Metallography: Part One

Sumário:

Microstructural examinations and visual evaluations of fracture surfaces provide an invaluable insight into the mechanism of component and assembly failures.
Typically, the metallography process uses sample specimens removed and mounted in bakelite plastic. The specimens are then ground to a fine finish with sandpaper and then polished to a mirror finish with diamond or alumina polishing materials.

Metallography is an informative tool in the processing of materials. It is essential in helping classify material problems and failures. Microstructural examinations and visual evaluations of fracture surfaces provide an invaluable insight into the mechanism of component and assembly failures. Metallurgical examination is a required tool for welders and also procedure qualification.

Metallography can also be classified as the characterization of the structure and substructure of metals, usually with a focus on examining the grains, phases, inclusions, defects, and other details. Traditionally, metallography is performed with optical microscopy, electron microscopy, and X-ray diffraction to identify and characterize different crystalline phases and other critical materials properties that are invisible to the naked eye.

The first step is cutting a specimen and mounting it, typically in plastic (Bakelite) or epoxy. The mounted specimen is ground with successively finer grits of sandpaper until the surface is relatively smooth, at which point silica, alumina, or diamond polishes are normally used to achieve a mirror-like finish. Chemical or electrochemical etching of the surface is then performed; depending on the method chosen, a variety of details can be identified and characterized. Color etchants may also be used to further distinguish the important constituents of the metal. Finally, microscopy, x-ray diffraction, and other characterization techniques are used to evaluate the critical details at magnification levels from 1 to 200,000X. X-ray diffraction utilizes a measurement of the diffraction pattern of an x-ray beam from the crystal lattice to assess the phases present, crystallinity, stresses, and other characteristics of crystalline materials.

At this point, photomicrographs are taken using high-quality microscopes to provide accurate and extensive characterization of the microstructure and other properties of the specimens. Three different steel compositions are shown below, with varied phases, precipitates, and other features that are highlighted by high-quality metallography.

Etchant Composition Conc. Conditions Comments
Nital Ethanol
Nitric acid
100 ml
1-10 ml
Immersion up to a few minutes. Most common etchant for Fe, carbon and alloys steels and cast iron - Immerse sample up from seconds to minutes; Mn-Fe, MnNi, Mn-Cu, Mn-Co alloys.
Murakami's K3Fe(CN)6
KOH
Water
10 grams
10 grams
100 ml
Pre-mix KOH and water before adding K3Fe(CN)6 Cr and alloys (use fresh and immerse); iron and steels reveals carbides; Mo and alloys uses fresh and immerse; Ni-Cu alloys for alpha phases use at 75 Celcius; W and alloys use fresh and immerse; WC-Co and complex sintered carbides.
Picral Ethanol
Picric acid
100 ml
2-4 grams
Seconds to minutes
Do not let etchant crystallize or dry –explosive
Recommended for microstructures containing ferrite, carbide, pearlite, martensite and bainite. Also useful for magnetic alloys, cast iron, high alloy stainless steels and magnesium.
Vilella’s Reagent Picric Acid
Hydrochloric acid
Ethanol
1 gram
5 ml
100 ml
Seconds to minutes Good for ferrite-carbide structures (tempered martensite) in iron and steel.

Table 1: The following table lists the most commonly used etchants

TYPICAL APPLICATIONS OF METALLOGRAPHY

  • Metal alloy heat treatment verification
  • Coating thickness measurement
  • Weld or braze joint evaluation
  • Case hardening depth determination
  • Corrosion resistance evaluation
  • Failure analysis
  • Microscopic defects in IC devices
  • In situ evaluation of thermo-mechanical degradation



Figure 1: Martenzite



Figure 2: 1.3%C: Cementite precipitates at austenite grain boundaries, remaining austenite is transformed into pearlite



Figure 3: Some of the Equipment examples used for metallography

Procurar conhecimento básico

Colocar uma frase para procurar por:

Procurar por

Texto completo
Palavras chaves

Títulos
Resumo

Este artigo pertence a uma série de artigos. Você pode clicar nos links abaixo para ler mais sobre este tema.

O banco de dados da Total Materia contém um grande número de imagens metalografia através de uma gama grande de países e padrões.

Usando o guia Metalografia projetado especificamente na barra de menu, você pode selecionar o material de seu interesse a partir da lista de materiais com dados metalografia incluído.

Metalografia dados também podem ser encontradas através do nosso padrão de pesquisa rápida e irá mostrar os dados relevantes são disponíveis através da página Subgrupo padrão para o material de interesse.

Basta digitar a sua designação de material para o 'Material' campo e selecione o padrão de juros, se conhecido, em seguida, clique em "Procurar".


As informações gerais sobre microestrutura pode ser encontrada, juntamente com a composição química relevante para o material de interesse.


Quando disponível, uma série de imagens será fornecido a exibir uma gama de detalhe estrutural em vários níveis de ampliação.

Também é possível selecionar opções diferentes de condição de suspensa a 'condição Selecionar' para mostrar imagens metalografia em processo diferente e estados de tratamento térmico.



Para você é uma oportunidade de fazer um test drive na Total Materia, nós convidamos você a participar de uma comunidade de mais de 150.000 usuários registrados através da Total Materia Free Trial.