Inoculation Mechanisms: Part Two

요약:

Inoculation can be summarized as the addition of silicon alloys during the latter stages to molten iron provides control in “chill” areas of castings e.g. thin sections and corners of the casting.
Covered in this article are the main processing factors to take notice of and also the main methods of inoculation including, ladle, in-stream and in-mould inoculation.

Inoculation is defined as the late addition of certain silicon alloys to molten iron to produce changes in graphite distribution, improvements in mechanical properties, and a reduction of the chilling tendency that are not explainable on the basis of composition change with respect to silicon. Graphite, added alone or in combination with ferrosilicon, will also produce these changes without significantly altering the chemistry of the iron. It is recognized that two irons with the same apparent composition can have dramatically different microstructures and properties if one is inoculated and the other is not. A great deal of research has been dedicated to determining the mechanics behind inoculation. Although many theories exist no conclusions have been reached regarding possible mechanisms.

Irons are inoculated for various reasons. The primary reason is to control chill in areas of castings that experience rapid solidification, such as in thin sections, at corners, and along edges. Tensile strength can be improved through inoculation. This is particularly true for the low-CE irons, which are selected for applications requiring a higher tensile strength (tensile strength decreases as the CE increases). However, low CE irons are also the grades that are most susceptible to carbide formation.

Inoculation helps overcome this problem by minimizing the chill forming tendency of the iron, thus allowing low CE irons to be poured in thin sections. Irons that are stored in holding furnaces or in pouring systems for an extended period of time are also more susceptible to chill formation. This susceptibility can be attributed to the reduction in nuclei in the melt that takes place during extended holding. This effect is accelerated if holding occurs at high temperatures. Melting method influences white iron formation; electric melted irons are generally more prone to carbide formation than cupola melted irons.

The principal inoculation mechanisms are quite different in grey and ductile irons. In grey iron, a stable oxide will be the primary nuclei for manganese sulphide precipitation that again will nucleate graphite flakes of good type A form. In ductile iron, a sulphide is the nuclei for complex silicates that again will nucleate a high number of graphite nodules. The same inoculant materials can however be used successfully in both type of irons, since the reactive elements such as Ca, Ba, Sr and Al are all strong oxide, sulphide and silicates formers in both grey or ductile irons.

The inoculant fading effect is connected to diffusion rate, growth and coarsening, and a general reduction in the number density of micro-inclusions as nucleation sites for graphite. In order to obtain a sound and reproducible iron production process some critical inoculation factors will have to be controlled properly. For grey iron one should pay special attention to the following factors:

1) The Mn/S ratio should be maintained at the same level every time and sulphur should preferentially be kept at minimum 0.05%.
2) Aluminum is found to be an important part of the nucleus core and should be adjusted and kept at controlled levels every time. Recommended residual Al level in grey iron is 0.005% - 0.01% for optimum inoculation effectiveness.
3) There should be a certain oxygen level in the base iron from fresh metal processing. The use of some rusty raw materials may assist in providing a good oxygen potential.
4) Pouring time after inoculation should be minimized in order to keep fading losses under control.
5) Use an inoculant with defined chemical composition and sizing.

Methods of Inoculation

Cast iron may be inoculated by several methods such as:

• Ladle Inoculation
Iron is inoculated by adding inoculant to the metal as it is transferred from the furnace to the pouring ladle. The turbulence quickly dissolves the inoculant and evenly disperses it throughout the molten bath (Figure 1)

• In-stream Inoculation
In many automatic pouring operations, inoculation is done in-the-stream (Figure 2)

• In-mould Inoculation
Inoculants may also be added as a preformed insert placed in the pouring basin of a mould or as granulated inoculant placed in the gating system. (Figures 3a and 3b)

In-stream and in-the-mould inoculation techniques offer little inoculation fades, and generally require less inoculants material to provide the desired results.



Figure 1: Ladle inoculation



Figure 2: In stream inoculation



Figure 3a: In the mould inoculation



Figure 3b: In the mould inoculation

기술 자료 검색

검색할 어구를 입력하십시오:

검색 범위

본문
키워드

머릿글
요약

이 문서는 전체 문서 중 일부분입니다. 이 주제에 대해 더 읽고 싶으시면 아래 링크를 클릭하시면 됩니다.

Total Materia는 다양한 나라와 규격에 따른 금속학 이미지에 대한 정보를 포함하고 있습니다.

메뉴 표시줄에 특별히 디자인된 금속학 탭을 이용하여, 금속학 데이터가 포함된 관심 재질을 리스트에서 선택하실 수 있습니다.

또한 금속학 데이터는 표준 빠른 검색을 통해 찾을 수 있으며 규격 내 소그룹 페이지를 통해 이용 가능한 관련 자료들이 표시됩니다.

재질명을 '재질'창에 입력하신 후 규격을 알고 계신다면 규격을 선택하고 '검색' 버튼을 클릭합니다.


미세 구조에 대한 일반적인 정보가 관련 관심 재질의 화학 조성과 함께 출력됩니다.


구조의 세부 범위를 보여주는 여러 배율에서의 이미지가 가능하다면 제공됩니다.

다양한 조건을 선택할 수 있으며, '조건 선택' 메뉴를 사용하여 다양한 공정 및 열처리에 따른 금속학 이미지를 보여줍니다.



Total Materia 데이터베이스를 사용해 보실 수 있는 기회가 있습니다. 저희는 Total Materia 무료 체험을 통해 150,000명 이상의 사용자가 이용하고 있는 커뮤니티로 귀하를 초대합니다.