Copper Bearing HSLA Steel: Part Two


The addition of copper in HSLA steels has been found to greatly benefit the strength levels of steels used for among other applications, offshore structures, pipelines and ship hulls.
In combination with copper additions, low carbon content is also essential for attaining the desired effects and during the last three decades, research has also extended to comparing the benefits of hot rolling versus quenching and tempering to make further gains in quality of the material properties.

Copper containing High Strength Low Alloy (HSLA) steels, typically HSLA-80 and HSLA-100, are of particular interest for large submarine and offshore structures, pipelines, hulls of ships, etc. and these applications often demand a combination of strength, toughness and weldability.

In order to attain the desired properties, several alloying elements, such as Mn, Cu, Ni, Cr, Mo, Nb etc., are added to exploit the benefits from the alloy chemistry. However, for obtaining a very high strength level (i.e. 550MPa in HSLA- 80 and 690MPa in HSLA-100) copper addition plays a crucial role, as it contributes to strength through the precipitation hardening process. The amount of copper precipitating as well as its size and morphology govern the properties of the copper bearing steel.

During the last three decades, several high yield steels (HY-80, HY-100 and HY-130) were developed for submarine-hull plate and hydrofoil applications. These are generally quenched and tempered (Q & T) steels and possess high strength (80–130 ksi YS) due to their martensitic structure. However, owing to the high carbon level, the weldability of these steels was not sufficient.

Over the past three decades, considerable research has been directed to increase the strength level of the steels in combination with good toughness and weldability through newer alloy design and processing routes. Reduction in carbon level is essential for improved toughness and better weldability. In the early 1980s, the US navy developed low carbon Cu bearing HSLA steels (HSLA-100 and -80) as a replacement to HY-100 and -80 steels.

The low carbon content in these steels is compensated by adding an increased amount of alloying elements like Ni, Mn, Cr and Mo to increase the hardenability of austenite. Microalloying elements i.e. Ti, Nb or V, which are incidentally a strong carbide former and also act as a grain refiner while in solution in austenite, are also added in these steels. On subsequent cooling, these microalloying elements precipitate as carbides and/or carbonitrides. These precipitates are fine enough to offer a hindrance to mobile dislocations leading to a significant increase in strength. An additional strengthening is obtained from fine ε-Cu particles upon ageing.

Thermo-mechanical controlled processing (TMCP) is another technique, which enhance the strength level of HSLA steels by prior austenite grain refinement, precipitation hardening together with dislocation sub structure strengthening.

Currently, there is a strong interest to develop the high strength steels in hot-rolled condition as a substitute of quenched and tempered steels to reduce the production cost. Moreover, some metallurgical defects like quench cracking, distortion or residual stress associated with the latter is also minimized. The developments in the area of high performance structural steel were demonstrated in several research papers of a conference held in 1995 in Ohio, USA. A few attempts were made to replace HY-130 steel with newer alloy design and lower carbon content for better weldability and improved toughness. However, research in this area is still in progress to meet the target requirements.

Continuous cooling transformation behavior

To better understand the response of characteristics of austenite decomposition, CCT diagrams were developed for three of the alloys: HSLA-80, A710 Modified and HSLA-100 with 0.06%C. These diagrams are useful for understanding the transformation response of these alloys to water quenching of carious plate thicknesses from austenitizing temperatures. The CCT work was performed on a Gleeble 1500 machine. The specimens used in the study were 6.35 mm round and 101.6 mm in length.

Figure 1: Continuous Cooling Transformation diagram for HSLA – 80 steel: A=austenite, PF=Proeutectoid Ferrite, AF=Acicular Ferrite, UB=Upper Bainite, Ms=Martensite Start

Figure 2: Continuous Cooling Transformation Diagram for A710 Modified: M-Martensite, GB-Granular Bainite

Figure 3: Continuous Cooling Transformation diagram for HSLA – 100 steel


1. Bhagat A.N., Pabi S.K., Ranganathan S., Mohanty O.N.: Aging Behaviour in Copper Bearing High Strength Low Alloy Steels, ISIJ International, Vol. 44, 2004, No. 1, p. 115–122

2. Ghosh A., Mishra B., Das S., Chatterjee S.: Structure and properties of a low carbon Cu bearing high strength steel, Materials Science and Engineering A 396, 2005, p. 320–332

3. Wilson A.D., Hamburg E.G., Colvin D.J., Thompson S.W., Krauss G.: Properties and microstructures of copper precipitation aged plate steels, Accessed 06-2013

Procurar conhecimento básico

Colocar uma frase para procurar por:

Procurar por

Texto completo
Palavras chaves


Este artigo pertence a uma série de artigos. Você pode clicar nos links abaixo para ler mais sobre este tema.

Diagramas de tratamento térmico estão disponíveis para um grande número de matérias no banco de dados da Total Materia.

Diagramas de tratamento térmico abrangendo temperabilidade têmpera dureza, TTT e CCT podem ser encontrados no conjunto de dados padrão.

Para selecionar materiais por propriedades especiais, você pode usar as caixas de seleção especiais de busca no módulo de Pesquisa Avançada.

Para definir os critérios de pesquisa, tudo que você tem a fazer é selecionar o país / padrão do seu interesse a partir do "País / Standard 'lista pop-up e para a caixa de verificação' Diagrama de Tratamento Térmico", situado na área de Pesquisa Especial do formar-se na parte inferior da página de pesquisa avançada.

Clique em Enviar.

Depois de selecionar o material de seu interesse, clique no link Tratamento Térmico para visualizar os dados para o material selecionado. O número de registos de tratamento térmico é apresentado entre parêntesis ao lado da ligação.

Todas as informações disponíveis de tratamento de calor será exibida para o material escolhido.

Para você é uma oportunidade de fazer um test drive na Total Materia, nós convidamos você a participar de uma comunidade de mais de 150.000 usuários registrados através da Total Materia Free Trial.