Fe-Ni-Mn Maraging Steels: Part Two

Sommario:

Maraging steels are a special class of low‐carbon ultra‐high‐strength steels which are produced by precisely controlling the amounts of nickel and manganese in the finished material.
The maraging response is highly dependent on the manganese content and at precise levels can produce profound hardness visible through classical age hardening curves as a function of aging temperature and time.

It is well known that Fe-Ni-Mn alloys show remarkable age-hardening behavior in the temperature range from 300 to 500°C. Although age hardening in these alloys has been studied extensively, the identity of precipitate particles in Fe-Ni-Mn alloys remains controversial. The f.c.t. θ-NiMn, b.c.c, β-NiMn, f.c.c. Ni3Mn and an ordered b.c.c. precipitate have been reported. These diversified opinions may be due to a variety of alloy compositions, various heat treatments or uncertainties of identification in electron diffraction analyses. The most common technique has been based on diffraction patterns from extracted precipitate particles. However, there are problems inherent in extraction methods in that lines from inclusions and oxides formed by the extraction solution may obscure the results. It should be noted that all reported results do not provide substantive experimental evidence for the specific precipitates.

In the study of Sung-Joon Kim and C. M. Wayman, the crystallography, the orientation relationship with the matrix and the shape of precipitates have been investigated using thin foil analytical electron microscopy and computer simulation of selected-area diffraction patterns (SADPs) for Fe-20wt.%Ni-Mn alloys.

The alloy compositions of the Fe-Ni-Mn studied are Fe-21.1wt.%Ni-1.27wt.%Mn (alloy A-0) and and Fe-20.8wt.%Ni-3.23wt.%Mn (alloy B-0); alloy A-0 has a lower manganese content than B-0 has.

The maraging response of the alloys investigated in this study was strongly dependent on the manganese content. The higher manganese alloys showed a similar precipitation behavior to that in low nickel Fe-Ni-Mn alloys with classical age hardening curves as a function of aging temperature and time. Fine spherical precipitates appeared first at 400°C aging, followed by the appearance of rod-shaped f.c.t. θ-NiMn and Widmanstätten austenite. Ordered f.c.t. θ-NiMn precipitates were identified using EDX analysis and confirmed by computer simulation of SADPs. The pronounced hardening is associated with the stress required for dislocations to cut through coherent zones or precipitates of spherical precipitates. The orientation relationship between metallic parent matrix and θ-NiMn precipitates is [011]M//[111]θ and (ĺ ĺ 1)M//(ĺ01)θ, whereas that between the martensite and Widmanstiitten austenite is the Kurdyumov-Sachs relation. The shapes of the θ-NiMn precipitates are dependent on the aging temperature. Rod-shaped θ-NiMn 16 precipitates become dominant at lower aging temperatures, while disc-shaped θ-NiMn appears at higher aging temperatures.

Floreen and Decker have shown that in 18 pct Ni maraging steels, the early stages of hardening may be represented by the empirical relationship:

Ht – H0 = ΔH = (Kt)n

where Ht = hardness at time t
H0 = initial hardness
K = constant
n = constant

During investigation of an Fe-12Ni-6Mn maraging alloy a similar behavior was found to occur (see Figure 1). This alloy consists of lath martensite in the air cooled condition and shows pronounced hardening on aging in the temperature range 350°C to 500°C (Figure 2). Hardening is due to precipitation of θ NiMn on dislocations (Figure 3).



Figure 1: Variation of initial hardness increase ΔH with aging time, t, in an Fe-12Ni-6Mn maraging alloy



Figure 2: Age-hardening curves for alloy



Figure 3: Thin foil electron micrograph of overaged alloy


References

1. S-J Kim, C. M. Wayman: Electron microscopy study of precipitates in Fe-Ni-Mn maraging alloys, Volume 136, 30 April 1991, p.121-129, Materials Science and Engineering A-Structure Materials Properties Microstructure and Processing, DOI :10.1016/0921-5093(91)90447-U;

2. D. R. Squires, E. A. Wilson: Kinetics of aging in an Fe-12Ni-6Mn maraging alloy, Metallurgical Transactions A, Vol.15A, October 1984, p.1947-1948.

Criteri di ricerca
Inserite il vostro testo in inglese per la ricerca:

Ricerca tramite

Ricerca tramite

Testo completo
Intestazioni

Articolo
Sommario

Il database Total Materia contiene un gran numero di immagini di metallografia per una ampia gamma di Paesi e Normative, in costante incremento.

Cliccando sull'icona "Metallografia" posta nella barra dei menu, è possibile selezionare il materiale di interesse dalla lista dei materiali con dati metallografici disponibili in forma numerica e/o fotografica.

i dati di Metallografia possono essere reperiti anche attraverso la Ricerca Base e l'esame dei Sottogruppi relativi al materiale selezionato.

E' sufficiente inserire la Designazione nella casella del materiale ed eventualmente la Normativa e dare Invio.


Informazioni generali sulla microstruttura si possono trovare unitamente alla composizione chimica.


Quando disponibili, vengono fornite delle immagini che mostrano una serie di dettagli strutturali a vari livelli di ingrandimento.

E 'anche possibile selezionare diverse opzioni di condizioni di stato dal menu a discesa del pulsante "selezionare la condizione": vengono mostrate differenti immagini relative ai vari processi di lavorazione e trattamenti termici.



Per consentirvi di testare il Database Total Materia "senza impegno", vi invitiamo a unirvi alla comunità degli Utenti registrati per i test gratuiti a Total Materia.