Shipbuilding Steels: Part One

요약:

Various shipbuilding requirements, such as reduction in welding man-hours, shortening of welding lines, elimination of cutting steps, stabilization of fabricated part quality and reduction in control costs, have been met by developing TMCP high-strength steels that require no preheating for welding, irregular-section plates and plates with close dimensional tolerances, and by increasing the stringency of pre-shipment plate quality control.

A demand for heavy thick plates with a good combination of high strength, toughness, and weldability has been widely growing in recent years for large container ship building. Because of this, e tra high-strength termomechanically processed steels TMCP have been developed to be more user friendly than the traditional steels.

E cellent handling properties are based on thermomechanical treatment that reduces the need for e cessive use of alloying elements to strengthen the steel. TMCP plates are thermomechanically controlled rolled, and with greater plate thicknesses, also accelerated cooled after rolling.

Generally, TMCP steels are supplied as heavy plates, surface treated plates and plate components. Due to the very low carbon equivalent, TMCP steels are easily weldable using all common processes. In addition, they are easy to form, bend and edge.

TMCP steels give many monetary advantages to the shipbuilder:

  • Reduced plate thickness
  • Saving weight in the final structure
  • Greater effective loads during use
  • Cost savings in welding and fabrication.

The successful application of thermo-mechanical control process (TMCP) with the recent innovative technology has induced the development of EH36, EH40, and EH47 grade steel plates. The alloying elements such as boron, copper, and nickel were added and the rolling and cooling processes were strongly and precisely controlled to improve the strength and toughness at the same time. EH36 steel plate for high heat input welding was successfully developed with good toughness at the heat affected zone (HAZ) by increasing the thermal stability of TIN particles at the high temperature.

The quality of shipbuilding steels has an e tremely large impact on the quality, efficiency and cost of ships built from those steels. Many steel producers established a system to supply wide and long plates to the shipbuilding industry.

Various shipbuilding requirements, such as reduction in welding man-hours, shortening of welding lines, elimination of cutting steps, stabilization of fabricated part quality and reduction in control costs, have been met by developing TMCP high-strength steels that require no preheating for welding, irregular-section plates and plates with close dimensional tolerances, and by increasing the stringency of pre-shipment plate quality control. Table 1 shows the common steel grades for shipbuilding.

Table 1: Steel for Ship Building

Lloyds Norske
Veritas
Germanischer
Lloyds
Bureau
Veritas
American Bureau
of Shipping
USSR
Register
Nippon
Kaigi Kyoka
A A A A A A A
B B B B B B B
D D D D SS D D
        CD/DS    
  NV A27S          
  NV D27S          
AH 32 NV A32 A 32 AH 32 AH 32 A 32  
DH 32 NV 32 D 32 DH 32 DH 32 D 32  
EH 32 NV E32 E 32 EH 32 EH 32 E 32  
AH 34S            
DH 34S            
EH 34S            
AH 35 NV A36 A 36 AH 36 AH 36 A 36  
DH 36 NV D36 D 36 DH 36 DH 36 D 36  
EH 36 NV E36 E 36 EH 36 EH 36 E 36  
  NV A40          
  NV D40          
  NV E40          
  NV A420          
  NV D420          
  NV E420          

Steel in shipbuilding

Shipbuilding traditionally uses structural steel plate to fabricate ship hulls. Modern steel plates have much higher tensile strengths than their predecessors, making them much better suited to the efficient construction of large container ships.

A particular type of plate is available with a designed-in resistance to corrosion, ideal for building oil tankers. Such steels make possible much lighter vessels than before, or larger capacity vessels for the same weight, offering significant opportunities to save on fuel consumption and hence CO2 emission.

The advanced steels used in these steel-plate applications also find uses in a number of related industries. Offshore oil rigs, bridges, civil engineering and construction machines, rail carriages, tanks and pressure vessels, nuclear, thermal and hydroelectric plants – all these applications benefit from the attributes of modern steels.







Figure 1: Ships: Navy, Cargo and Cruise

In recent years, more attention has been paid to the safety and durability of ships and environment protection of sea, which have lead to the development of new structural steel plates. One of them is the development of more corrosion resistant plates for double-hull tankers. Crude oil carriers are now required to have double hulls to prevent oil spill, and an increase in temperature in oil tanks with the double hull structure increases the likelihood of corrosion of upper deck steel plates exposed to the vapor space in the tanks. To prevent the corrosion and to increase the life time of the ships, different corrosion resistant steel palates have been developed.

The development of new steel plates has also been made to increase construction efficiency and thereby to decrease construction cost. Longitudinally profiled (LP) steel plates were developed in this context. Thickness change within a plate was achieved by controlled rolling, which made it possible to replace the plates which had been made by welding steel plates of different thickness, and therefore to reduce the welding time and cost.

Another development is concerned with residual stress retaining in steel plates. TMCP steel plates are likely to possess residual stresses from their production, and this often results in distortion in different ways after cutting and welding of the plates. In order to achieve residual stress-reduced steel plates, temperature differences over the large surface area in a wide and long plate and through the thickness should be minimized and cold levering is also used for the purpose of reducing inhomogeneous stress for block shape accuracy.

A number of research projects are currently being carried out on the European and national levels to improve the application of lasers and optical technologies in shipbuilding. In laser beam welding, centre line solidification cracks in the fused zone are in issue and can limit the travel speed and hence productivity.

The fused zones are typically of the same composition as the steel being welded and whilst there are several welding procedural factors which can be used to minimize the risk of cracking, the problem hinges on the steel composition. Lower S and P levels may thus be required as shown in Table 2.

Table 2: Classification society guidelines for laser welding of ship hull

C 0.12% max (lower speeds ≤ 0.15%)
S 0.005% max (≤ 0.010% for ≤ 12 mm, 0.6 m/min)
P 0.010% max (≤ 0.015% for ≤ 12 mm, 0.6 m/min)
CE 0.38% max  
Weld hardness ≤ 380 HV5 max (≤ 400 HV5 isolated)

기술 자료 검색

검색할 어구를 입력하십시오:

검색 범위

본문
키워드

머릿글
요약

이 문서는 전체 문서 중 일부분입니다. 이 주제에 대해 더 읽고 싶으시면 아래 링크를 클릭하시면 됩니다.

Total Materia는 다양한 나라와 규격에 따른 수천개의 구조용 철강 재질에 대한 정보를 포함하고 있습니다.

재질의 화학적 조성, 기계적 특성, 물리적 특성, 고급 물성 데이터 등의 전체적인 특성 정보들을 어디서든 검토하실 수 있습니다.

고급 검색 내 전 텍스트 검색을 이용하여, 다목적 용 재질을 검색하는 것이 가능합니다.

검색 범위 좀 더 줄이기를 원하신다면 국가/규격과 같은 다른 조건을 지정할 수 있습니다.

검색 버튼을 클릭합니다.


선택된 정보에 부합하는 일련의 재질이 검색됩니다.


결과 리스트에서 재질을 선택하시면, 일련의 규격 사양 소그룹이 나타납니다.


여기에서 선택한 재질의 특정 특성 데이터를 검토하실 수도 있고, 강력한 상호 참조 표를 이용하여 유사 재질이나 등가 재질을 검토하는 것 또한 가능합니다.

예를 들어, 소그룹 내 화학적 조성 링크를 클릭하시면, 재질의 화학적 조성 데이터를 검토하실 수 있습니다.


구조용 철강에 중요한 정보를 제공하는 기계적 특성(항복 응력, 인장 응력, 연신율 및 충격 데이터) 또한 검토 하실 수 있습니다.


Total Materia 데이터베이스를 사용해 보실 수 있는 기회가 있습니다. 저희는 Total Materia 무료 체험을 통해 150,000명 이상의 사용자가 이용하고 있는 커뮤니티로 귀하를 초대합니다.