Sensitization of Austenitic Stainless Steels

Sumário:

Sensitization refers to the susceptibility of materials to intergranular corrosion and comes about by a combination of factors in the materials composition and treatment.
Contributing factors can include heating and cooling through specific temperature ranges, increased C content or decreased Cr content and among other factors.

An alloy is said to be “sensitized” if it is more susceptible to intergranular corrosion than a non-sensitized sample of the same alloy. Atkinson and Van Droffelar 1982 have made some observation on sensitization which are:

1) Sensitization occurs when the alloys are slowly heated or cooled through the range of approximately 500°C to 800°C.

2) Fast cooling through this temperature range does not result in sensitization

3) Quenching from elevated temperatures followed by reheating in the range of 500°C to 800°C causes the steel to become sensitized

4) The degree of sensitization increases markedly with increasing carbon content and and to a lesser extent with decreasing chromium content

5) The degree of sensitization varies within the sensitization temperature range

6) The degree of sensitization also increases with time at the sensitization temperature

7) The prominent feature of sensitized austenitic stainless is the presence of precipitates of chromium carbides at the grain boundaries

A steel which has been sensitized may appear essentially unaffected, yet it will be found to possess reduced strength and corrosion resistance which, if severe enough, will cause the steel to lose its characteristic metallic ring if struck with a metal object; while bending or twisting will produce cracks. The most popular explanation for the sensitization phenomenon is the chromium depletion theory. According to Miller and Boulton (1982) intergranular corrosion occurs along the grain boundaries of a metal.

Sensitization resulting from isothermal exposure is normally represented by time-temperature-sensitization (TTS) diagrams which are plots of aging time versus the temperature necessary for sensitization. These are “C” shaped curves, which separate the sensitized and non-sensitized regions. The TTS diagrams show the time required for isothermal sensitization at various temperatures and can be used to solve the problems such as the selection of conditions of annealing which will not result in sensitization. The nose of this curve specifies the critical temperature at which the minimum time (tmin) is required for sensitization.

In the paper M. Dománková et al., some preliminary comparisons are reported on the combined effects of deformation, temperature and aging time on sensitization in AISI 316 austenitic stainless steel.

The chemical composition of experimental steel is given in Table 1. The material examined was supplied in the condition after solution annealing (1050°C for 60 min), followed by water quenching.



Table 1: Chemical composition in wt.% of austenitic stainless steel used in this study

The oxalic acid etch test was used for the determination of steel sensitivity to intergranular corrosion. The specimens were electrolytically etched in 10% oxalic acid for 90 sec. at a current density of 1 A/cm2. The etched microstructures were then examined at 250x.

The rapid oxalic acid etch test was used for the analysis of the grain boundary sensitization development. Examples of microstructure obtained by etch test for AISI 316 are given in Figure 1. The TTS diagram was obtained by plotting sensitization test results on a temperature versus log soaking time axes and drawing a line which demarcates the sensitized and non-sensitized regions (Figure 2). The nose of this curve for the experimental steel AISI 316 was at the temperature 800°C and tmin=20 min.







Figure 1: Examples of AISI 316 microstructure obtained after oxalic acid etch test a) after solution annealing (step), b) after aging 800°C/10 min. (dual), c) after aging 800°C/10 h (ditch)



Figure 2: TTS diagram for AISI type 316 austenitic stainless steel established according to the test ASTM A262 practice A

Procurar conhecimento básico

Colocar uma frase para procurar por:

Procurar por

Texto completo
Palavras chaves

Títulos
Resumo

O banco de dados da Total Materia contém um grande número de imagens metalografia através de uma gama grande de países e padrões.

Usando o guia Metalografia projetado especificamente na barra de menu, você pode selecionar o material de seu interesse a partir da lista de materiais com dados metalografia incluído.

Metalografia dados também podem ser encontradas através do nosso padrão de pesquisa rápida e irá mostrar os dados relevantes são disponíveis através da página Subgrupo padrão para o material de interesse.

Basta digitar a sua designação de material para o 'Material' campo e selecione o padrão de juros, se conhecido, em seguida, clique em "Procurar".


As informações gerais sobre microestrutura pode ser encontrada, juntamente com a composição química relevante para o material de interesse.


Quando disponível, uma série de imagens será fornecido a exibir uma gama de detalhe estrutural em vários níveis de ampliação.

Também é possível selecionar opções diferentes de condição de suspensa a 'condição Selecionar' para mostrar imagens metalografia em processo diferente e estados de tratamento térmico.



Para você é uma oportunidade de fazer um test drive na Total Materia, nós convidamos você a participar de uma comunidade de mais de 150.000 usuários registrados através da Total Materia Free Trial.