The SIMA Process: Part One

요약:

The strain induced melt activation (SIMA) process is a well-known semi-solid metal processing technology that helps to obtain a non-dendritic morphology by stirring the alloy in between the solidus and liquid point.
The SIMA process consists of four stages; casting, hot-working, cold-working and finally isothermal conditioning.

The main aim of semi-solid metal (SSM) processing is to obtain the non-dendritic morphology by stirring the alloy in between the solidus and liquid point. Semi-solid forming, which has been widely use in the field of automobile, spaceflight and aviation, is a promising method of materials processing.

Usually, the semi-solid slurry, prepared by stirring process known as rheocasting, is used directly for forming products. Thixoforming is another two step method where thixoformed feed stock is reheated to semi solid temperature to provide the SSM slurry subsequently used for component shaping.

A number of methods, such as mechanical or electromagnetic stirring, the addition of grain refining elements, spray casting, and rapid cooling, have been reported to obtain near equiaxed grain structures. Alternatively, the strain-induced melt activation (SIMA) process produces the desired structures by deformation and a following heat treatment in the mushy zone. Parameters such as heating time and temperature, and the degree of cold working, are critical factors in controlling the semi-solid microstructures in the SIMA process. It has been shown that the microstructure of an alloy prepared in the semi-solid state depends on its microstructure prior to partial remelting, so it is important to study the initial microstructure and subsequent evolution process during partial melting.

As one of the SSM process, the strain induced melt activation (SIMA) process developed by Young et. al. in 1980s is used to produce Mg alloys. This combines both casting and forging/rolling. For this method, residual strain is stored in a billet and a global structure is evolved by the strain energy stored in the billet after reheating. The process is based on scientific understanding that grain boundaries induced by plastic deformation and recrystallization will be wetted by liquid metal at the semi solid temperature, resulting in a fine and globular structure. In this study, various parameters which relate the microstructure and mechanical characteristics of thixoformed A356 alloy, such as grain size, solid fraction and shape of primary Al and morphology of silicon particles are addressed. Grain coarsening mechanism has also been discussed.

The SIMA process involves the four processing stages: casting, hot working, cold working, and recystallization and partial melting (RAP). In the SIMA process, an alloy having the sufficient stored energy by cold working is heated to a mushy zone. During heating, recovery and recrystallization occur before liquid formation with the aid of the stored energy. Reaching the mushy zone, liquid is formed by preferential melting at grain boundaries with high energy state, and penetrates into high angle boundaries of recrystallized grains. Accordingly, the amount and distribution of the stored energy by cold working is the most critical factor in the SIMA process since they control the recovery and recrystallization kinetics and the uniformity of the resultant microstructure.

SIMA process consists of four discrete stages. First the alloy is cast in convenient sizes to obtain a typical dendritic microstructure. Subsequently, it is hot worked so a directional microstructure is introduced and the thickness of the casting is decreased. The third stage involves the introduction of a critical level of stored energy in the alloy by cold working. Finally, the deformed alloy is semisolid partially remelted, and held isothermally for a short time. In SIMA, the strain is introduced into the materials through predeformation. In a general point of view, during soaking, recrystallization takes place, and once the liquid starts to form, grain boundaries are wetted and penetrated by it, leading to formation of fine equiaxed particles.

Deformation step can be carried out by some different procedures such as rolling, forging, upsetting and extrusion. All these methods have some restrictions in amount and homogeneity of the strain that can be induced in each pass. Some new technologies are under development that do not have these restrictions and can be used as commercial and engineering applications. It was well showed that in the SIMA process increasing the globalizing temperature increases the amount of the liquid at the grain boundaries. Due to the effects of surface tension and interface curvature, the convex edges of the dendrites melt and decrease the interface area of the dendrites leading to a lower free energy. Moreover, concentration of the solute in the concave parts of the grains is higher, which increases the amount of the liquid in these areas. When the liquid of the two concaves contacted with each other, the grains would separate into autonomous small grains. It should be noted that increasing the heat treatment temperature causes a further dissolution of the eutectics and spheroidization of the α-Al grains.



Figure 1: Schematic illustrations of SIMA Process: SS-Semi Solid, WQ-Water Quenched, RT=Room Temperature


References

1. R. Gupta, A. Sharma, S. Kumar: Characterization study of Al alloy cast through Strain Induced Melt Activated (SIMA) Process, International Conference on Multidisciplinary Research & Practice, Volume I Issue VII IJRSI ISSN 2321-2705 p.21-24;

2. N. Saklakoglu, I. Etem Saklakoglu, M. Tanoglu, O. Oztas, O. Cubukcuoglu: Mechanical properties and microstructural evaluation of AA5013 aluminum alloy treated in the semi-solid state by SIMA process, Journal of Materials Processing Technology 148, 2004, p.103–107;

3. Y- B Song, K-T Park, Chun Pyo Hong: Recrystallization Behavior of 7175 Al Alloy during Modified Strain-Induced Melt-Activated (SIMA) Process, Materials Transactions, Vol. 47, No. 4, 2006, p. 1250-1256, 2006;

4. M. Karamouz, M. Alizadeh, A. Reza Ahmadi: Mechanical Properties and Microstructure Improvement of a Two-Step Strain Induced Melt Activation Processed 7075 Aluminum Alloy Compared to that SIMA Process, 2017, NOT PEER-REVIEWED, doi:10.20944/preprints201704.0172.v1.

기술 자료 검색

검색할 어구를 입력하십시오:

검색 범위

본문
키워드

머릿글
요약

열처리 도표는 Total Materia 데이터베이스 내 많은 재질에서 검토하실 수 있습니다.

열처리 도표는 경화도, 경도 탬퍼링, TTT 및 CCT를 포함하며 모두 규격 데이터에서 검색하실 수 있습니다.

특수 속성 자료를 선택하려면, 고급 검색 모듈에서 특수 검색 기능을 사용하시면 됩니다.

검색 조건을 정의하려면, '국가/규격' 목록에서 귀하에게 관심 국가/규격을 선택하고 특별 검색 영역에 위치한 '열처리 도표' 박스를 체크하는 것입니다. 이는 고급 검색 페이지의 하단 부분에 있습니다.

검색 버튼을 클릭합니다.


관심 소재를 선택 후, 선택된 소재의 열처리 데이터 링크를 클릭하십시오. 열처리 기록의 개수는 링크 옆 괄호 안에 표시됩니다.


선택된 자료의 사용 가능한 모든 열처리 정보가 표시됩니다.






Total Materia 데이터베이스를 사용해 보실 수 있는 기회가 있습니다. 저희는 Total Materia 무료 체험을 통해 150,000명 이상의 사용자가 이용하고 있는 커뮤니티로 귀하를 초대합니다.