The Steel Carburizing Process: Part One


Steel carburizing is a process whereby carbon is diffused into the surface of steel (usually low-carbon steel) at high temperatures where austenite is present and the diffusion rate of carbon in steel is reasonably high.
Each with their own specific characteristics, there are five main carburizing methods; pack, gas, liquid bath, vacuum, and plasma carburizing.

Process Carburizing, sometimes called cementation, is a process where carbon is diffused into the surface of a steel (usually a low-carbon steel) at a temperature well above the AC3 where austenite is present and the diffusion rate of carbon in steel is reasonably high. The carbon content increases according to the diffusion rate at the chosen temperature (generally 1700 to 1750°F, or 930 to 955°C) and the nature of the carbonaceous media used. However, the carbon content in the case will not exceed the carbon content of austenite defined by the Acm line. However, for alloy steels, particularly tool steels, the carbon content at the surface can easily exceed 3% after carburizing.

There are five carburizing methods—pack, gas, liquid bath, vacuum, and plasma. Pack carburizing uses a furnace to heat the metal parts to be carburized that are packed inside a container with a sufficient amount of carbon powder. The heating process will last for 12 to 72 hours at a high temperature. This method is noted to be slow compared to the other methods and has heating inefficiencies because of the difficulty in maintaining an even temperature. Gas carburizing follows the same procedure applied in pack carburizing. It, however, feeds carbon monoxide (CO) to the furnace to improve diffusion, which is not done in the pack method. The process has safety issues because CO is a poisoning gas that is odorless and colorless and could be inhaled by persons working inside the plant. The gas method is preferred in carburizing large volumes of metal.

Carburizing is one of the most widely used surface hardening technique. As mentioned above, the process involves diffusing carbon in to low carbon steel alloy to form a high carbon steel surface. Carburizing steel is widely used as a material of machines, gears, springs, automobiles and wires which are required to have high strength, toughness, hardness and wear resistance. These mechanical properties and wear properties can be obtained from the carburization and quenching processes.

The key to the successful improvement in carburizing, however, is understanding, and interpreting the microstructure of the carburized case.

To illustrate the carburizing behavior of the steels, in the paper of L.-D. Liu, F.-S. Chen, three commercial steels, JIS SCM 415, JIS SNCM 220 and AISI 1008 were carburized in a two-chamber vacuum furnace at temperature ranging between 900°C and 1050°C in an acetylene atmosphere. Steel SCM 415 consists of mainly 0.12% C, 1.0% Cr and 0.17% Mo, steel SNCM 220 consists of 0.18% C, 0.55% Mo, 0.42% Cr and 0.17% Mo, while steel AISI 1008 is a 0.058% C plain carbon steel. The carburized specimens were characterized for the hardness distribution and the microstructure of the carburized layers using thermodynamic analysis. Experimental results show that, under the same treatment conditions, the SNCM 220 steel exhibited the best performance in both the effective case depth (ECD) and total case depth (TCD) of the carburized layers. However, the carbon concentration in the carburized surface of the SCM 415 steel was higher than that for the SNCM 220 steel. The AISI 1008 steel was the worst among the steels investigated. Furthermore, the carbon potential of the atmosphere for the SCM 415 steel should be controlled lower than that for the SNCM 220 steel if the same carbon concentration in the work surface is an essential requirement. The plain carbon steel AISI 1008 required the highest carbon potential among the three steels.

Figure 1: The cross-sectional metallographic pictures of the carburized layer of specimens: (A) AISI 1008 (B) SNCM 220 (C) SCM 415. The carburizing was conducted at 1000°C for 1 h at 5 Torr acetylene pressure. After carburizing, the specimens were held at 830°C for 20 min and then quenched into an 80°C oil bath and followed by 2 h×180°C tempering.

Figure 2: Variation of hardness with the carburization temperature

Figure 3: Variation of tensile strength with carburization temperature


1. G.F.Vander Voort, G.M.Lukas: Microstructural characterization of carburized steels, Heat Treating Progress, September 2009, p.37-42;

2. H.Elzanaty: Effect of Carburization on the Mechanical Properties of the Mild Steel, International Journal of Innovation and Applied Studies ISSN 2028-9324 Vol. 6 No. 4 July 2014, p. 987-994;

3. R. R. Panda, A.M Mohanty, D.K Mohanta: Mechanical and Wear Properties of Carburized Low Carbon Steel Samples, International Journal of Multidisciplinary and Current Research, Jan/Feb 2014, ISSN: 2321-3124;

4. G. Fillari, T. Murphy, I. Gabrielov: Effect of Case Carburizing on Mechanical Properties And Fatigue Endurance Limits of P/M Steels, Accessed March 2018;

5. L.-D. Liu, F.-S. Chen: The influences of alloy elements on the carburized layer in steels using vacuum carburization in an acetylene atmosphere, Materials Chemistry and Physics 82, 2003, p. 288–294.

기술 자료 검색

검색할 어구를 입력하십시오:

검색 범위



열처리 도표는 Total Materia 데이터베이스 내 많은 재질에서 검토하실 수 있습니다.

열처리 도표는 경화도, 경도 탬퍼링, TTT 및 CCT를 포함하며 모두 규격 데이터에서 검색하실 수 있습니다.

특수 속성 자료를 선택하려면, 고급 검색 모듈에서 특수 검색 기능을 사용하시면 됩니다.

검색 조건을 정의하려면, '국가/규격' 목록에서 귀하에게 관심 국가/규격을 선택하고 특별 검색 영역에 위치한 '열처리 도표' 박스를 체크하는 것입니다. 이는 고급 검색 페이지의 하단 부분에 있습니다.

검색 버튼을 클릭합니다.

관심 소재를 선택 후, 선택된 소재의 열처리 데이터 링크를 클릭하십시오. 열처리 기록의 개수는 링크 옆 괄호 안에 표시됩니다.

선택된 자료의 사용 가능한 모든 열처리 정보가 표시됩니다.

Total Materia 데이터베이스를 사용해 보실 수 있는 기회가 있습니다. 저희는 Total Materia 무료 체험을 통해 150,000명 이상의 사용자가 이용하고 있는 커뮤니티로 귀하를 초대합니다.