Complex Phase Steels

概要:

Complex-phase steels display high fatigue strength. Based on stress-strain curves they display higher fatigue strength than dual-phase and retained austenite steels, but they are more sensitive to severe strain peaks, i.e. abusive loads.
The structure of the steels is a ferrite/bainite matrix containing martensite and small amounts of retained austenite and/or perlite. This creates a high yield strength tensile strength ratio.

The complex-phase (CP) steels belong to the group of AHSS grade, which gain their strength through extremely fine grain size and a microstructure containing bainite, martensitic, retained austenite and pearlite. These steel grades have been used for parts that require high energy-absorption capacity, such as bumpers and B-pillar reinforcements.

Complex – phase steels can be welded to other complex-phase steels and to other common steel grades. The welding parameters must be matched to the material. To spot-weld complex-phase steels the same equipment can generally be used as for unalloyed deep-drawing steels.

Compared with lower-strength steel grades, complex-phase steels tend to have a lower electrical conductivity, which is why they require lower welding current with the same electrode force in spot welding. When resistance spot welding galvanises sheets, the welding currents must be raised due to the higher conductivity of the coating compared with the base metal. In addition, increasing the electrode force and welding time has a favorable effect on the welding current range.

As well as sheet grade, surface and thickness ratio, other factors such as the type of electrode used play an important role in determining the optimum joining parameters.

Fatigue strength

Complex-phase steels display high fatigue strength. Based on stress-strain curves they display higher fatigue strength than dual-phase and retained austenite steels, but they are more sensitive to severe strain peaks, i.e. abusive loads.

As an illustration of CP steel grades, please note some information about these materials produced by well known producers.

Dogal CP (Complex Phase steels) are cold-rolled advanced high strength steels, which are hot-dip galvanized for corrosion protection. Dogal CP grades are multiphase steels. The structure of the steels is a ferrite/bainite matrix containing martensite and small amounts of retained austenite and/or perlite.

This creates a high yield strength tensile strength ratio. Generally CP steels are easy to cold-form and excellent for stretch forming and roll forming. The steel grades are supplied in accordance with EN 10336.

Also, ThyssenKrupp supplies two hot-rolled grades and one cold-rolled grade with strengths between 800 MPa and 1,000 MPa. Strip can be supplied in thicknesses between 0.8 and 3.0 mm and with two different coatings.

Tables 1, 2 and 3 give some common information about ThyssenKrupp steel grades.

ThyssenKrupp Steel   EN 10336
Hot rolled CP-W®800 HDT 780C
Hot rolled CP-W®1000 HDT 950C
Cold rolled CP-K®60/78 HCT 780C
Cold rolled CP-K®70/98 HCT 980C

Table 1: Steel grade designations

Steel grade   %C
max
%Si
max
%Mn
max
%P
max
%S
max
%Cr+%Mo
max
%Nb+%Ti
max
%Al
max
%V
max
%B
max
CP-W®800 Hot rolled 0.12 0.80 2.20 0.04 0.015 1.00 0.15 1.20 0.20 0.005
CP-W®1000 Hot rolled 0.17 0.80 2.20 0.04 0.015 1.00 0.15 1.20 0.20 0.005
CP-K®60/78 Cold rolled 0.12 0.80 2.20 0.04 0.015 1.00 0.15 1.20 0.20 0.005

Table 2: Chemical composition (ladle analysis in wt.%)

Steel grade σ0.2
MPa
σm
MPa
Elongation
A80, % min
CP-W®800 680-830 800-980 10
CP-W®1000 720-920 950-1130 10
CP-K®60/78 600-700 780-940 10

Table 3: Mechanical properties for uncoated sheet (transverse)

Complex Phase steels exhibit good fatigue properties and can be used in suspension system parts such as suspension arms. The figure below gives examples of Wöhler curves for a variety of Complex Phase steels produced by ArcellorMittal. They are expressed as stress amplitude versus cycles to failure and are obtained with a stress ratio of R = 0.1 and repeated tensile loading.



Figure 1: Wöhler or SN curves for Complex Phase steels (R=0.1)

The graph below shows the low cycle or EN curves for the same steels. These are expressed as strain amplitude versus number of reversals (one cycle equals two reversals). Other high and low cycle fatigue data are available on request.



Figure 2: Low cycle or EN curves for Complex Phase steels (R=-1)

ナレッジベース検索

検索したい語句を入力:

検索方法

全文一致
キーワード

前方一致
要約

Total Materia Extended Range(拡張版)には数千種の金属合金、熱処理、負荷条件に応じた疲労データならびに繰り返し特性に関する最大のデータベースが収録されております。歪み寿命と応力寿命ともに収録されており、参考としてモノトニック特性、統計的パラメータ、推測値も含まれております。

簡単でしかも数秒以内でデータベースの繰り返し特性を探せます。

検索対象の材料名を入力します。材料入力のフィールドで国/規格を指定し検索を絞る事ができます。’検索’をクリックします。


対象材料を選んでから疲労データのリンクをクリックするとデータが御覧になれます。御覧になれる疲労データの数はリンクわきのカッコ内に表示されております。


Total Materia Extended Range(拡張版)の繰り返し特性は規格それぞれに中立的なものでサブグループのどれが適切なリンクをクリックしてデータを見て下さい。歪み寿命、応力寿命は表形式で表示されグラフ表示される場合もあります。


データソースに関する明確な参照先が表示されますので下記の例を御覧下さい。


Total Materiaデータベースをあなたにテスト評価を頂くために15万人以上の方が登録されている無料お試しコミュニティ-へ御招待致します。