Atmospheric Corrosion of Aluminum Alloys

Abstrakt:

Relative humidity, temperature, sunshine, pollutants, salinity all play a significant role in the atmospheric corrosion rate of materials and when very specific conditions are taken into consideration e.g. subtropical marine environments, can result in some of the most extreme corrosion conditions possible.
As one of the most widely produced metals on the planet, aluminum is the subject of many investigations in this area with at times, some interesting results.

Except for ferrous metals, aluminum is one of the most produced metals globally. Aluminum has many advantageous properties such as lightness, suitability for surface treatments, functional advantages of extruded and cast semi-products, high thermal and electrical conductivity. Aluminum forms a diverse group of alloys, which gives a wide range of properties and uses. It is also easy to form and recycle; the recycling of aluminum requires only 5% of the energy it takes to extract the metal from its ore. Aluminum has good corrosion resistance, especially in the atmosphere, due to the natural oxide layer.

Atmospheric corrosion is one of the most common types of corrosion responsible for the degradation metallic structures, devices, and products exposed to the atmosphere. Atmospheric conditions such as relative humidity, temperature, sunshine period’s pollutants, salinity, etc. play an essential role in corrosion of the exposed metals. In particular, the tropical and subtropical marine environment introduces one of the most aggressive conditions which results in serious atmospheric corrosion of metals.

Aluminum is widely used in plenty of industrial applications such as construction, electrical engineering, transport, and especially in the food industry for the manufacture of processing, production, storage and transportation equipment and machinery.

In the paper of Li T. et al., corrosion product formed on 2A12 Al alloy after 3 months of exposure in South China Sea atmosphere was analyzed by various surface analysis techniques, including scanning electron microscopy (SEM), energy-dispersive x-ray analysis (EDXA), x-ray protoelectron spectroscopy (XPS), and x-ray diffraction (XRD). The mechanism for atmospheric corrosion of Al alloy in the tropical marine environment was analyzed too. The authors realized that the atmospheric exposure usually took 1 year or more for a study cycle. Furthermore, it is worth pointing out that there is no typical four-season climate in the test location.

Figure 1 shows the optical views of macroscopic morphology of the top and bottom of the Al alloy specimen after 3 months of atmospheric exposure. It is clear that the specimen was heavily corroded, with localized corrosion occurring on the specimen surface. Both views show that the specimen lost brightness and became rough, with a yellowish gray patina present on the surface. Moreover, corrosion of the Al alloy specimen on the bottom was more serious than that on the top section.



Figure 1: Optical views of surface morphology of top and bottom parts of Al alloy specimen after 3 months of exposure in Xi-Sha Island atmosphere

Durchforschen Sie bitte den Informationsteil der Datenbank

Geben Sie bitte eine Anfrage, um Suche einzuleiten:

Suche nach

Vollständiger Text
Schlüsselwörter

Überschriften
Abstracts

Die Total Materia Datenbank enthält viele korrosionsbeständige Werkstoffe aus vielen Ländern und Normen.

Wenn zur Verfügung stehend, können alle Informationen über die Werkstoffeigenschaften angezeigt werden, einschliesslich chemische Zusammensetzung, mechanische und physikalische Eigenschaften, vortschrittliche Daten und vieles mehr.

Auf der Seite der erweiterten Suche ist es möglich Werkstoffe nach Schlüsselwörtern ihrer Beschreibung mit Hilfe der Normbeschreibungsfunktion zu finden.

Es kann auch notwendig sein daß Sie Ihre Suche weiter einschränken indem Sie die anderen Felder der erweiterten Suche, wie z.B. Land/Norm benutzen.

Klicken Sie auf "Absenden".


Es wird danach eine Liste von Werkstoffen angezeigt von welcher Sie auswählen können.


Nachdem Sie auf der Ergebnisliste auf den entsprechenden Werkstoff geklickt haben, wird eine Liste der Untergruppen, welche Normspezifikationen sind, angezeigt.

Von hieraus ist es möglich, spezifische Eigenschaften für den ausgewählten Werkstoff anzuzeigen und äquivalente Werkstoffe mit unseren leistungsstarken Cross-Reference Tabellen zu finden.


Es ist, zum Beispiel möglich, durch klicken auf den entsprechenden Link, der Seite der Untergruppen, die chemische Zusammensetzung des erwünschten Werkstoffs anzuzeigen.


Um unsere Datenbank auszuprobieren, laden wir Sie ein sich unserer Nutzergemeinschaft von über 150 000 angemeldeten Benutzern, mit einem kostenlosen Probeaboanzuschliessen.