High Boron Cast Iron: Part One

요약:

Boride emerged as a good alloying option for iron based alloys to help improve toughness and specifically help in applications where wear resistance is important.
The addition of boron causes martensite transformation to a mixed state with austenite and this provides the platform for improved overall toughness in the material.

Among iron-based wear-resistant materials, there has been a lot of research and application for white cast iron alloyed with carbide; however, low toughness limits their application range. In recent years, much attention has been paid to iron-based alloys that include boride in the wear-resistant phases. Compared with carbide, boride is much harder and has better heat stability, so it can be used as a wear-resistant phase.

Boron is interesting as an alloying element in chromium white irons. It is more known as a micro-alloying element of steel, where it is applied in the amounts of several tens to several hundreds of ppm-s. There, its role is to ensure the necessary hardenability of austenite. However, since the application of carbidizing elements has become popular in the investigation practice of improving the properties of chromium white irons properties, it became normal to perform experiments with boron, bearing in mind its properties, especially the structural and electrochemical ones.

Sources of boron contamination, in addition to steel scrap, may include boron pickup from refractory linings and silicon carbide charge materials. The technical literature relating to the effects of boron on the mechanical properties of ductile iron are somewhat conflicting. Very low levels of boron have been reported to act as carbide stabilizers and promote pearlite while recently others have reported just the opposite effect. Boron levels in the range of 0.0011% to 0.0020% (11 to 20 ppm’s) reduce pearlite levels in pearlitic ductile irons and reduce Brinell hardness levels (BHN). Large quantities of pearlite stabilizing elements such as copper and tin are required to return to normal hardness and microstructures.

The effect of boron, in the amounts of 0.26, 0.39, and 0.59 wt.%, on the volume fraction and structure of carbides in Cr white irons was examined in the paper S. M. Tomović-Petrović, S.V. Marković, S. Zec. It was demonstrated that the addition of boron can change the microstructural characteristics of white iron containing about 13 wt.% Cr. With increasing boron content, the volume fractions of M3C carbide increase, but the volume fracton of M7C3 carbide remains unchanged. The addition of boron tends to produce hard borides and/or borocarbides. It also prevents the formation of pearlite, which results in alloys possessing good wear resistance.

The microstructures of the examined alloys are shown in Figure 1. Detailed analysis confirmed that the structure obtained in this investigation is typical for chromium white cast iron. The base alloy (No. 1) is characterized by the presence of primary austenitic dendrite and a eutectic that consists of eutectic carbides and eutectic austenite. The structure of the other alloys also consists of a primary phase and an eutectic, but the following differences can be noticed:

  • With increasing boron content, the dendritic structure slowly disappears, while the primary phase obtains the form of isolated islands surrounded by the eutectic (Figure 1–c, e, g).
  • In the presence of boron, the primary phase becomes a mixture of austenite and martensite. The degree of martensite tranformation increases with increasing boron content. The development of this transformation can be seen on the SE microphotographs (Fig. 1 – d, f, h).



Figure 1: Microstructure: a), b) – alloy No. 1; c), d) – alloy No. 2; e), f) – alloy No. 3; g), h) – alloy No. 4 (a, c, e, g – optical microphotographs; b, d, f, h – SEM).


References

1. Z. Liu, Y. Li, X. Chen: Effect of tempering temperature on microstructure and mechanical properties of high boron white cast iron, China Foundry, November 2012, p.313-317;

2. S. M. Tomović-Petrović, S.V.Marković, S.Zec: The effect of boron on the amount and type of carbides in chromium white irons, J. Serb. Chem. Soc. 67, (10), 2002, p. 697–707, UDC 546.27:549.261+546.76;

3. R. L. Naro, J. F. Wallace, Y.Zhu: Elimination and neutralization of boron in ductile irons, Accessed April 2018;

기술 자료 검색

검색할 어구를 입력하십시오:

검색 범위

본문
키워드

머릿글
요약

Total Materia는 다양한 나라와 규격에 따른 금속학 이미지에 대한 정보를 포함하고 있습니다.

메뉴 표시줄에 특별히 디자인된 금속학 탭을 이용하여, 금속학 데이터가 포함된 관심 재질을 리스트에서 선택하실 수 있습니다.

또한 금속학 데이터는 표준 빠른 검색을 통해 찾을 수 있으며 규격 내 소그룹 페이지를 통해 이용 가능한 관련 자료들이 표시됩니다.

재질명을 '재질'창에 입력하신 후 규격을 알고 계신다면 규격을 선택하고 '검색' 버튼을 클릭합니다.


미세 구조에 대한 일반적인 정보가 관련 관심 재질의 화학 조성과 함께 출력됩니다.


구조의 세부 범위를 보여주는 여러 배율에서의 이미지가 가능하다면 제공됩니다.

다양한 조건을 선택할 수 있으며, '조건 선택' 메뉴를 사용하여 다양한 공정 및 열처리에 따른 금속학 이미지를 보여줍니다.



Total Materia 데이터베이스를 사용해 보실 수 있는 기회가 있습니다. 저희는 Total Materia 무료 체험을 통해 150,000명 이상의 사용자가 이용하고 있는 커뮤니티로 귀하를 초대합니다.