Strain Ageing of Steel: Part Two

概要:

Strain ageing can have a serious detrimental effect on low carbon structural steels and so two material examples are examined to see how different pre-strain and ageing conditions affect material mechanical properties.
A carbon steel (40% martensite) and a microalloyed steel (20% martensite) were both treated under the same parameters and then the UTS and stress strain curves were evaluated to gain some valuable conclusions.

Strain ageing has been found to cause a detrimental effect in low carbon structural steels. A lot of studies have been made on the effect of different parameters on strain ageing characteristics of theses steels.

In the work of S. Gündüz, the ageing behaviour of a carbon steel with 40% martensite volume fractions and a microalloyed steel with 20% martensite volume fractions were studied. The variation of mechanical properties, especially the increase in YS was measured by tensile tests. The specimens were pre-strained in tension by 2, 4 and 6%, aged at 25, 100, 150, 200 and 250°C for 30 min followed by restraining.

The steels used in this investigation are commercially produced a carbon steel (without alloying elements) and a microalloyed steel with a chemical composition shown in Table 1. All the specimens were first subjected to an annealing treatment at 900 °C for 30 min followed by air cooling to homogenize the micro-structure.

Samples used for the annealing treatment are of dimensions approximately 170mm × 30mm × 4.5 mm. A Carbolit furnace capable of operating up to 1200°C was used. The temperature in the heat treatment furnace was measured using a K-type thermocouple and temperature variation during heat treatment did not exceed ±3°C.

  %C %Si %S %P %Mn %V %Ti %Al %Nb
Microalloyed steel 0.11 0.10 0.010 0.020 1.20 0.10 0.05 0.020 0.070
Carbon steel 0.22 0.40 0.020 0.025 1.40 - - 0.015 -

Table 1: Chemical composition of the investigated steels

As mentioned above, the specimens were pre-strained in tension by 2, 4 or 6%. After this, they were unloaded and aged at 25, 100, 150, 200 and 250°C for 30 min. After ageing of the specimens, they were subjected to a tensile test at ambient temperature at a crosshead speed of 2 mm/min. At least three specimens were tensile tested for each ageing temperature and average values were calculated.

The increase in flow stress as a result of restraining was taken as the strain ageing, ΔY2, which is illustrated in Figure 1. For samples, pre-strained in tension, ΔY2 was determined with single specimen by the difference between lower yield stress after ageing and the flow stress at the end of the pre-straining.



Figure 1: Stress–strain curve for low carbon steel strained to point A, unloaded, and then restrained immediately (curve a) and after ageing (curve b).

Figures 2 and 3 show the stress–strain diagrams of the dual phase carbon steel and the microalloyed steel pre-strained in tension by 2, 4 or 6%, aged at different temperatures, and restrained.

As shown, the dual phase carbon steel and the microalloyed steel, prior to any ageing, exhibits continuous yielding which has been commonly attributed to mobile dislocations introduced during cooling from the intercritical annealing temperature. Many dislocation sources come into action at low strain and plastic flow begins simultaneously through the specimen, thereby suppressing discontinuous yielding.



Figure 2: Variation of stress–strain curves of the dual phase carbon steel at different ageing temperatures for the pre-strains of 2% (a), 4% (b) and 6% (c).



Figure 3: Variation of stress–strain curves of the dual phase microalloyed steels at different ageing temperatures for the pre-strains of 2% (a), 4% (b) and 6% (c).

The main conclusions from this study are as follows:
1. Both steels displayed significant changes in appearance as the ageing temperature was increased for the pre-strain in the range studied. This indicated that static strain ageing takes place in both dual phase carbon steel and microalloyed steel.
2. In contrast to the negative effect of pre-strains on the change in ΔY2 produced by subsequent ageing, it was found that increasing pre-strain markedly increased the change of UTS of both dual phase carbon steel and microalloyed steel. This indicated that ΔY2 value is insensitive to dislocation density and is principally dependent on the solute segregation per dislocation.
3. Both dual phase carbon steel and microalloyed steel showed significant increases in YS, UTS and ΔY2, however the percentage elongation to fracture decreased as the ageing temperature was raised from 25 to 100°C for the pre-strain in the range studied. This is due to atmosphere formation at dislocation and precipitation of carbonitride on dislocations during strain ageing.
4. Further increase in ageing temperature to 150, 200 and 250°C caused a reduction in YS, but an increase in percentage elongation. These are signs of overageing probably due to tempering effect of martensite and coarsening of the precipitates on the dislocations.
5. The ageing in the dual phase microalloyed steel occurred more slowly than the dual phase carbon steel. This was associated with the chemical composition of dual phase microalloyed steel which, in addition to carbon atoms, contained nitrogen and carbide forming elements such as titanium, vanadium and aluminum.

ナレッジベース検索

検索したい語句を入力:

検索方法

全文一致
キーワード

前方一致
要約

この記事は連載記事として掲載されております。詳細を見るには下記のリンクをクリックして下さい。

Total Materia Extended Range(拡張版)には数千種の金属合金塑性域、熱処理、加工温度等における計算に必要な応力‐歪み曲線が収録されております。さまざまな歪み速度に応じた真応力、エンジニアリング応力曲線も表示されます。

簡単でしかも数秒以内でデータベースの応力‐歪み曲線を探せます。

検索対象の材料を入力して下さい。材料入力のフィールドで国/規格を指定し検索を絞る事ができます。


対象材料を選んでから応力‐歪み曲線のリンクをクリックするとデータが御覧になれます。御覧になれる応力‐歪みデータの数はリンクわきのカッコ内に表示されております。


Total Materiaデータベースの応力‐歪み曲線は規格それぞれに中立的なものでサブグループのどれが適切なリンクをクリックしてデータを見て下さい。


他の加工温度に対する応力‐歪み曲線をみることができます。

まず、決められた温度範囲内で新たな温度を’ 温度入力’ のフィールドに入力するだけで構いません。

次に計算ボタンをクリックすると新しい曲線が表示され表の数字が入力された温度に応じて表示されます。 250°Cにて入力した場合の例を御覧下さい。


Total Materiaデータベースをあなたにテスト評価を頂くために15万人以上の方が登録されている無料お試しコミュニティ-へ御招待致します。