True Stress - True Strain Curve: Part Two

Abstrakt:

Generally, the metal continues to strain-harden all the way up to fracture, so that the stress required to produce further deformation should also increase. If the true stress, based on the actual cross-sectional area of the specimen, is used, it is found that the stress-strain curve increases continuously up to fracture. If the strain measurement is also based on instantaneous measurements, the curve, which is obtained, is known as a true-stress-true-strain curve.

The engineering stress-strain curve does not give a true indication of the deformation characteristics of a metal because it is based entirely on the original dimensions of the specimen, and these dimensions change continuously during the test. Also, ductile metal which is pulled in tension becomes unstable and necks down during the course of the test.

Because the cross-sectional area of the specimen is decreasing rapidly at this stage in the test, the load required continuing deformation falls off. The average stress based on original area likewise decreases, and this produces the fall-off in the stress-strain curve beyond the point of maximum load. Figure 1 shows the true stress-strain curves in tension at room temperature for various metals.

Figure 1: True stress-strain curves in tension at room temperature for various metals


Actually, the metal continues to strain-harden all the way up to fracture, so that the stress required to produce further deformation should also increase. If the true stress, based on the actual cross-sectional area of the specimen, is used, it is found that the stress-strain curve increases continuously up to fracture. If the strain measurement is also based on instantaneous measurements, the curve, which is obtained, is known as a true-stress-true-strain curve. This is also known as a flow curve since it represents the basic plastic-flow characteristics of the material.

Any point on the flow curve can be considered the yield stress for a metal strained in tension by the amount shown on the curve. Thus, if the load is removed at this point and then reapplied, the material will behave elastically throughout the entire range of reloading.

The true stress s is expressed in terms of engineering stress s by

(1)


The derivation of Eq. (1) assumes both constancy of volume and a homogenous distribution of strain along the gage length of the tension specimen. Thus, Eq. (1) should only be used until the onset of necking. Beyond maximum load the true stress should be determined from actual measurements of load and cross-sectional area.

(2)


The true strain e may be determined from the engineering or conventional strain e by

(3)

Figure 2. Comparison of engineering and true stress-strain curves


This equation is applicable only to the onset of necking for the reasons discussed above. Beyond maximum load the true strain should be based on actual area or diameter measurements.

(4)


Figure 1 compares the true-stress-true-strain curve with its corresponding engineering stress-strain curve. Note that because of the relatively large plastic strains, the elastic region has been compressed into the y-axis. In agreement with Eqs. (1) and (3), the true-stress-true-strain curve is always to the left of the engineering curve until the maximum load is reached. However, beyond maximum load the high-localized strains in the necked region that are used in Eq. (4) far exceed the engineering strain calculated from Eq. (1).

Frequently the flow curve is linear from maximum load to fracture, while in other cases its slope continuously decreases up to fracture. The formation of a necked region or mild notch introduces triaxial stresses, which make it difficult to determine accurately the longitudinal tensile stress on out to fracture.

Durchforschen Sie bitte den Informationsteil der Datenbank

Geben Sie bitte eine Anfrage, um Suche einzuleiten:

Suche nach

Vollständiger Text
Schlüsselwörter

Überschriften
Abstracts

Dieser Artikel ist Teil einer Artikelserie. Klicken Sie die Links um mehr über dieses Thema zu lesen.

Total Materia Extended Range beinhaltet eine einzigartige Sammlung von Spannungs-Dehnungs-Diagrammen für Berechnungen im plastischen Bereich, für tausende von Metalllegierungen, Wärmebehandlungen und Arbeitstemperaturen. Sowohl das wahre, als auch das nominelle Spannungs-Dehnungs-Diagramm werden, wo passend, für verschiedene Dehnungsgeschwindigkeiten angeboten.

Ein Spannungs-Dehnungsdiagramm in der Datenbank zu finden ist einfach und sekundenschnell.

Geben Sie die Bezeichnung des werkstoffs der Sie interessiert in das Feld der Schnellsuche ein. Sie können auch, falls erwünscht, Ihre Suche weiter einschrenken indem Sie eine Norm/Land in das vorgesehene Feld eingeben, bevor Sie Ihre Suche absenden.


Nachdem Sie den Werkstoff der Sie interessiert, ausgesucht haben, klicken Sie auf den Link der Spannungs-Dehnungsdiagramme um die Daten für diesen Werkstoff zu sehen. Die Anzahl der zur Verfügung stehenden Daten der physikalischen Eigenschaften ist neben dem Link, in Klammern, angegeben.


Da Total Materia Spannungs-Dehnungsdiagramme unabhänig von den Normen sind, können Sie diese anzeigen indem Sie auf den entsprechenden Link jedweder Untergruppe klicken.

Neben den Spannungs-Dehnungsdiagrammen bei verschiedenen Temperaturen, sind Belastung und Materialspannung auch in Tabellenform angezeigt, was praktisch ist um diese zu kopieren, zum Beispiel für CAE Software.


Es ist auch möglich, Spannungs-Dehnungsdiagramme und Daten für andere Arbeitstemperaturen zu sehen.

Hierzu, geben Sie einfach eine neue Temperatur, inerhalb der definierten Spanne, in das entsprechende Feld ein.

Nachdem Sie auf den Button "Berechnen" geklickt haben, wird eine neue Kurve angezeigt und die Daten der Tabelle entsprechen nun der Temperatur die Sie festgelegt haben. Sehen Sie untenstehend ein Beispiel bei 250°C.


Um unsere Datenbank auszuprobieren, laden wir Sie ein sich unserer Nutzergemeinschaft von über 150 000 angemeldeten Benutzern, mit einem kostenlosen Probeaboanzuschliessen.