Fe-Ni-Mn Maraging Steels: Part Two

Abstrakt:

Maraging steels are a special class of low‐carbon ultra‐high‐strength steels which are produced by precisely controlling the amounts of nickel and manganese in the finished material.
The maraging response is highly dependent on the manganese content and at precise levels can produce profound hardness visible through classical age hardening curves as a function of aging temperature and time.

It is well known that Fe-Ni-Mn alloys show remarkable age-hardening behavior in the temperature range from 300 to 500°C. Although age hardening in these alloys has been studied extensively, the identity of precipitate particles in Fe-Ni-Mn alloys remains controversial. The f.c.t. θ-NiMn, b.c.c, β-NiMn, f.c.c. Ni3Mn and an ordered b.c.c. precipitate have been reported. These diversified opinions may be due to a variety of alloy compositions, various heat treatments or uncertainties of identification in electron diffraction analyses. The most common technique has been based on diffraction patterns from extracted precipitate particles. However, there are problems inherent in extraction methods in that lines from inclusions and oxides formed by the extraction solution may obscure the results. It should be noted that all reported results do not provide substantive experimental evidence for the specific precipitates.

In the study of Sung-Joon Kim and C. M. Wayman, the crystallography, the orientation relationship with the matrix and the shape of precipitates have been investigated using thin foil analytical electron microscopy and computer simulation of selected-area diffraction patterns (SADPs) for Fe-20wt.%Ni-Mn alloys.

The alloy compositions of the Fe-Ni-Mn studied are Fe-21.1wt.%Ni-1.27wt.%Mn (alloy A-0) and and Fe-20.8wt.%Ni-3.23wt.%Mn (alloy B-0); alloy A-0 has a lower manganese content than B-0 has.

The maraging response of the alloys investigated in this study was strongly dependent on the manganese content. The higher manganese alloys showed a similar precipitation behavior to that in low nickel Fe-Ni-Mn alloys with classical age hardening curves as a function of aging temperature and time. Fine spherical precipitates appeared first at 400°C aging, followed by the appearance of rod-shaped f.c.t. θ-NiMn and Widmanstätten austenite. Ordered f.c.t. θ-NiMn precipitates were identified using EDX analysis and confirmed by computer simulation of SADPs. The pronounced hardening is associated with the stress required for dislocations to cut through coherent zones or precipitates of spherical precipitates. The orientation relationship between metallic parent matrix and θ-NiMn precipitates is [011]M//[111]θ and (ĺ ĺ 1)M//(ĺ01)θ, whereas that between the martensite and Widmanstiitten austenite is the Kurdyumov-Sachs relation. The shapes of the θ-NiMn precipitates are dependent on the aging temperature. Rod-shaped θ-NiMn 16 precipitates become dominant at lower aging temperatures, while disc-shaped θ-NiMn appears at higher aging temperatures.

Floreen and Decker have shown that in 18 pct Ni maraging steels, the early stages of hardening may be represented by the empirical relationship:

Ht – H0 = ΔH = (Kt)n

where Ht = hardness at time t
H0 = initial hardness
K = constant
n = constant

During investigation of an Fe-12Ni-6Mn maraging alloy a similar behavior was found to occur (see Figure 1). This alloy consists of lath martensite in the air cooled condition and shows pronounced hardening on aging in the temperature range 350°C to 500°C (Figure 2). Hardening is due to precipitation of θ NiMn on dislocations (Figure 3).



Figure 1: Variation of initial hardness increase ΔH with aging time, t, in an Fe-12Ni-6Mn maraging alloy



Figure 2: Age-hardening curves for alloy



Figure 3: Thin foil electron micrograph of overaged alloy


References

1. S-J Kim, C. M. Wayman: Electron microscopy study of precipitates in Fe-Ni-Mn maraging alloys, Volume 136, 30 April 1991, p.121-129, Materials Science and Engineering A-Structure Materials Properties Microstructure and Processing, DOI :10.1016/0921-5093(91)90447-U;

2. D. R. Squires, E. A. Wilson: Kinetics of aging in an Fe-12Ni-6Mn maraging alloy, Metallurgical Transactions A, Vol.15A, October 1984, p.1947-1948.

Durchforschen Sie bitte den Informationsteil der Datenbank

Geben Sie bitte eine Anfrage, um Suche einzuleiten:

Suche nach

Vollständiger Text
Schlüsselwörter

Überschriften
Abstracts

Die Total Materia Datenbank enthält eine große Anzahl von Gefügebildern aus vielen Ländern und Normen.

Benutzen Sie den Button Metallographie der Menüleiste um aus der angezeigten Liste den Werkstoff auszusuchen der Sie interessiert und der über Gefügebilder verfügt.

Gefügebilder können auch über die Schnellsuche gefunden werden. Falls die betreffenden Informationen, für den Werkstoff Ihrer Wahl, zur Verfügung stehen, wird dies auf der Seite der Untergruppen angezeigt.

Geben Sie einfach die gesuchte Werkstoffbezeichnung in das Feld der Schnellsuche ein, wählen Sie die Norm aus, falls Sie diese kennen und senden Sie Ihre Suche ab.


Generelle Informationen über die Mikrostruktur werden, für den betroffenen Werkstoff, zusammen mit der chemischen Zusammensetzung angezeigt.


Wenn verfügbar, wird eine Reihe von Schaubildern strukturelle Details mit verschiedenen Vergrößerungen anzeigen.

Es ist auch möglich, verschiedene Bedingungen aus der Auswahlliste "Bedingung" auszuwählen um Gefügebilder unter verschiedenen Bearbeitungs- und Wärmebehandlungsbedingungen zu sehen.



Um unsere Datenbank auszuprobieren, laden wir Sie ein sich unserer Nutzergemeinschaft von über 150 000 angemeldeten Benutzern, mit einem kostenlosen Probeaboanzuschliessen.