Cold Working Processes

Abstrakt:

Cold working is the plastic deformation of metals below the recrystallization temperature. In most cases, such cold forming is done at room temperature.
The major cold-working operations can be classified basically as squeezing, bending, shearing and drawing.

Cold working is the plastic deformation of metals below the recrystallization temperature. In most cases of manufacturing, such cold forming is done at room temperature. Sometimes, however, the working may be done at elevated temperatures that will provide increased ductility and reduced strength, but will be below the recrystallization temperature.

When compared to hot working, cold-working processes have certain distinct advantages:

  • No heating required
  • Better surface finish obtained
  • Superior dimension control
  • Better reproducibility and interchangeability of parts
  • Improved strength properties
  • Directional properties can be minimized

Some disadvantages associated with cold-working processes include:

  • Higher forces required for deformation
  • Heavier and more powerful equipment required
  • Less ductility available
  • Metal surfaces must be clean and scale-free
  • Strain hardening occurs (may require intermediate anneals)
  • Imparted directional properties may be detrimental
  • May produce undesirable residual stresses

Table 1: The major cold-working operations

The major cold-working operations can be classified basically under the headings of squeezing, bending, shearing and drawing, as follows.

Squeezing Processes

Most of the cold-working squeezing processes have identical hot-working counterparts or are extensions of them. The primary reasons for deforming cold rather than hot are to obtain better dimensional accuracy and surface finish. In many cases, the equipment is basically the same, except that it must be more powerful.

Cold Rolling

Cold rolling accounts for by far the greatest tonnage of cold-worked products. Sheets, strip, bars and rods are cold rolled to obtain products that have smooth surfaces and accurate dimensions.

Swaging

Swaging basically is a process for reducing the diameter, tapering, or pointing round bars or tubes by external hammering. A useful extension of the process involves the formation of internal cavities. A shaped mandrel is inserted inside a tube and the tube is than collapsed around it by swaging.

Cold Forging

Extremely large quantities of products are made by cold forging, in which the metal is squeezed into a dive cavity that imparts the desired shape. Cold heading is used for making enlarged sections on the ends of rod or wire, such as the heads on bolts, nails, rivets and other fasteners.

Sizing

Sizing involves squeezing areas of forgings or ductile castings to a desired thickness. It is used principally on basses and flats, with only enough deformation to bring the region to a desired dimension.

Extrusion

Extrusion is a bulk deformation process where a billet, generally cylindrical, is placed in a chamber and forced through a die. The die opening can be round to produce a cylindrical product, or the opening can have a variety of shapes. Typical extrusion products are shown in Figure 1. Because of large reductions imparted during the extrusion process, most extrusion processes are performed hot in order to reduce the flow strength of the metal. Cold extrusion can occur but it is usually one step in a multi step cold forging operation.

Figure 1: Schematic of extrusion processes: a-direct or forward extrusion; b-indirect or reverse extrusion; c-impact extrusion and d-hydrostatic extrusion.

Durchforschen Sie bitte den Informationsteil der Datenbank

Geben Sie bitte eine Anfrage, um Suche einzuleiten:

Suche nach

Vollständiger Text
Schlüsselwörter

Überschriften
Abstracts

Physikalische Eigenschaften stehen, in der Total Materia Datenbank, für eine grosse Anzahl von Werkstoffen zur Verfügung.

Die Daten sind sowohl über offizielle Informationen der Normen, als auch über Total Materia einzigartige Cross-Reference Funktion erhältlich welche eine neue Dimension für Ihre Suche nach phzsikalischen Eigenschaften eröffnet.

Geben Sie den gesuchten Werkstoff in das Feld der Schnellsuche ein.Sie können auch, falls erwünscht, Ihre Suche weiter einschrenken indem Sie eine Norm/Land in das vorgesehene Feld eingeben, bevor Sie Ihre Suche absenden.


Nachdem Sie den Werkstoff der Sie interessiert, ausgesucht haben, klicken Sie auf den Link der physikalischen Eigenschaften um die Daten für diesen Werkstoff zu sehen. Die Anzahl der zur Verfügung stehenden Daten der physikalischen Eigenschaften ist neben dem Link, in Klammern, angegeben.


Physikalische Eigenschaften werden nach Ursprung der Daten angezeigt. Offizielle Daten der Normen können über den Reiter "Offiziell" gefunden werden, Daten aus anderen Quellen, werden unter den dementsprechenden Reitern angezeigt.


Der Reiter "Ähnliche Werkstoffe" zeigt alle Werkstoffe an die dem originalen Werkstoff ähnlich sind und Einträge für physikalische Eigenschaften haben. Das kann sehr praktisch sein wenn Sie nach äquivalenten Werkstoffen suchen.


Der Reiter "Typisch" gibt eine generelle Übersicht über die Werkstoffeigenschaften des ausgewählten Materials, welche Sie als Ausgangspunkt für weitere Nachforschungen benutzen können.


Um unsere Datenbank auszuprobieren, laden wir Sie ein sich unserer Nutzergemeinschaft von über 150 000 angemeldeten Benutzern, mit einem kostenlosen Probeaboanzuschliessen.