Arctic Steels: Part Two

요약:

There are many technological and management challenges in working under the harsh conditions of the arctic and these challenges extend into the use of materials in many varied applications.
A range of applications specific tests can be employed for artic steels to ensure their suitability including microstructural examination, static tension tests, crack tip opening displacement tests, to name but a few.

Currently, most investigations into materials for Arctic use have focused on the mechanical properties of these materials in a low-temperature environment.

To meet increasing demand for hydrocarbon reserves, exploration and extraction activities in the Arctic have increased significantly in recent years, in light of estimates that 13% of the world’s undiscovered oil and gas can be found in the area.

The challenging new requirements for existing steel grades are an improved toughness at lower temperatures without decrease of strength and an adapted weldability. In the paper of P. Flüss, D. Rupp, F. Hanus, W. Schütz, the development of high-strength heavy plates with improved low temperature toughness is described and illustrated with a recent application. Plates of grade S420G1/2 up to 65 mm thickness and Charpy impact properties down to -80°C and CTOD (Crack Tip Opening Displacement)-properties down to -50°C were successfully produced and delivered for the construction of an offshore loading tower in Siberia.

The paper of P. Layus, P. Kah, M. Pirinen describes the results of a comparative study of two Finnish and Russian Arctic shipbuilding thick steel plates. E500 steel plate (TMCP, 25 mm thickness, Ruukki) and F500W steel plate (QT, 35 mm thickness, CRISM Prometey), which are designed for operation in Arctic conditions at temperatures as low as -40°C and -60°C, respectively, were tested.

Comparison analysis of the two steel grades included chemical composition and microstructure examination, mechanical properties tests, impact tests at low temperatures, and special cold-resistance tests. The set of experiments is the following:
• Microstructure examination
• Static tension tests and other basic mechanical properties tests
• Impact tests with the V-notch
• Determination of the temperature of null-ductility (NDT)
• Determination of Tkb
• Crack tip opening displacement test (CTOD)

Specimens for the tests were cut from the steel plates using a water jet cutting machine. This cutting method was selected to minimize heat input to the base metal and to reduce the waste of metal during the cutting process. Tests were carried out according to international and Russian standards.

Figure 1 gives a graphical presentation of the results while Table 1 presents the results of the experiments.



Figure 1: Static tension tests of cylindrical samples



Table 1: Mechanical properties of E500 and F500W steels based on static tension tests of cylindrical samples, where σв – Tensile strength, σ0.2 – Yield strength, δ5 - Elongation, ψ – Relative contraction ratio in thickness direction

Conclusion

  • Based on the conducted experiments the following conclusions can be drawn: Both steel plates studied, F500W (made in Russia) and E500 (made in Finland), meet Russian Maritime Register of Shipping (RMRS) standards requirements.
  • Resistance to brittle fracture of high strength steels is defined by material metallurgy features, which depend on chemical composition and manufacturing technology.
  • F500W obtains better results in special tests like NDT (-100°C > -65°C) and CTOD (CTOD -40°C average 1.18 mm > 0.41 mm). Using quenching followed by high tempering enables possible operational temperatures down to -70°C. From the economic perspective, F500W steel should only be used for special applications that require high NDT and CTOD test values.
  • E500 TMCP steel has lower carbon equivalent than F500W QT steel and therefore better weldability properties.
  • The applied thermomechanical processing of E500 steel leads to the formation of oriented structures that limit operational temperatures to -40°C.


References

1. Y-Y Choi, M-H Kim: Corrosion behaviour of welded low-carbon steel in the Arctic marine environment, The Royal Society of Chemistry 2018 (RSC Adv.), 2018, 8, p. 30155–30162;

2. P. Layus, P. Kah, M.Pirinen: Comparison of Finiiish steel E500 and Russian steel F500 for Arctic applications, 2015, IIW International Conference High-Strength Materials - Challenges and Applications 2-3July 2015, Helsinki, Finland

3. P. Flüss, D. Rupp, F. Hanus, W. Schütz: New Developments on Arctic Steels by Application of TMCP Technology, Proceedings of the Twenty-sixth (2016) International Ocean and Polar Engineering Conference Rhodes, Greece, June 26-July 1, 2016, Copyright © 2016 by the International Society of Offshore and Polar Engineers (ISOPE), ISBN 978-1-880653-88-3; ISSN 1098-6189.

기술 자료 검색

검색할 어구를 입력하십시오:

검색 범위

본문
키워드

머릿글
요약

Total Materia는 수천개의 재질에 대한 기계적 특성 테이터가 포함되어 있으며, 데이터를 검토하는 것은 매우 쉽습니다.

데이터베이스는 다양한 특성 정보를 포함하고 있으며, 수 많은 재질의 항복 응력, 인장 응력과 연신율은 데이터를 쉽게 찾을 수 있을 것입니다.

신속 검색에 검색할 재질명을 입력합니다. 원하신다면 국가/규격을 지정하신 후 검색 버튼을 클릭합니다.


Total Materia 데이터베이스에서 검색된 관심 재질의 목록이 즉시 생성됩니다.
관심 재질을 클릭합니다.


소그룹 페이지에서, 선택된 재질의 기계적 특성 링크를 클릭하여 데이터를 검토합니다. 기계적 특성 데이터 기록의 개수는 링크 옆 괄호 안에 표시됩니다.


기계적 특성 데이터는 참조를 위해 선택한 모든 재질 정보와 함께 표시됩니다.

기계적 특성 데이터는 가능한 모든 조건과 처리 상태에 대해 표시됩니다.


또한 한 번의 클릭으로 귀하의 선택에 따라 단위 값을 메트릭(SI)과 앵글로 색슨 단위로 전환할 수도 있습니다.


Total Materia 데이터베이스를 사용해 보실 수 있는 기회가 있습니다. 저희는 Total Materia 무료 체험을 통해 150,000명 이상의 사용자가 이용하고 있는 커뮤니티로 귀하를 초대합니다.