Corrosion of Titanium Alloys: Part Two

요약:

In general titanium has excellent resistance against corrosion but this does not mean it is infallible and susceptibility still remains to a range of corrosive forces.
The main corrosion areas to be considered when dealing with titanium alloys are erosion corrosion, stress corrosion cracking, corrosion fatigue, and crevice corrosion.

Erosion Corrosion

Titanium has the ability to resist erosion by high velocity seawater. Velocities as high as 120 ft./sec. cause only a minimal rise in the erosion rate. The presence of abrasive particles, such as sand, has only a small effect on the corrosion resistance of titanium under conditions that are extremely detrimental to copper and aluminum base alloys. Titanium is considered one of the best cavitation-resistant materials available for seawater service.

Ti-3-2.5 shows excellent resistance to erosion in flowing seawater. Commercially pure titanium has been shown to be resistant to erosion in velocities up to 131 ft/sec (40 m/sec) even with 15 g/l of sand particles present. Ti-3-2.5 samples exhibited no signs of corrosion after a 30 day exposure in 320°F (160°C) flowing seawater with a flow rate of 10.2 ft/sec (3.1 m/sec).



Table 1: Corrosion Rate of Titanium Grade 2 Ti

Stress-Corrosion Cracking

Ti-3-2.5 shows excellent resistance to stress corrosion cracking (SCC) in hot chloride solutions. Grade 9 does not exhibit the kind of SCC problems which occur with higher strength titanium alloys and high oxygen commercially pure titanium.

Ti-3-2.5 U bend specimens have been tested for 440 days in boiling seawater without showing any signs of SCC. Samples run under the same conditions with 200 ppm of sulfide ion present in solution also showed no corrosion problems.

Corrosion Fatigue

Titanium, unlike many other materials, does not suffer a significant loss of fatigue properties in seawater. In fatigue- limited applications, Boiler Code criteria or actual in situ fatigue testing should be considered.

Crevice Corrosion

Titanium alloys may be subject to localized attack in tight crevices exposed to hot (>70°C) chloride, bromide, iodide, and fluoride, or sulfate-containing solutions. Crevices can stem from adhering process stream deposits or scales, metal-to-metal joints (for example, poor weld design or tube-to-tube sheet joints), and gasket-to-metal flange and other seal joints. Titanium alloys generally exhibits superior resistance to crevice corrosion as compared to stainless steel and nickel-base alloys.

In the chemical process industry and sea water desalination, crevice corrosion is the limiting factor for the application of titanium. Concentrated brines at high temperature and low pH values are characteristic of such media, where crevice corrosion is the predominant corrosion mechanism for titanium. Critical temperatures for the onset of crevice corrosion on Ti are thought to be above 80°C. In rare cases, crevice corrosion has been reported at lower temperatures, as for example for the alloy Ti-6Al-4V at 50°C in saturated NaCl solution (300 g/L as compared to 9 g/L for Ringer solution), and at pH 4.

Another case was reported for CP titanium in NaCl solution (60 g/L; pH6) under argon atmosphere. In this test, Ti specimens were exposed in the form of a compressed sandwich assembly, tightly sealed to styrene-acrylic-copolymer, into which NaCl crystals were embedded. In spite of these examples of deviations from the 80°C rule, it is still correct to assume that crevice corrosion will not occur under in vivo conditions.

On the one hand, the test conditions for the experiments described above are not comparable to those found in physiological systems: on the other hand, experience teaches us that crevice corrosion can start only if an acidic electrolyte (Ph<2) can form inside the crevice. The formation of such toxic conditions is not possible at the interface of titanium – this is a vital tissue.

Crevice corrosion of unalloyed titanium may occur in seawater at temperatures above the boiling point. TIMETAL Code-12 (Grade 12) and TIMETAL 50A Pd (Grades 7 and 16) and 35A Pd (Grades 11 and 17) offer resistance to crevice corrosion in seawater at temperatures up to 500°F (260°C).



Figure 2: Influence of temperature, concentration and pH on crevice and pitting corrosion of commercially pure titanium in sea water and sodium chloride brines

기술 자료 검색

검색할 어구를 입력하십시오:

검색 범위

본문
키워드

머릿글
요약

Total Materia는 내부식용으로 적합한 다양한 국가와 규격 내 수천개의 재질에 대한 정보를 포함하고 있습니다.

재질의 화학적 조성, 기계적 특성, 물리적 특성, 고급 물성 데이터 등의 전체적인 특성 정보들을 어디서든 검토하실 수 있습니다.

고금 검색 내 규격 설명 기능을 이용하여, 규격 내 재질에 설명된 키워드를 통해 재질을 검색하실 수 있습니다.

검색 범위 좀 더 줄이기를 원하신다면 국가/규격과 같은 다른 조건을 지정할 수 있습니다.

검색 버튼을 클릭합니다.


선택된 정보에 부합하는 일련의 재질이 검색됩니다.


결과 리스트에서 재질을 선택하시면, 일련의 규격 사양 소그룹이 나타납니다.

여기에서 선택한 재질의 특정 특성 데이터를 검토하실 수도 있고, 강력한 상호 참조 표를 이용하여 유사 재질이나 등가 재질을 검토하는 것 또한 가능합니다.


예를 들어, 소그룹 내 화학적 조성 링크를 클릭하시면, 재질의 화학적 조성 데이터를 검토하실 수 있습니다.


Total Materia 데이터베이스를 사용해 보실 수 있는 기회가 있습니다. 저희는 Total Materia 무료 체험을 통해 150,000명 이상의 사용자가 이용하고 있는 커뮤니티로 귀하를 초대합니다.