Engineering Stress-strain Curve: Part One

Sumário:

The engineering tension test is widely used to provide basic design information on the strength of materials and as an acceptance test for the specification of materials. In the tension test a specimen is subjected to a continually increasing uniaxial tensile force while simultaneous observations are made of the elongation of the specimen.

The shape and magnitude of the stress-strain curve of a metal will depend on its composition, heat treatment, prior history of plastic deformation, and the strain rate, temperature, and state of stress imposed during the testing. The parameters, which are used to describe the stress-strain curve of a metal, are the tensile strength, yield strength or yield point, percent elongation, and reduction of area. The first two are strength parameters; the last two indicate ductility.

An example of the engineering stress-strain curve for a typical engineering alloy is shown in Figure 1. From it some very important properties can be determined. The elastic modulus, the yield strength, the ultimate tensile strength, and the fracture strain are all clearly exhibited in an accurately constructed stress strain curve.


Figure 1: An example of the engineering stress strain curve for a typical engineering alloy

The elastic modulus, E (Young’s modulus) is the slope of the elastic portion of the curve (the steep, linear region) because E is the proportionality constant relating stress and strain during elastic deformation: σ = Eε.

The 0.2% offset yield strength is the stress value, σ0.2%YS of the intersection of a line (called the offset) constructed parallel to the elastic portion of the curve but offset to the right by a strain of 0.002. It represents the onset of plastic deformation.

The ultimate tensile strength is the engineering stress value or σuts, at the maximum of the engineering stress-strain curve. It represents the maximum load, for that original area, that the sample can sustain without undergoing the instability of necking, which will lead inexorably to fracture.

The fracture strain is the engineering strain value at which fracture occurred.

At the outset, though, a clear distinction must be made between a true stress-true strain curve and an engineering stress-engineering strain curve. The difference is shown in Figure 2, which are plotted, on the same axes, the stress-strain curve and engineering stress-strain curve for the same material. The difference is also evident in the definitions of true stress-true strain and engineering stress-engineering strain.


Figure 2: Comparison of engineering and true stress-strain curves

The engineering stress is the load borne by the sample divided by a constant, the original area. The true stress is the load borne by the sample divided by a variable the instantaneous area. Note that the true stress always rises in the plastic, whereas the engineering stress rises and then falls after going through a maximum.

The maximum represents a significant difference between the engineering stress-strain curve and the true stress-strain curve. In the engineering stress-strain curve, this point indicates the beginning of necking. The ultimate tensile strength is the maximum load measured in the tension test divided by the original area.

Procurar conhecimento básico

Colocar uma frase para procurar por:

Procurar por

Texto completo
Palavras chaves

Títulos
Resumo

Este artigo pertence a uma série de artigos. Você pode clicar nos links abaixo para ler mais sobre este tema.

A Total Materia Extended Range inclui uma coleção única de curvas tensão-deformação e diagramas para os cálculos na faixa de plástico para milhares de ligas de metal, tratamentos térmicos e temperaturas de trabalho. Curvas tensão verdadeira e engenharia são dadas para várias taxas de deformação quando aplicável.

Encontrar um gráfico de tensão-deformação no banco de dados é simples e leva apenas alguns segundos.

Digite o material de interesse no campo de pesquisa rápida. Você pode, opcionalmente, limitar a sua pesquisa, especificando o país / padrão de escolha no campo designado e então, clique em Pesquisar.


Depois de selecionar o material de seu interesse, clique no link diagramas de tensão-deformação para visualizar os dados para o material selecionado. O número de disponíveis diagramas de tensão-deformação é exibido entre parênteses ao lado do link.


Porque as curvas tensão-deformação da Total Materia são neutras em especificações padrão, pode rever tensão-diagramas, clicando no link apropriado para qualquer um dos subgrupos.

Além das curvas de tensão-deformação a diferentes temperaturas, o stress e os dados de deformação são dadas em um formato tabular que é conveniente para a cópia para, por exemplo, um software CAE.


É também possível ver curvas tensão-deformação e dados para outras temperaturas de trabalho.

Para isso, basta inserir uma nova temperatura no 'Enter temperatura' campo dentro do intervalo definido.

Após clicar no botão Calcular, uma nova curva é plotada e valores na tabela agora correspondem com a temperatura que você definiu. Veja o exemplo abaixo de 250°C.


Para você é uma oportunidade de fazer um test drive na Total Materia, nós convidamos você a participar de uma comunidade de mais de 150.000 usuários registrados através da Total Materia Free Trial.