Abstrakt:

Generally, the high carbon steels contain from 0.60 to 1.00% C with manganese contents ranging from 0.30 to 0.90%.
The pearlite has a very fine structure, which makes the steel very hard. Unfortunately this also makes the steel quite brittle and much less ductile than mild steel.

Medium and high carbon steels are widely used in many common applications. Increasing carbon as the primary alloy for the higher strength and hardness of steels is usually the most economical approach to improved performance. However, some of the effects of elevated carbon levels include reduced weldability, ductility and impact toughness. When these reduced properties can be tolerated, the increased strength and hardness of the higher carbon materials can be used to a significant advantage. Common applications of higher carbon steels include forging grades, rail steels, spring steels (both flat rolled and round), pre-stressed concrete, wire rope, tire reinforcement, wear resistant steels (plates and forgings), and high strength bars.

To increase the performance of steels in these applications, it is common to maximize strength and hardness by raising the carbon level to the highest practical level. The limiting factor to carbon additions will vary depending on the type of applications. For forging steels and bar products, it may be toughness or weldability. For high strength wire, the limiting factor for carbon addition is generally the eutectoid carbon level, above which the presence of grain boundary carbides will dramatically reduce drawability.

Generally, the high carbon steels contain from 0.60 to 1.00% C with manganese contents ranging from 0.30 to 0.90%. High carbon steels are used for spring materials and high-strength wires. Ultrahigh carbon steels are experimental alloys containing approximately 1.25 to 2.0% C. These steels are thermomechanically processed to produce microstructures that consist of ultrafine, equiaxed grains of ferrite and a uniform distribution of fine, spherical, discontinuous proeutectoid carbide particles. Such microstructures in these steels have led to superplastic behavior.



Figure 1: Historical Description of the Fe-C phase diagram



Figure 2: Microstructure of high carbon steel

Figure 2 shows the microstructure of high carbon steel with about 0.8% C by weight, alloyed with iron. The steel has one major constituent, which is pearlite. It is made up from a fine mixture of ferrite and iron carbide, which can be seen as a "wormy" texture. The pearlite has a very fine structure, which makes the steel very hard. Unfortunately this also makes the steel quite brittle and much less ductile than mild steel. The high carbon steel has good wear resistance, and until recently was used for railways. It is also used for cutting tools, such as chisels and high strength wires. These applications require a much finer microstructure, which improves the toughness.

The common standards which define high carbon spring steel wire are:

ASTM A-227 Class I/II
ASTM A-417 Class I/II
ASTM A-407 Type A/B/C/D/E/F/G/H
ASTM A-228 Music Wire

Application

High carbon steel is used for applications in which high strength, hardness and wear resistance are necessary, such as wear parts, knives, saw blades, springs, gear wheels, chains, brackets etc. cold chisels, wrenches, Jaws for vices, pneumatic drill bits, wheels for railways service, wire for structural work, shear blades, hacksaws

Durchforschen Sie bitte den Informationsteil der Datenbank

Geben Sie bitte eine Anfrage, um Suche einzuleiten:

Suche nach

Vollständiger Text
Schlüsselwörter

Überschriften
Abstracts

Die Total Materia Datenbank, enthält mehrere tausende von Baustählen aus vielen Ländern und Normen.

Wenn zur Verfügung stehend, können alle Informationen über die Werkstoffeigenschaften angezeigt werden, einschliesslich chemische Zusammensetzung, mechanische und physikalische Eigenschaften, vortschrittliche Daten und vieles mehr.

Auf der Seite der erweiterten Suche ist es möglich Werkstoffe nach Anwendung mit Hilfe der Volltextsuche zu finden.

Es kann auch notwendig sein daß Sie Ihre Suche weiter einschränken indem Sie die anderen Felder der erweiterten Suche, wie z.B. Land/Norm benutzen.

Klicken Sie auf "Absenden".


Es wird danach eine Liste von Werkstoffen angezeigt von welcher Sie auswählen können.


Nachdem Sie auf der Ergebnisliste auf den entsprechenden Werkstoff geklickt haben, wird eine Liste der Untergruppen, welche Normspezifikationen sind, angezeigt.


Von hieraus ist es möglich, spezifische Eigenschaften für den ausgewählten Werkstoff anzuzeigen und äquivalente Werkstoffe mit unseren leistungsstarken Cross-Reference Tabellen zu finden.

Es ist, zum Beispiel möglich, durch klicken auf den entsprechenden Link, der Seite der Untergruppen, die chemische Zusammensetzung des erwünschten Werkstoffs anzuzeigen.


Andere kritische Werkstoffeigenschaften für Baustähle, wie mechanische Eigenschaften, mit Fließspannung, Zugspannung, Dehnung und Kerbschlagarbeit, können auch angezeigt werden.


Um unsere Datenbank auszuprobieren, laden wir Sie ein sich unserer Nutzergemeinschaft von über 150 000 angemeldeten Benutzern, mit einem kostenlosen Probeaboanzuschliessen.