요약:

Electroslag remelting can be summarized as a secondary refining process through consumable electrode remelting.
Characteristics of slag with ample refining ability include optimal electrical resistance, low viscosity, stable content and a low original content of hydrogen.

Conventional steels are produced using secondary metallurgical processes like BOF and EAF with subsequent treatment in ladle using Ladle furnace (LF) and vacuum degassing systems (VD, RH, etc). At the end of the refining the liquid will be casted using top and bottom pouring to produce ingots or billets using the continuous casting process with all its limitations in refining of the material and solidification structure in the final product.

Nowadays it has not been possible to meet the increasingly stringent requirements with regard to gas content, cleanliness, and homogeneity either with conventional melting and casting processes or with the vacuum induction furnace alone. Therefore ingots or billets casted in the conventional secondary metallurgy with top shrinkage cavity can be used for further processing in re-melting technology to achieve additional refinement of the structure and increase the cleanliness of the end product. Re-melting furnace like Electro Slag Remelting (ESR) can be used to achieve best material quality.

ESR (Electroslag remelting) is the abbreviated name given to electroslag consumable electrode remelting and secondary refining process. It is also used to describe three separate processes, using the principle of electroslag namely (i) consumable electrode metal refining and cost structure improvement process (ii) the semi-continuous or continuous alloy making process and (iii) the bulk metal deposit process for rebuilding worn parts and joining very heavy metal sections.

The history of slag for ESR began with the fluorine slag on the basis of the fluorspar, the main component of which is calcium fluoride. CaF2 makes a melt which has good electro conductivity (mostly ionic type) and sufficient resistance, excellent fluidity, does not create non-stable modifications under temperatures of the process and does not oxidize the metal. But it is expensive, deficient and ecologically harmful.

The most widespread are the slags of the CaF2-CaO-Al2O3 system in different ratios of their elements with the addition of SiO2, MgO and others. The diversity of the contents is quite large, as each manufacturer introduces their own contents which slightly vary, but have different markings. The properties of oxygen fluoride slag, naturally, depend on its content. To the common differentiating features belong a wider interval of solidification and a higher oxidizing in comparison to the slag from fluorspar.

Today the slag should provide not only the refining of metal (by the way, one of the names of the process in English speaking literature is “electroslag refining”) by reducing the content of admixtures, but also the preserving the chemical content of metal and preventing the loss of alloying elements, that is, taking into account the modern achievements of secondary metallurgy the requirements to the refining ability at ESR may be significantly lowered.

Thus, the slag should have a sufficient (taken into consideration the purity of a consumable electrode) refining ability for the fullest deletion of sulphur, gases and nonmetal inclusions and serve as a firm barrier for the transferring from the atmosphere into the metal bath of oxygen, nitrogen and hydrogen.

A slag should have:

  • an optimal electric resistance, providing the sufficient production of the heat in the slag bath;
  • a low viscosity, slightly increasing with the lowering of temperature, a high interfacial tension on the boundary with metal melt and minimal one on the boundaries with non-metal inclusion;
  • a stable content that under the condition of significant overheat its liquidus did not change over a lengthy period of melting (dozens to hundreds of hours) or could be easily corrected;
  • a low original content of hydrogen (it should be provided by the technology of melting in the fluxmelting furnace irrespective of the humidity of original mixture and air, degree of component reduction and carbonization) and the absence of crystallization water and adsorbed humidity.

Formed on the surface of ingot the slag skull should have a small thickness (1-3 mm), as its increase lowers the heat emission from the ingot and increases the slag consumption:

  • be dense and have a good metal adhesion to the temperatures of the end of the process of the slow ingot cooling in order to isolate the surface from the oxidizing and forming the oxide during the lengthy contact of the ingot with the atmosphere;
  • easily peel off after the cooling of the ingot or disintegrate into powder.

All these requirements often contradict each other in practice, and it is quite difficult or almost impossible to create the slag which would meet all of them. Nevertheless in every specific case it is possible to find a slag that would meet the most important requirements.

기술 자료 검색

검색할 어구를 입력하십시오:

검색 범위

본문
키워드

머릿글
요약

화학 조성을 Total Materia 데이터베이스에서 검색하는 것은 매우 쉽습니다.

몇 초 내로 데이터베이스 내 175,000개 이상의 재질에서 유용한 화학 조성 데이터를 검색하는 것이 가능합니다.

신속 검색에 검색할 재질명을 입력합니다. 원하신다면 국가/규격을 지정하신 후 검색 버튼을 클릭합니다.


Total Materia 데이터베이스에서 검색된 관심 재질의 목록이 즉시 생성됩니다.
관심 재질을 클릭합니다.


소그룹 페이지에서, 선택된 재질의 화학 조성 링크를 클릭하여 데이터를 검토합니다. 화학 조성 데이터 기록의 개수는 링크 옆 괄호 안에 표시됩니다.


화학 조성 데이터는 참조를 위해 선택한 모든 재질 정보와 함께 표시됩니다.


Total Materia 데이터베이스를 사용해 보실 수 있는 기회가 있습니다. 저희는 Total Materia 무료 체험을 통해 150,000명 이상의 사용자가 이용하고 있는 커뮤니티로 귀하를 초대합니다.