Sacrificial Anodes: Part One


Sacrificial anodes are specifically designed to act as corrosion ‘decoys’ for materials which require protection from a variety of corrosive forces.
Typically with more negative electrochemical potential sacrificial anodes for steel can include zinc, aluminum and magnesium based on their position in the galvanic series.

Sacrificial Anodes are highly active metals that are used to prevent a less active material surface from corroding. Sacrificial Anodes are created from a metal alloy with a more negative electrochemical potential than the other metal it will be used to protect. The sacrificial anode will be consumed in place of the metal it is protecting, which is why it is referred to as a "sacrificial" anode.

To understand the action of sacrificial anodes for cathodic protection it is necessary to have in mind the galvanic series of metals. The galvanic series for a few selected metals in sea water is shown in Table 1.

Table 1: Galvanic series of some metals in sea water

It is evident that when the tendency for metal to go into solution as metal ions increases (leaving an excess of electrons on the metal surface), i.e.

M > M+ + e ... (1)

the metal becomes more electronegative. Thus, since zinc, aluminum and magnesium are more electronegative than steel they are increasingly able to supply electrons to the more electropositive steel when in electrical contact in water, and will effect cathodic protection of the steel surface. Clearly, if steel was coupled to copper in sea water, steel would supply electrons to copper which would become cathodically protected, and the corrosion of the steel would be enhanced. The principle of cathodic protection is well explained by the Wagner-Traud mixed potential theory.

According to this theory, any corrosion process can be divided into two or more oxidation and reduction partial reactions with no net accumulation of electric charge during the process. The corrosion reactions occurring in aluminum in an aqueous medium are shown in Equations 2–4:

Anodic reaction:

Al → Al3+ + 3e− (Aluminum dissolution) … (2)

Cathodic reactions:

O2 + 2H2O + 4e− → 4OH (Oxygen reduction on Al in neutral or basic solution) … (3)

O2 + 4H+ + 4e− → H2O (Oxygen reduction on Al in acid solutions) … (4)

Corrosion is initiated only when both the anodic and cathodic reactions occur simultaneously. The total rate of oxidation must equal the total rate of reduction in any system. In Figure 1, the relationship between the anodic and cathodic partial corrosion currents for Al has been shown, using mixed potential theory and kinetic equations.

Figure 1: Evans diagram explaining the principle of cathodic protection

As shown in Figure 2, polarization of the cathode in a negative direction from the corrosion potential decreases the corrosion rate. By polarizing the system from Ecorr to E’corr with a known applied current through the sacrificial anode or direct current source, the corrosion current density decreases from Icorr to I'corr.

Figure 2: Schematic showing cathodic protection methods using sacrificial anode

For complete inhibition of corrosion processes, it is necessary to polarize the metal to its reversible potential EAl/Al 3+. The applied current at EAl/Al 3+ potential is termed as the protection current.

기술 자료 검색

검색할 어구를 입력하십시오:

검색 범위



Total Materia는 내부식용으로 적합한 다양한 국가와 규격 내 수천개의 재질에 대한 정보를 포함하고 있습니다.

재질의 화학적 조성, 기계적 특성, 물리적 특성, 고급 물성 데이터 등의 전체적인 특성 정보들을 어디서든 검토하실 수 있습니다.

고금 검색 내 규격 설명 기능을 이용하여, 규격 내 재질에 설명된 키워드를 통해 재질을 검색하실 수 있습니다.

검색 범위 좀 더 줄이기를 원하신다면 국가/규격과 같은 다른 조건을 지정할 수 있습니다.

검색 버튼을 클릭합니다.

선택된 정보에 부합하는 일련의 재질이 검색됩니다.

결과 리스트에서 재질을 선택하시면, 일련의 규격 사양 소그룹이 나타납니다.

여기에서 선택한 재질의 특정 특성 데이터를 검토하실 수도 있고, 강력한 상호 참조 표를 이용하여 유사 재질이나 등가 재질을 검토하는 것 또한 가능합니다.

예를 들어, 소그룹 내 화학적 조성 링크를 클릭하시면, 재질의 화학적 조성 데이터를 검토하실 수 있습니다.

Total Materia 데이터베이스를 사용해 보실 수 있는 기회가 있습니다. 저희는 Total Materia 무료 체험을 통해 150,000명 이상의 사용자가 이용하고 있는 커뮤니티로 귀하를 초대합니다.