High Boron Cast Iron: Part One

概要:

Boride emerged as a good alloying option for iron based alloys to help improve toughness and specifically help in applications where wear resistance is important.
The addition of boron causes martensite transformation to a mixed state with austenite and this provides the platform for improved overall toughness in the material.

Among iron-based wear-resistant materials, there has been a lot of research and application for white cast iron alloyed with carbide; however, low toughness limits their application range. In recent years, much attention has been paid to iron-based alloys that include boride in the wear-resistant phases. Compared with carbide, boride is much harder and has better heat stability, so it can be used as a wear-resistant phase.

Boron is interesting as an alloying element in chromium white irons. It is more known as a micro-alloying element of steel, where it is applied in the amounts of several tens to several hundreds of ppm-s. There, its role is to ensure the necessary hardenability of austenite. However, since the application of carbidizing elements has become popular in the investigation practice of improving the properties of chromium white irons properties, it became normal to perform experiments with boron, bearing in mind its properties, especially the structural and electrochemical ones.

Sources of boron contamination, in addition to steel scrap, may include boron pickup from refractory linings and silicon carbide charge materials. The technical literature relating to the effects of boron on the mechanical properties of ductile iron are somewhat conflicting. Very low levels of boron have been reported to act as carbide stabilizers and promote pearlite while recently others have reported just the opposite effect. Boron levels in the range of 0.0011% to 0.0020% (11 to 20 ppm’s) reduce pearlite levels in pearlitic ductile irons and reduce Brinell hardness levels (BHN). Large quantities of pearlite stabilizing elements such as copper and tin are required to return to normal hardness and microstructures.

The effect of boron, in the amounts of 0.26, 0.39, and 0.59 wt.%, on the volume fraction and structure of carbides in Cr white irons was examined in the paper S. M. Tomović-Petrović, S.V. Marković, S. Zec. It was demonstrated that the addition of boron can change the microstructural characteristics of white iron containing about 13 wt.% Cr. With increasing boron content, the volume fractions of M3C carbide increase, but the volume fracton of M7C3 carbide remains unchanged. The addition of boron tends to produce hard borides and/or borocarbides. It also prevents the formation of pearlite, which results in alloys possessing good wear resistance.

The microstructures of the examined alloys are shown in Figure 1. Detailed analysis confirmed that the structure obtained in this investigation is typical for chromium white cast iron. The base alloy (No. 1) is characterized by the presence of primary austenitic dendrite and a eutectic that consists of eutectic carbides and eutectic austenite. The structure of the other alloys also consists of a primary phase and an eutectic, but the following differences can be noticed:

  • With increasing boron content, the dendritic structure slowly disappears, while the primary phase obtains the form of isolated islands surrounded by the eutectic (Figure 1–c, e, g).
  • In the presence of boron, the primary phase becomes a mixture of austenite and martensite. The degree of martensite tranformation increases with increasing boron content. The development of this transformation can be seen on the SE microphotographs (Fig. 1 – d, f, h).



Figure 1: Microstructure: a), b) – alloy No. 1; c), d) – alloy No. 2; e), f) – alloy No. 3; g), h) – alloy No. 4 (a, c, e, g – optical microphotographs; b, d, f, h – SEM).


References

1. Z. Liu, Y. Li, X. Chen: Effect of tempering temperature on microstructure and mechanical properties of high boron white cast iron, China Foundry, November 2012, p.313-317;

2. S. M. Tomović-Petrović, S.V.Marković, S.Zec: The effect of boron on the amount and type of carbides in chromium white irons, J. Serb. Chem. Soc. 67, (10), 2002, p. 697–707, UDC 546.27:549.261+546.76;

3. R. L. Naro, J. F. Wallace, Y.Zhu: Elimination and neutralization of boron in ductile irons, Accessed April 2018;

ナレッジベース検索

検索したい語句を入力:

検索方法

全文一致
キーワード

前方一致
要約

Total Materiaデータベースは世界の国々と広範な規格に関する多くの金属組織画像を収録しております。

メニュウバーにある組織のタブを使うと材料のリストから対象とする材料を選びその金属の組織データをみる事ができます。

組織データは標準のベーシックモジュールにて探す事ができ対象とする材料に関するサブグループで関連するデータをみることができます。

フィールドに材料名を、また規格が分かれば規格も入力し’検索’をクリックします。


すると対象材料の化学成分と共に微細構造を見る事ができます。


一連の画像があり倍率レベルごとに詳細な構造が表示されます。

'条件を選ぶ’のドロップダウンメニューからさまざまな条件を選びいろいろな工程と熱処理状況での組織画像を表示します。



Total Materiaデータベースをあなたにテスト評価を頂くために15万人以上の方が登録されている無料お試しコミュニティ-へ御招待致します。