Testing Methods for JIS Steel Materials

요약:

Tensile test is the most widely used test to determine the mechanical properties of materials. In this test, a piece of material is pulled until it fractures.

Strain and stress are calculated from these values, and are used to construct a stress-strain curve. From this curve, the elastic modulus and yield strength are determined.

The tensile test is the most widely used test to determine the mechanical properties of materials. In this test, a piece of material is pulled until it fractures. During the test, the specimen elongation and applied load is measured. Strain and stress are calculated from these values, and are used to construct a stress-strain curve. From this curve, the elastic modulus and yield strength are determined.

The highest load in the tensile test gives the tensile or ultimate strength. After fracture, the final length and cross-sectional area of the specimen are used to calculate the percent elongation and percent reduction of area, respectively. These quantities indicate the ductility of the material. By using the instantaneous length and cross-sectional area, the true stress and true plastic strain are calculated from the load and elongation.

The strain hardening properties of the material are then determined from a log-log plot of the true stress vs. the true plastic strain. Thus, from one test a large amount of information can be obtained about the mechanical properties of a material.

Numerous groups have developed standard methods for conducting the tensile test. In the United States, standards published by ASTM are commonly used to define tensile-test procedures and parameters. Standard Methods for conducting the tensile test are also available from other standards organizations, such as the Japanese Industrial Standards (JIS), the Deutsche Institut für Normung (DIN), and the International Organization for Standardization (ISO). Other domestic technical groups in the United States have developed standards, but in general, these are based on ASTM E.8.

Typical test pieces are shown below. They are normally circular, but may be flat. The standard diameter is 12.5mm.



Figure 1: Typical test pieces



Figure 2: Unstretched and full stretched specimens



Figure 3: Test pieces after tensile testing

The tensile test piece is mounted into the grips of the tensile test machine. The grips are moved apart at a constant rate and the applied load is measured by a load cell while the extension is measured by an extensometer.



Figure 4: Tensile test machine

The test is normally destructive - the test piece is permanently deformed and usually fractured in the test.

This Japanese Industrial Standard specifies test pieces for tensile test for metallic materials (hereafter referred to as “test piece”). The type of test piece depends upon the form and size and these are generally classified into the proportional test piece and the non-proportional piece as described in Table 1.

Table 1: Classification of test piece

Form of test piece Flat form test piece Bar form test piece Tubular form test piece Arc section test piece Wire form test piece
Proportional test piece N°14B N°2; N°14A N°14C N°14B  
Non-proportional test piece N°1A; N°1B; N°5; N°13A; N°13B N°4; N°10; N°8A; N°8B; N°8C; N°8D N°11 N°12A; N°12B; N°12C N°9A; N°9B

The selection of the type of test piece to be used shall be in accordance with the requirements of the standard for that particular material, but it is recommended to be selected as given in Table 2.

Table 2: Classification of test piece

Material Test Piece Remarks
Form Dimensions Proportional Non-proportional
Sheet, Plate, Shape, Strip *t > 40 N°14A N°4; N°10 For bar form test piece
N°14B - For bar form test piece
20 < t ≤ 40 N°14A N°4; N°10 For bar form test piece
N°14B N°1A For flat form test piece
6 < t ≤ 20 N°14B N°1A; N°5
N°5; N°13A; N°13B
3 < t ≤ 6
t ≤ 3 -
Bar - N°2; N°14A N°4; N°10 -
Wire - - N°9A; N°9B -
Pipe Pipe of small outside diameter N°14C N°11 For tubular form test piece
**D ≤ 50 N°14B N°12A For arc section test piece
50 < D ≤170 N°12B
D >170 N°12C
D ≥200 N°14B N°5 For flat form test piece or arc section test piece
Thick wall pipe N°14A N°4 For bar form test piece
Casting - N°14A N°4; N°10 -
- - N°8A; N°8B; N°8C; N°8D To be used when elongation value is not required. To be taken from test coupon casted for test piece.
Forging - N°14A N°4; N°10 -

*t - thicknesses in mm
**D - outside diameter in mm

Remarks:
1. N°1B test piece shall be used in the case where the test pieces shown in Table 2 are not suitable to be used.
2. N°3, N°6 and N°7 test piece specified in Annex should be used when the use of test pieces given in Table 2 is not suitable.
3. For the materials specified in the International Standard, the division of use shown in the following remarks Table 1 may be used.

Remarks Table 1: Division of use and dimension of test piece based on International Standard

Shape of cross section of product Dimension
[mm]
Width
W
Gauge length
L
Parallel length
P
Distance from end of parallel portion to grip
Sheet t < 3 12.5 50 75 87.5
20 80 120 140
t ≥ 3   5.65√***A L+2√A  
Bar D < 4   200   250
  100   150
D ≥ 3   5D L+2D  
Wire D < 4   200   250
  100   150
D ≥ 4   5D L+2D  
Pipe t < 3 12.5 50 75 87.5
20 80 120 140
t ≥ 3   5.65√A L+2√A  
Shape t < 4   200   250
  100   150
t ≥ 4   5D L+2D  

***A- sectional area of parallel portion

기술 자료 검색

검색할 어구를 입력하십시오:

검색 범위

본문
키워드

머릿글
요약

Total Materia Extended Range는 수천개 재질의 탄성 영역 범위 내 계산용 응력-변형률 곡선, 열처리 및 공정 온도 정보를 포함하고 있습니다. 다양한 변형률 속도에 따른 진응력-진변형률 곡선 및 공칭응력-공칭변형률 곡선 또한 제공됩니다.

응력-변형률 곡선을 데이터베이스에서 검색하는 것은 매우 쉽습니다.

신속 검색에 검색할 재질명을 입력합니다. 원하신다면 국가/규격을 지정하신 후 검색 버튼을 클릭합니다.


관심 소재를 선택한 후, 선택된 소재에 대한 응력-변형률 곡선의 링크를 클릭하십시오. 가능한 응력 - 변형률 곡선 기록의 개수는 링크 옆 괄호 안에 표시됩니다.


Total Materia 응력-변형률 곡선은 규격 사양서와 무관하므로, 어떠한 소그룹 내의 링크를 클릭하셔도 응력-변형률 곡선을 검토하실 수 있습니다.

온도가 달라지면 응력-변형률 곡선도 변하기 때문에, 응력과 변형률 정보는 표로 주어져 있습니다. 이는 CAE 소프트웨어 등에 쉽게 응용하실 수 있습니다.


다른 작동 온도에서 응력-변형률 곡선을 검토하실 수도 있습니다.

이를 위해서는 간단히 범위 내 새로운 온도를 온도 입력 창에 입력하시면 됩니다.

계산 버튼을 누르시면 새로운 온도와 그에 대응하는 값이 출력됩니다. 250°C에서의 예를 보십시오.


Total Materia 데이터베이스를 사용해 보실 수 있는 기회가 있습니다. 저희는 Total Materia 무료 체험을 통해 150,000명 이상의 사용자가 이용하고 있는 커뮤니티로 귀하를 초대합니다.