Dispersion Strengthened Copper Alloys: Part Two

Sumário:

Coppers range of advantageous characteristics a quite well known including high electrical and thermal conductivity, excellent corrosion resistance to name but a few.
Dispersion strengthened coppers add the advantage of higher strengths which means they can be used for a range or applications such as welding consumables.

Copper (Cu) is a widely used metal due to the advantages of high electrical and thermal conductivities, outstanding corrosion resistance and ease of production. However, in the pure form, mechanical properties of copper deteriorate dramatically at elevated temperature conditions. Based on the existing need for materials which possess high thermal conductivity coupled with high strength and also provide resistance to softening and degradation, different copper alloys have been developed. In order to increase strength of copper at high temperatures, precipitation hardening and oxide dispersion strengthening or both of these mechanisms can be used.

GLIDCOP AL-60 (C15760) is primarily designed for applications requiring the highest elevated temperature strength coupled with relatively high electrical and thermal conductivities. It exhibits a high degree of resistance to softening after exposure to elevated temperatures. GLIDCOP AL-60 has sufficient cold working characteristics for heading, extrusion and some drawing and rolling operations.

Recommended for:

  • Resistance welding electrodes
  • Solder gun tips and MIG contact tips
  • Welding electrodes made from GLIDCOP exhibit improved life
  • Good non-sticking performance on coated steels

GLIDCOP AL-60 is designated in UNS as C15760.



Table 1: Mechanical properties - Typical room temperature properties of GLIDCOP® AL-60

Figure 1 shows comparison of HV hardness vs. Temperature for different tips of manufactured copper alloys/ dispersion strengthened copper alloy. It is evident that DSC copper tip provided up to 5x the life in comparing with a DHP tip. Also, Figure 2 shows comparison of hardness vs. temperature for different copper alloys.



Figure 1: Hardness vs. Temperature for some Copper alloys: DSC-Dispersion Strengthened Copper; DHP-Deoxidized High Phosphorus Coper, DSC-TiC-Dispersion Strengthened copper with Titanium Carbide



Figure 2: Contact tip conductivity comparison at 20°C: Copper Silver (CuAg); Deoxidized High Phosphorus Copper (DHP); Copper Chrome Zirconium (CuCrZr); (Dispersion Strengthened Copper, (DSC); Dispersion Strengthened Copper w/ Titanium Carbide

The study of J. Ďurišin et al., compares an influence of the two different oxide dispersoids on strengthening of the copper matrix after thermo-deformation consolidation of the Cu–Al2O3 and Cu–MgO powders into bulk compacts and annealing of the compacts at elevated temperatures. Nanocrystalline dispersion strengthened copper alloys are particularly attractive for high temperature applications in electrotechnical industry (spot welding electrodes, contacts, switches, etc.).

Structural stability of the both as-extruded materials after 1h annealing in H2 at 200 to 900°C was tested by light microscopy, (see Figure 3) and also indirectly, by means of the Brinell hardness (see Figure 4). The Cu–MgO composite hardness is only 90 HB, and falls down above 200°C as a result of the softening due to the recrystallization and abnormal grain growth. Figure 3a documents a typical fully recrystallized microstructure. On the other hand, the very good initial Cu–Al2O3 hardness of 160 HB exhibits no/minor hardness changes after the annealing and cooling to room temperature, Figure 4, thus suggesting an excellent thermal stability of the microstructure. The Cu–Al2O3 microstructure after 1h annealing at 900°C depicted in Figure 3b shows that in the material have took place recrystallization processes but newly formed grains have remained in ultra-fine sizes due to the effective Al2O3 dispersoids.



Figure 3: Light micrographs of the as-annealed microstructures: (a) Cu–MgO after annealing at 600°C for 1h in H2; (b) Cu–Al2O3 after annealing at 900°C for 1h in H2



Figure 4: The Brinell hardness versus annealing temperature for the Cu–Al2O3 and Cu–MgO materials


References

1. O.Dinçer, M.Kaan Pehlivanoglu, A.F.Dericioglu: High strength copper alloys for extreme temperature conditions, 18. Uluslararası Metalurji ve Malzeme Kongresi, IMMC 2016, p.693-696, Accessed July 2017;

2. GLIDCOP® Dispersion Strengthened Copper, Accessed 7 July 2017;

3. LUVATA, Accessed July 2017;

4. J. Ďurišin, K.Ďurišinova, M.Orolínová: Thermal stability of nanostructure of dispersion strengthened copper alloys, METAL 2015, Jun 3rd-5th, 2015, Brno, Czech Republic, EU.

Procurar conhecimento básico

Colocar uma frase para procurar por:

Procurar por

Texto completo
Palavras chaves

Títulos
Resumo

O banco de dados da Total Materia contém um grande número de imagens metalografia através de uma gama grande de países e padrões.

Usando o guia Metalografia projetado especificamente na barra de menu, você pode selecionar o material de seu interesse a partir da lista de materiais com dados metalografia incluído.

Metalografia dados também podem ser encontradas através do nosso padrão de pesquisa rápida e irá mostrar os dados relevantes são disponíveis através da página Subgrupo padrão para o material de interesse.

Basta digitar a sua designação de material para o 'Material' campo e selecione o padrão de juros, se conhecido, em seguida, clique em "Procurar".


As informações gerais sobre microestrutura pode ser encontrada, juntamente com a composição química relevante para o material de interesse.


Quando disponível, uma série de imagens será fornecido a exibir uma gama de detalhe estrutural em vários níveis de ampliação.

Também é possível selecionar opções diferentes de condição de suspensa a 'condição Selecionar' para mostrar imagens metalografia em processo diferente e estados de tratamento térmico.



Para você é uma oportunidade de fazer um test drive na Total Materia, nós convidamos você a participar de uma comunidade de mais de 150.000 usuários registrados através da Total Materia Free Trial.