Hot Cracking Sensitivity Factors

Выдержки:

Identified by the appearance of liquid films along grain boundaries or to another location in the material structure, hot cracking can be divided into several categories.
As potential and serious threat to weld integrity, during this article we cover different ways to quantify, measure and ultimate prevent this phenomena.

It is known that some weld metal hot cracking theories have their origins in castings. However, it is critical to emphasize that casting processes have important differences as compared to weld processes, like time and length ratios. The cracking during welding can be attributed to the effect of tensile stresses on a not well developed dendritic network in the weld metal and/or heat affected zone (HAZ). “Hot cracking” is related to the appearance of liquid films along grain boundaries or to another location in the structure and can be divided into:
1) solidification cracking in the weld metal,
2) liquation cracking in the HAZ, and
3) weld metal liquation cracking.

This is then followed by “warm cracking”.

Warm cracking includes:
1) ductility-dip cracking,
2) reheat cracking,
3) strain age cracking, and
4) lamellar cracking.

Warm cracking can appear either during the welding process or after post weld heat treatment. Last, but not least, “cold cracking” develops at room temperature because of the presence of hydrogen and hydrogen-assisted cracking mechanisms.

As mentioded above, hot cracking refers to cracking that occurs during welding, casting or hot working at temperatures close to the melting point of the material. The cracking is known to occur both above the liquation temperature – known as supersolidus cracking and in the solid state, called subsolidus cracking. The various types of hot cracks encountered in stainless steel weldments have been classified by Hemsworth et al (1969). Supersolidus cracking may manifest as solidification cracking, occurring in the presence of a liquid phase in the fusion zone, or as liquation cracking in the heat-affected zone (HAZ) where it is accompanied by grain-boundary melting. Solidification cracking in the weld metal is considered the most deleterious and is more widely observed than the other types of cracking.

Solidification cracking occurs as a result of the simultaneous presence of:
1) depressed solidification temperature liquid films along solidification sub-grain boundaries (SSGBs), or more commonly, solidification grain boundaries (SGBs) in the fusion zone (FZ); and
2) weld restraint resulting from both intrinsic and extrinsic sources. Figure 1 schematically indicates the boundary types which can exist in the FZ of fully austenitic materials during solidification as described by Lippold et al.. SSGBs represent the boundaries between adjacent cells or dendrites with similar orientation, while SGBs are those boundaries which are formed when packets of subgrains intersect. A solidification crack is formed when liquid films along SSGBs and/or SGBs rupture during solidification.



Figure 1: Schematic representation of interfaces which may exist in a single phase weld metal following solidification

Quantification of Hot Cracking Susceptibility in 304L and 316L austenitic stainless steel

Quantification of HAS for various specifications of types 304L and 316L can be done with the help of following equation. But it is advisable to have S<0.035%, Ni<1.0%, Mn>0.8%, C<0.15% and Mn/S>35.

The calculated values of the Hot Crack Sensitivity for given specifications, is shown in Figure 2. Here results reveal that HCS for the typical SA240-304L is found least and is maximum for SA 312 (pipe) 316L. Hot cracking susceptibility increases markedly as the P and S contents exceeds 0.015%. Lowest value 0.053 is observed for P and S contents, which directly illustrates emphasis of P+ S effect on HCS. As with the increased value of P+S, HCS increases. The sulphur range should be 0.005 to 0.030% for acceptable penetration for both types of steels. Increasing the nitrogen content improves the resistance to hot cracking of those types of 304L and 316L steels, which contain no niobium as nitrogen containing steels have less hot cracking resistance.



Figure 2: Calculated HCS of various specifications of types 304L, and 316L using the extremes of the composition


References

1. D. Manitsas, J. Andersson: Hot Cracking Mechanisms in Welding Metallurgy: A Review of Theoretical Approaches, MATEC Web of Conferences 188, 03018, 2018, ICEAF-V 2018;

2. V Shankar, T P S Gill, S L Mannan, S. Sundaresan: Solidification cracking in austenitic stainless steel welds, Sāadhanā Vol. 28, Parts 3 & 4, June/August 2003, p. 359–382.

3. B. James Sutton: Solidification Behavior and Hot Cracking Susceptibility of High Manganese Steel Weld Metals, The Ohio State University, the Degree Master of Science 2013;

4. R. Saluja, K M Moeed: The Emphasis of Phase Transformations and Alloying Constituents on hot Cracking Susceptibility of type 304L and 316L Stainless Steel Welds, International Journal of Engineering Science and Technology (IJEST) Vol. 4 No.05 May 2012, p.2206-20216; ISSN: 0975-5462

Поиск в Банке Знаний

Введите фразу для поиска:

Поиск по

Всему тексту
Ключевым словам

Заголовкам
Выдержкам

Total Materia Extended Range includes the largest database of fracture mechanics parameters for hundreds of metal alloys and heat treatments conditions. K1C, KC, crack growth and Paris law parameters are given, with the corresponding graph of crack growth.

Monotonic properties are added for the reference, as well as estimates of missing parameters based on monotonic properties where applicable.

Enter the material of interest into the quick search field. You can optionally narrow your search by specifying the country/standard of choice in the designated field and click Search.

solution img

After clicking the material from the resulting list, a list of subgroups that are standard specifications appears.

solution img

Because Total Materia Extended Range fracture mechanics parameters are neutral to standard specifications, you can review fracture mechanics data by clicking the appropriate link for any of the subgroups.

The data are given in a tabular format, with the Paris curve (Region II) where applicable. Explicit references to the data sources are given for each dataset.

solution img

For you’re a chance to take a test drive of the Total Materia database, we invite you to join a community of over 150,000 registered users through the Total Materia Free Demo.