Master Alloys for Aluminum Alloys: Part Two

概要:

The article summarizes common additions are used for aluminum alloys, the engineering practice has acquired the following main addition methods for them, and recommendations, which should be kept in mind for selection of the master alloys and performing the aluminum alloy modification and grain refinement.

The following common additions are used for aluminum alloys, and the engineering practice has acquired the following main addition methods for them:

  • Boron is added to precipitate transition metal impurities such as Ti and V and so improve electrical properties. It is mainly added as a dilute master alloy <1% B). Originally borax (Na2B4O7), or B2O3 was added to the electrolytic cell, or KBF4 was added to the melting furnace to tie up transition metal impurities such as vanadium and titanium which adversely affect electrical conductivity of aluminum. These procedures resulted in cell contamination, or generation of toxic fumes and residual spent salt (KAlF4) in the melting furnace.
  • Bismuth is added both as the pure metal and as a dilute master alloy to enhance machinability of the aluminum alloys.
  • Chromium prevents grain growth in Al-Mg alloys, inhibits recrystallization in Al-Mg-Si and Al-Mg-Zn alloys, and corrects for Fe to produce a golden color in anodizing. The main addition form is the concentrated tablet or briquette, although a significant quantity is also added as dilute master alloy.
  • Copper is added mainly to increase strength, and it is added in many forms (pure metal, master alloys, concentrated tablets, and powder injection).
  • Iron improves the high-temperature strength of some kinds of alloys. Addition forms are similar to that for copper.
  • Magnesium provides high strength with good ductility, together with excellent corrosion resistance and weldability. For AI-Si alloys, it also improves heat treatment ability. It is mostly added as the pure metal, although master alloys are also widely used.
  • Manganese improves strength and also plays a role in preventing recrystallization. The main technique of addition is as concentrated tablets or briquettes, powder injection, and, to a lesser extent, master alloys.
  • Lead, like bismuth, is principally used to enhance machinability. The main method of addition is as the pure metal, although concentrated tablets and master alloys are also used.
  • Silicon is used in "foundry alloys" (silumines) as it gives excellent fluidity in casting. It is also used in extrusion alloys, to which it contributes high mechanical properties. The main method of addition is as pure metal, but significant amounts are added as master alloys and through powder injection.
  • Strontium is added to modify the eutectic in Al-Si alloys. It is mostly added as a dilute master alloy.
  • Titanium provides an important contribution to grain refinement. It is mainly added as tablets (including pure metal), but most often through master alloys.
  • Zinc is used to improve strength. It is almost exclusively added as the pure metal.
  • Zirconium is added to inhibit recrystallization. It is mainly added as a master alloy (up to 15% Zr), but also as a concentrated tablet.

Tabele 1. Aluminium Master Alloys.

The contents are summarized in the following statements or recommendations, which should be kept in mind for selection of the master alloys and performing the aluminum alloy modification and grain refinement. A good guideline rule tells us that there are no absolute guidelines, but all possible factors should be taken into account:

  • Aluminum alloy history (processing, impurities, possible metallurgical heritage, charge composition, i.e. scrap content, etc.).
  • Casting technology parameters (heating rate, overheating temperature, soaking time, pouring temperature, and soaking time at this point, crystallization rate at different parts of castings, etc.).
  • The results of the microstructural, macrostructural, and physical investigation, that is are the alloy processing parameters optimal from the point of view of grain size, mechanical properties, foundry defects, etc. If not, can temperature and time programs be adjusted, and what will the result be in that case.
  • When the optimal processing parameters are fixed, the selection of modifying master alloy(s) may be done on the basis of the most desired effect (grain size refinement, DAS decrease, strength and elongation increase, hardness adjustment, etc.)
  • The optimal amount of master alloy(s), introduction temperature and time, soaking, mixing, and pouring parameters have to be determined on the basis of target properties of castings. The formation of possible metastable phases and their influence on the morphology and microstructure of the final alloys should be taken into account. This requires more scientific effort to be applied to the problem before the operational window is set up for the casting process.

ナレッジベース検索

検索したい語句を入力:

検索方法

全文一致
キーワード

前方一致
要約

この記事は連載記事として掲載されております。詳細を見るには下記のリンクをクリックして下さい。

Total Materiaデータベースは世界の国々と広範な規格に関する数千種類のアルミ材料に関するデータを収録しております。

必要に応じて、化学組成分、機械的特性、物理特性、高度な特性等々の材料特性を御覧になれます。

高度な検索のページで材料グループのポップアップリストから’アルミニウム(Aluminum)’を選び検索条件を決定します。さらに国/規格のフィールドを使い検索条件を絞ることもできます。

確定をクリックします。


選んだ材料の材料リストが表示されます。


結果リストで材料をクリックすると規格から導きだされるサブグループリストが表示されます。

そこから選んだ材料の特性を見る事ができさらにパワフルな相互参照表により類似材料、同等材料をみることもできます。


対象とする材料の特性データをクリックします。




Total Materiaデータベースをあなたにテスト評価を頂くために15万人以上の方が登録されている無料お試しコミュニティ-へ御招待致します。