High Manganese Austenitic Steels: Part Two

概要:

The main advantages of high manganese inclusion can include increased ductility, very high toughness and much improved tribology characteristics in the materials resistance to abrasion.
The mechanical properties of austenitic manganese steels are directly related to the carbon and manganese content. Typically the optimum is to go for mid-range content to balance between acceptable properties and economic sense.

Cast high-manganese steel containing 1.2% C and 12% Mn is a material with high resistance to abrasion, provided, however, that it is used under the conditions of high dynamic loads. In its typical embodiment, this steel in as-cast condition is characterised by an austenitic microstructure with precipitates of alloyed cementite and the triple phosphorus eutectic of an Fe-(Fe,Mn)3C-(Fe,Mn)3P type, which appears when the phosphorus content exceeds 0.04%. It also contains nonmetallic inclusions such as oxides, sulphides and nitrides (Figures 1-2). This type of microstructure is unfavourable due to the presence of the (Fe,Mn)xCy carbides spread along the grain boundaries. Combined with the effect of non-metallic inclusions, these carbides clearly reduce the ductility of cast Hadfield steel.



Figure 1: Cast high-manganese steel Hadfield steel; austenitic matrix with precipitates of acicular alloyed cementite; Nital etching

For this reason, the aim to be achieved during heat treatment (the heat-treatment of Hadfield steel castings involves solutioning and cooling in water) is to produce a purely austenitic microstructure, i.e. free from the carbide precipitates (Figure 2).



Figure 2: Cast Hadfield steel after solution treatment in water; austenitic matrix free from the precipitates of alloyed cementite spread along the grain boundaries; Nital etching

In the paper of G. Tęcza, S. Sobula, is showed the result of the samples which were treated at three different temperatures, i.e. 1100, 1150 and 1200°C, one batch for 40 minutes, another batch for 80 minutes. Other samples were solution treated at a temperature of 1150°C with the time of heat treatment extended to 4 hours (in 30 minute steps). From thus prepared samples, the metallographic sections were prepared, the chemical composition of the visible carbides was examined, and microhardness of the matrix and precipitates was measured. Solution treatment of the cast high-chromium Hadfield steel carried out at 1100, 1150 and 1200°C for 40 minutes does not lead to a purely austenitic structure. The cross-sections of metallographic specimens show the presence of undissolved cementite present along the austenite grain boundaries. (see Figure 3).



Figure 3: Cast Hadfield steel after solution treatment in water (1150°C/240 minutes); austenitic matrix with undissolved carbides spread along the grain boundaries; nital etching

The mechanical properties of austenitic manganese steels vary with carbon and manganese content. There is a tendency to operate close to the midpoint carbon range and with 12-13%Mn since the lover level of the composition range is associated with somewhat inferior tensile properties and the upper extreme has no economic advantage.



Figure 4: Effect of carbon content on (a) yield and tensile strength, (b) ductility of the 12-14Mn Hadfield steels



Figure 5: Effect of Mn content on (a) yield and tensile strength, (b) elongation and total reduction of height of Hadfield steels


References

1. G. Tecza, S. Sobula: Effect of heat treatment on change microstructure of cast high-manganese Hadfield steel with elevated chromium content, Archives of Foundry Engineering, ISSN 1897-3310, Vol.14, Special Issue 3/2014, p.67-70;

2. Standard Specification for Steel Castings, Austenitic Manganese, ASTM Designation: A128/A128M − 93 (Reapproved 2017).

ナレッジベース検索

検索したい語句を入力:

検索方法

全文一致
キーワード

前方一致
要約

Total Materiaデータベースは世界の国々と広範な規格に関する多くの金属組織画像を収録しております。

メニュウバーにある組織のタブを使うと材料のリストから対象とする材料を選びその金属の組織データをみる事ができます。

組織データは標準のベーシックモジュールにて探す事ができ対象とする材料に関するサブグループで関連するデータをみることができます。

フィールドに材料名を、また規格が分かれば規格も入力し’検索’をクリックします。


すると対象材料の化学成分と共に微細構造を見る事ができます。


一連の画像があり倍率レベルごとに詳細な構造が表示されます。

'条件を選ぶ’のドロップダウンメニューからさまざまな条件を選びいろいろな工程と熱処理状況での組織画像を表示します。



Total Materiaデータベースをあなたにテスト評価を頂くために15万人以上の方が登録されている無料お試しコミュニティ-へ御招待致します。