Sensitization of Austenitic Stainless Steels

요약:

Sensitization refers to the susceptibility of materials to intergranular corrosion and comes about by a combination of factors in the materials composition and treatment.
Contributing factors can include heating and cooling through specific temperature ranges, increased C content or decreased Cr content and among other factors.

An alloy is said to be “sensitized” if it is more susceptible to intergranular corrosion than a non-sensitized sample of the same alloy. Atkinson and Van Droffelar 1982 have made some observation on sensitization which are:

1) Sensitization occurs when the alloys are slowly heated or cooled through the range of approximately 500°C to 800°C.

2) Fast cooling through this temperature range does not result in sensitization

3) Quenching from elevated temperatures followed by reheating in the range of 500°C to 800°C causes the steel to become sensitized

4) The degree of sensitization increases markedly with increasing carbon content and and to a lesser extent with decreasing chromium content

5) The degree of sensitization varies within the sensitization temperature range

6) The degree of sensitization also increases with time at the sensitization temperature

7) The prominent feature of sensitized austenitic stainless is the presence of precipitates of chromium carbides at the grain boundaries

A steel which has been sensitized may appear essentially unaffected, yet it will be found to possess reduced strength and corrosion resistance which, if severe enough, will cause the steel to lose its characteristic metallic ring if struck with a metal object; while bending or twisting will produce cracks. The most popular explanation for the sensitization phenomenon is the chromium depletion theory. According to Miller and Boulton (1982) intergranular corrosion occurs along the grain boundaries of a metal.

Sensitization resulting from isothermal exposure is normally represented by time-temperature-sensitization (TTS) diagrams which are plots of aging time versus the temperature necessary for sensitization. These are “C” shaped curves, which separate the sensitized and non-sensitized regions. The TTS diagrams show the time required for isothermal sensitization at various temperatures and can be used to solve the problems such as the selection of conditions of annealing which will not result in sensitization. The nose of this curve specifies the critical temperature at which the minimum time (tmin) is required for sensitization.

In the paper M. Dománková et al., some preliminary comparisons are reported on the combined effects of deformation, temperature and aging time on sensitization in AISI 316 austenitic stainless steel.

The chemical composition of experimental steel is given in Table 1. The material examined was supplied in the condition after solution annealing (1050°C for 60 min), followed by water quenching.



Table 1: Chemical composition in wt.% of austenitic stainless steel used in this study

The oxalic acid etch test was used for the determination of steel sensitivity to intergranular corrosion. The specimens were electrolytically etched in 10% oxalic acid for 90 sec. at a current density of 1 A/cm2. The etched microstructures were then examined at 250x.

The rapid oxalic acid etch test was used for the analysis of the grain boundary sensitization development. Examples of microstructure obtained by etch test for AISI 316 are given in Figure 1. The TTS diagram was obtained by plotting sensitization test results on a temperature versus log soaking time axes and drawing a line which demarcates the sensitized and non-sensitized regions (Figure 2). The nose of this curve for the experimental steel AISI 316 was at the temperature 800°C and tmin=20 min.







Figure 1: Examples of AISI 316 microstructure obtained after oxalic acid etch test a) after solution annealing (step), b) after aging 800°C/10 min. (dual), c) after aging 800°C/10 h (ditch)



Figure 2: TTS diagram for AISI type 316 austenitic stainless steel established according to the test ASTM A262 practice A

기술 자료 검색

검색할 어구를 입력하십시오:

검색 범위

본문
키워드

머릿글
요약

Total Materia는 다양한 나라와 규격에 따른 금속학 이미지에 대한 정보를 포함하고 있습니다.

메뉴 표시줄에 특별히 디자인된 금속학 탭을 이용하여, 금속학 데이터가 포함된 관심 재질을 리스트에서 선택하실 수 있습니다.

또한 금속학 데이터는 표준 빠른 검색을 통해 찾을 수 있으며 규격 내 소그룹 페이지를 통해 이용 가능한 관련 자료들이 표시됩니다.

재질명을 '재질'창에 입력하신 후 규격을 알고 계신다면 규격을 선택하고 '검색' 버튼을 클릭합니다.


미세 구조에 대한 일반적인 정보가 관련 관심 재질의 화학 조성과 함께 출력됩니다.


구조의 세부 범위를 보여주는 여러 배율에서의 이미지가 가능하다면 제공됩니다.

다양한 조건을 선택할 수 있으며, '조건 선택' 메뉴를 사용하여 다양한 공정 및 열처리에 따른 금속학 이미지를 보여줍니다.



Total Materia 데이터베이스를 사용해 보실 수 있는 기회가 있습니다. 저희는 Total Materia 무료 체험을 통해 150,000명 이상의 사용자가 이용하고 있는 커뮤니티로 귀하를 초대합니다.