility improvement of high Mn steels. One way for the number of ε-martensite plates to be suppressed is through austenite grain size refinement. Takaki et al. investigated the grain size effects on ε-martensite formation in Fe-15Mn alloys and discovered that when the grain size was below 10 µm, the ε-martensite transformation was almost suppressed. In a quite recent study, it was demonstrated that Fe-17Mn-0.6C alloys with coarse grain sizes (10–37 µm) demonstrated a brittle fracture at −150°C due to ε-martensite formation. In contrast, this embrittlement was suppressed by grain refinement to 3.5 µm. The formation of ε-martensite could also be suppressed by an increase in the Mn content. Tomota et al. demonstrated that, regarding the binary Fe-Mn system, when the Mn content was increased to 36%, no ε-martensite was observed in the tensile tested samples at room temperature, whereas only 4.2% of ε-martensite was formed following tensile deformation to a strain value exceeding 60% at the liquid nitrogen temperature. Fe-34.5Mn-0.04C steels are recently developed steels with potential applications at low temperatures.

Among 9% nickel steel, austenitic steel, aluminium alloy and austenitic Fe-Ni alloy that are materials applicable to LNG tanks, the three except for 9% nickel steel have a FCC crystal structure. Metallic materials with FCC structure do not show the property of ductile-brittle transition unlike those with common Body-Centered Cubic (BCC) structure. Thus, they maintain high toughness also at cryogenic temperatures. An exception is the 9% nickel steel, which has the residual FCC structure with a basis of Body-Centered Tetragonal (BCT) structure due to a special heating process that ensures toughness at cryogenic temperatures.

Alloy steel with FCC crystal structure is referred to as austenitic steel. Types of austenitic steel are nickel-based austenitic stainless steel such as types 304, 304L, 316, 316L, 321 and 347. Since the 1970s, comprehensive studies on austenitic steel for cryogenic applications based on manganese have been actively carried out. Recently, high manganese austenitic steel for cryogenic service (hereinafter referred to as “high Mn steel”) has been developed as an alternative that overcomes the disadvantage of FCC-structured metallic materials, namely low yield strength, and leverages the economic feasibility of manganese. Chemical composition of high Mn steel is registered in Korean industrial standards (KS-D-3031) as follows:



Table 1: Chemical compositions of high Mn steel (wt%)

Mechanical properties of high Mn steel were tested in accordance with international standard procedures as seen in Table 2. They were clarified through a comparison with other materials used for LNG tanks shown in Table 3. Particularly, Type 304 was chosen to represent austenitic stainless steel.



Table 2: Mechanical test items for high Mn steel



Table 3: Specifications of 5 different cryogenic materials

In Figure 1(a) is showed, yield strength of high Mn steel. As can be seen the yield stress is between those of Type 304 (equivalent to STS 304 in Korean Standards) and 9% nickel steel. In terms of ultimate tensile strength, it shows superiority over every type of metallic material in comparison. High Mn Steel recorded an elongation of around 80% of that of Type 304 and around 1.8-fold of that of 9% nickel steel. (a) Comparison with other cryogenic (b) Variation with respect to temperature Materials (25°C) Figure 1(b) shows the yield strength and ultimate tensile strength of high Mn steel increase monotonically and its elongation decreases, as test temperature decreases.



Figure 2: Stress-Strain curves of high Mn steel - (a) Comparison with other cryogenic materials (25°C) (b) Variation with respect to temperature


References

1. B. James Sutton: Solidification Behavior and Hot Cracking Susceptibility of High Manganese Steel Weld Metals, The Ohio State University, 2013;

2. Y. Wang, B. Shi, Y. He, H. Zhang, Y. Peng, T. Wang: A Fine Grain, High Mn Steel with Excellent Cryogenic Temperature Properties and Corresponding Constitutive Behaviour, Materials 2018, 11, 253; doi:10.3390/ma11020253;

3. Suitability of High manganese austenitic steel for cryogenic service and development of any necessary amendments to the IGC code and IGF code 2016, Accessed NOV 2018.

기술 자료 검색

검색할 어구를 입력하십시오:

검색 범위

본문
키워드

머릿글
요약

Total Materia Extended Range는 수천개 재질의 탄성 영역 범위 내 계산용 응력-변형률 곡선, 열처리 및 공정 온도 정보를 포함하고 있습니다. 다양한 변형률 속도에 따른 진응력-진변형률 곡선 및 공칭응력-공칭변형률 곡선 또한 제공됩니다.

응력-변형률 곡선을 데이터베이스에서 검색하는 것은 매우 쉽습니다.

신속 검색에 검색할 재질명을 입력합니다. 원하신다면 국가/규격을 지정하신 후 검색 버튼을 클릭합니다.


관심 소재를 선택한 후, 선택된 소재에 대한 응력-변형률 곡선의 링크를 클릭하십시오. 가능한 응력 - 변형률 곡선 기록의 개수는 링크 옆 괄호 안에 표시됩니다.


Total Materia 응력-변형률 곡선은 규격 사양서와 무관하므로, 어떠한 소그룹 내의 링크를 클릭하셔도 응력-변형률 곡선을 검토하실 수 있습니다.

온도가 달라지면 응력-변형률 곡선도 변하기 때문에, 응력과 변형률 정보는 표로 주어져 있습니다. 이는 CAE 소프트웨어 등에 쉽게 응용하실 수 있습니다.


다른 작동 온도에서 응력-변형률 곡선을 검토하실 수도 있습니다.

이를 위해서는 간단히 범위 내 새로운 온도를 온도 입력 창에 입력하시면 됩니다.

계산 버튼을 누르시면 새로운 온도와 그에 대응하는 값이 출력됩니다. 250°C에서의 예를 보십시오.


Total Materia 데이터베이스를 사용해 보실 수 있는 기회가 있습니다. 저희는 Total Materia 무료 체험을 통해 150,000명 이상의 사용자가 이용하고 있는 커뮤니티로 귀하를 초대합니다.