Cold Extrusion of Steel: Part One


Cold extrusion of metals is one of the most important manufacturing processes today and effectively involves forcing the material through the die at room temperature to create a continuous product of consistent cross-section.
Although there are minor variations, the 3 main extrusion process can be covered by forward extrusion, backward extrusion and upsetting which differ basically by the direction of the metal flow during the extrusion process.

Extrusion, though one of the most important manufacturing processes today, is a relatively young metalworking process. The cold extrusion process involves forcing a billet of material through a die at room or slightly elevated temperatures, producing a continuous product of constant cross-section. Numerous metals are suitable for cold extrusion, including lead, tin, aluminum alloys, copper, titanium, molybdenum, vanadium, and steel.

A wide variety of parts can be produced, including collapsible tubes, aluminum cans, cylinders and gear blanks. Cold extruded parts do not suffer from oxidation and often have improved mechanical properties due to severe cold working, as long as the billet temperature remains below the re-crystallization temperature.

Cold extrusion technology permits the forming of a part to the desired size and shape by moving the metal at room temperature into the die. Sufficient force is required to exceed the yield strength of the stainless steel and ensure plastic deformation results, enabling the metal to fill out the die cavities to extremely close tolerances. Although there are many different cold extrusion operations, all are variations of one or more of the following:

Forward extrusion forces the metal to flow in the same direction as the descending punch and through a hole in the die to form the required shape and dimensions, as shown in Figure 1a). Forward extrusion is especially useful in the production of bolts and screws, stepped shafts, and cylinders.

Backward extrusion forces the metal to flow upwards around the descending punch, as illustrated in Figure 1b). Extrusion pressures are generally higher and slug preparation is more critical.

Upsetting is the gathering of metal in certain sections along the length of a bar, rod or wire as shown in Figure 1c). The metal is forced to flow at right angles to the motion of the tolling. Upsetting is often performed in conjunction with backward or forward extrusions.

Figure 1: a) Forward extrusion b) Backward extrusion c) Upsetting

Figure 2: Examples of cold extrusion design

기술 자료 검색

검색할 어구를 입력하십시오:

검색 범위



이 문서는 전체 문서 중 일부분입니다. 이 주제에 대해 더 읽고 싶으시면 아래 링크를 클릭하시면 됩니다.

물리적 특성은 Total Materia 데이터베이스 내 많은 재질에서 검토하실 수 있습니다.

데이터는 규격의 공식 정보와 Total Materia의 강력한 상호 참조 표를 통해 검색 가능하며 이는 물리적 특성 데이터 검색에 매우 효과적일 것입니다!

신속 검색에 검색할 재질명을 입력합니다. 원하신다면 국가/규격을 지정하신 후 검색 버튼을 클릭합니다.

관심 있는 재질을 선택하신 후, 물리적 특성 링크를 클릭하셔서 선택된 재질의 데이터를 검토합니다. 물리적 특성 데이터 기록의 개수는 링크 옆에 괄호 안에 표시됩니다.

물리적 특성은 원래 데이터 값에 따라 표시됩니다. 규격에 의한 공식 데이터는 공식 탭에서 찾을 수 있고, 다른 출처를 통해 검색된 재질의 데이터는 자신의 탭에 표시 됩니다.

유사 재질 탭에는 원래 재질과 비슷하며 물리적 특성이 포함된 재질을 표시합니다. 등가 재질 검색 시에 매우 유용할 수 있습니다!

일반 탭은 특성 데이터에 대한 일반적인 개요를 제공하며 추가 조사를 위한 유용한 출발점으로 사용될 수 있습니다.

Total Materia 데이터베이스를 사용해 보실 수 있는 기회가 있습니다. 저희는 Total Materia 무료 체험을 통해 150,000명 이상의 사용자가 이용하고 있는 커뮤니티로 귀하를 초대합니다.