Atmospheric Corrosion of Aluminum Alloys


Relative humidity, temperature, sunshine, pollutants, salinity all play a significant role in the atmospheric corrosion rate of materials and when very specific conditions are taken into consideration e.g. subtropical marine environments, can result in some of the most extreme corrosion conditions possible.
As one of the most widely produced metals on the planet, aluminum is the subject of many investigations in this area with at times, some interesting results.

Except for ferrous metals, aluminum is one of the most produced metals globally. Aluminum has many advantageous properties such as lightness, suitability for surface treatments, functional advantages of extruded and cast semi-products, high thermal and electrical conductivity. Aluminum forms a diverse group of alloys, which gives a wide range of properties and uses. It is also easy to form and recycle; the recycling of aluminum requires only 5% of the energy it takes to extract the metal from its ore. Aluminum has good corrosion resistance, especially in the atmosphere, due to the natural oxide layer.

Atmospheric corrosion is one of the most common types of corrosion responsible for the degradation metallic structures, devices, and products exposed to the atmosphere. Atmospheric conditions such as relative humidity, temperature, sunshine period’s pollutants, salinity, etc. play an essential role in corrosion of the exposed metals. In particular, the tropical and subtropical marine environment introduces one of the most aggressive conditions which results in serious atmospheric corrosion of metals.

Aluminum is widely used in plenty of industrial applications such as construction, electrical engineering, transport, and especially in the food industry for the manufacture of processing, production, storage and transportation equipment and machinery.

In the paper of Li T. et al., corrosion product formed on 2A12 Al alloy after 3 months of exposure in South China Sea atmosphere was analyzed by various surface analysis techniques, including scanning electron microscopy (SEM), energy-dispersive x-ray analysis (EDXA), x-ray protoelectron spectroscopy (XPS), and x-ray diffraction (XRD). The mechanism for atmospheric corrosion of Al alloy in the tropical marine environment was analyzed too. The authors realized that the atmospheric exposure usually took 1 year or more for a study cycle. Furthermore, it is worth pointing out that there is no typical four-season climate in the test location.

Figure 1 shows the optical views of macroscopic morphology of the top and bottom of the Al alloy specimen after 3 months of atmospheric exposure. It is clear that the specimen was heavily corroded, with localized corrosion occurring on the specimen surface. Both views show that the specimen lost brightness and became rough, with a yellowish gray patina present on the surface. Moreover, corrosion of the Al alloy specimen on the bottom was more serious than that on the top section.

Figure 1: Optical views of surface morphology of top and bottom parts of Al alloy specimen after 3 months of exposure in Xi-Sha Island atmosphere

기술 자료 검색

검색할 어구를 입력하십시오:

검색 범위



Total Materia는 내부식용으로 적합한 다양한 국가와 규격 내 수천개의 재질에 대한 정보를 포함하고 있습니다.

재질의 화학적 조성, 기계적 특성, 물리적 특성, 고급 물성 데이터 등의 전체적인 특성 정보들을 어디서든 검토하실 수 있습니다.

고금 검색 내 규격 설명 기능을 이용하여, 규격 내 재질에 설명된 키워드를 통해 재질을 검색하실 수 있습니다.

검색 범위 좀 더 줄이기를 원하신다면 국가/규격과 같은 다른 조건을 지정할 수 있습니다.

검색 버튼을 클릭합니다.

선택된 정보에 부합하는 일련의 재질이 검색됩니다.

결과 리스트에서 재질을 선택하시면, 일련의 규격 사양 소그룹이 나타납니다.

여기에서 선택한 재질의 특정 특성 데이터를 검토하실 수도 있고, 강력한 상호 참조 표를 이용하여 유사 재질이나 등가 재질을 검토하는 것 또한 가능합니다.

예를 들어, 소그룹 내 화학적 조성 링크를 클릭하시면, 재질의 화학적 조성 데이터를 검토하실 수 있습니다.

Total Materia 데이터베이스를 사용해 보실 수 있는 기회가 있습니다. 저희는 Total Materia 무료 체험을 통해 150,000명 이상의 사용자가 이용하고 있는 커뮤니티로 귀하를 초대합니다.