Spark Plasma Sintering (SPS) is a sintering technique which is well matched to mechanically milled materials such as tool steels due to its low temperature and short cycle time.
Tool steels have been specifically manufactured to exhibit exceptionally high strain hardening, a characteristic which can be undone by high temperature sintering processes such as hot isostatic pressing.

Powder metallurgy is a well consolidated route to produce tool steels. The conventional process, involving the consolidation of atomized powders by hot isostatic pressing (HIP) followed by thermomechanical processing (extrusion, forging…) and final heat treatment leads to a finer microstructure and improved properties than similar wrought grades obtained from ingots.

Tool steel microstructures can be further refined by mechanical milling. The repeated impacts between powder particles and the balls/vial cause fragmentation and induce a high defects density. The crystallite size is progressively reduced down to nanometric scale and considerable strain hardening is observed.

During sintering, recrystallization is generally easier that in unmilled powders, according to the higher internal energy of the system. Sintering techniques assisted by pulsed current, like Spark Plasma Sintering (SPS), permits to get near full dense materials at lower temperature and for shorter time than HIP. This allows to preserve parts of the benefits induced by mechanical milling, leading to a very fine microstructure of the consolidated steels.

Spark plasma sintering (SPS) is a relatively new compaction technique which utilizes the heat generated in the sintering system when a pulsed DC current passes through both electrically conducting graphite dies and the conducting powders to be compacted. For non-conducting powders, only the graphite die and punches heated due to resistance act as the heat source. A schematic diagram depicting the main parts of SPS system is shown in Figure 1.

The powder to be compacted is loaded into a die usually made of graphite. The employment of graphite as the material for punches and dies limits the external sintering pressure to a value of 100 MPa. The pressure applied during compaction is uniaxial, which can be maintained at a constant value or changed in the subsequent stages. The sintering temperature is measured using a thermocouple inserted through a horizontal die-hole about 1-2 mm away from the loaded powders.

Sintering is carried out under any one of the commonly used environments including vacuum, air, nitrogen and argon. The heat generated in the system by ON-OFF DC pulse voltage and a current from a pulse generator and high applied mechanical stress activates diffusion-oriented processes and the electric field present in the system enhances the diffusion rate. Therefore, very dense components can be produced at comparatively low temperature in short duration.

Figure 1:Schematic representation of SPS system

Spark plasma sintering (SPS), also called Field Assisted Sintering Technique (FAST), represents a novel method of preparation of sintered materials from powders. The main advantage of the SPS method is a high achievable heat rate (>200° C/min) and high sintering temperatures (up to 2200°C). Combination of high heating rate, rather high pressures (up to 80 MPa) and electric field fluctuations leads to an effective sintering and significant reduction of sintering time for both coarse-grained and nanocrystalline powders. Composite materials may be easily obtained by mixing or layering of different powders.


1. M. Pellizzari , A. Fedrizzi , T. Gebremariam Kotecho, F. Deirmina , M. Zadra: Design of novel tool steels by Mechanical Milling and Spark Plasma Sintering, Accessed Dec 2017;

2. M.Kumar Mani: Development of Fe-50Co Alloy and its Composites by Spark Plasma Sintering, Wolfson Centre for Magnetics Cardiff School of Engineering Cardiff University Wales, United Kingdom, January 2014, Accessed Dec 2017;

3. R. Musálek, Z. Dlábaček, M. Vilémová, Z. Pala, J. Matĕjiček, T. Chráska: Preparation of multiphase materials with spark plasma sintering, METAL 2013, 15. - 17. 5. 2013, Brno, Czech Republic, EU, Accessed Dec 2017.

기술 자료 검색

검색할 어구를 입력하십시오:

검색 범위



Total Materia는 용접용으로 적합한 다양한 국가와 규격 내 수천개의 재질에 대한 정보를 포함하고 있습니다.

재질의 화학적 조성, 기계적 특성, 물리적 특성, 탄소 등가 데이터와 용접용으로 재질 이용 시 필요한 정보 등의 전체적인 특성 정보들을 어디서든 검토하실 수 있습니다.

고급 검색을 이용하여, 검색 조건의 재질 리스트에서 '용접 필러 재료'를 선택합니다. 검색 범위 좀 더 줄이기를 원하신다면 국가/규격과 같은 다른 조건을 지정할 수 있습니다.

검색 버튼을 클릭합니다.

선택된 정보에 부합하는 일련의 재질이 검색됩니다.

결과 리스트에서 재질을 선택하시면, 일련의 규격 사양 소그룹이 나타납니다.

여기에서 선택한 재질의 특정 특성 데이터를 검토하실 수도 있고, 강력한 상호 참조 표를 이용하여 유사 재질이나 등가 재질을 검토하는 것 또한 가능합니다.

자세한 특성 데이터를 보시려면 특성 데이터 링크를 클릭하세요.

Total Materia 데이터베이스를 사용해 보실 수 있는 기회가 있습니다. 저희는 Total Materia 무료 체험을 통해 150,000명 이상의 사용자가 이용하고 있는 커뮤니티로 귀하를 초대합니다.