Fatigue of Nickel-Based Superalloys: Part One

Sumário:

A critical property of nickel-based superalloys is their resistance to fatigue-crack propagation, particularly at service temperatures.
Many nickel-based superalloys are subject to formation of cracks or incipient cracks, either in fabrication or in use, and that the cracks can actually propagate or grow while under stress during the use in structures such as gas turbines and jet engines.

Nickel-based superalloys are widely used in turbines for both aerospace and land-based power-generation applications, due to their exceptional elevated-temperature strength, high resistance to creep, oxidation, and corrosion, and good fracture toughness. However, a critical property of these alloys is their resistance to fatigue-crack propagation, particularly at service temperatures.

In engine applications, there are often two components to this problem:

  • low-cycle fatigue, which results from relatively large cycles associated with the stopping and starting of the turbine, and
  • high-cycle fatigue (HCF), associated with vibrational loading during service.

Fatigue results in rapid, and often unpredictable, failures due to the propagation of fatigue cracks in blade and disk components under high-frequency loading, where the cracking initiates from small defects, in many instances resulting from fretting or foreign-object damage. Due to the high vibrational frequencies involved, even cracks growing at slow per-cycle velocities can propagate to failure in short time periods, possibly within a single flight segment. Consequently, HCF-critical turbine-engine components must be operated below the fatigue-crack initiation or growth thresholds, such that cracking cannot occur within ~109 cycles.

Nickel-based superalloys have been used extensively in jet engines, in land based gas turbines and other machinery where they must retain high strength and other desirable physical properties at elevated temperatures of 1000°F (540°C) or more. Many of these alloys contain a γ' precipitate in varying volume percentages. The γ' precipitate contributes to the high performance properties of such alloys at their elevated use temperatures.

A problem which has been recognized to a greater and greater degree with many nickel-based superalloys is that they are subject to formation of cracks or incipient cracks, either in fabrication or in use, and that the cracks can actually propagate or grow while under stress as during use of the alloys in such structures as gas turbines and jet engines. The propagation or enlargement of cracks can lead to part fracture or other failure and the consequences of failures of the moving mechanical part due to crack formation and propagation can be particularly hazardous.

A principal finding of a NASA sponsored study was that the rate of propagation based on fatigue phenomena or in other words, the rate of fatigue crack propagation (FCP), was not uniform for all stresses applied nor to all manners of applications of stress. More importantly, the finding was that fatigue crack propagation actually varied with the frequency of the application of stress to the part where the stress was applied in a manner to enlarge the crack.

More surprising still was the magnitude of the finding from the NASA sponsored study that the application of stress of lower frequencies rather than at the higher frequencies previously employed in studies, actually increased the rate of crack propagation. In other words the NASA study verified that there was a time dependence in fatigue crack propagation. Further, the time dependence of fatigue crack propagation was found to depend not on frequency alone but on the time during which the member was held under stress, so-called hold-time.

To date, the grain-boundary engineering approach has been shown to be particularly successful in promoting fracture resistance in specific cases, notably in the context of intergranular stress-corrosion cracking and creep. However, its effect on the fatigue resistance has largely been unexplored.

According to one study, ambient temperature, smooth-bar, tension-tension fatigue lives for two γ / γ' superalloys were reported to be increased by a factor of ~1.5 in an Fe-based alloy by increasing the fraction of special boundaries from 20 to 65 pct and by a factor of 3 in a Ni-based alloy by increasing this fraction from 9 to 49 pct, although no mechanistic explanation was presented.

Clearly, the effectiveness of grain-boundary engineering will depend upon the nature of the crack path, specifically, the preponderance of intergranular versus transgranular cracking. In light of this, the objectives of the studies was to investigate, the feasibility of using grain boundary engineering processing to promote resistance to fatigue-crack propagation, particularly at near-threshold levels, in a new polycrystalline nickel-based disk alloy, ME3 (Ni-Co-Cr Alloy). Specifically, the crack growth rates and threshold behavior of large (8 to 20 mm) through-thickness cracks were examined over a range of temperatures (25°C, 700°C, and 800°C) in order to enhance the incidence of intergranular crack growth, Figure 1.



Figure 1: Variation in fatigue-crack propagation behavior for small surface cracks in the grain-coarsened ME3, together with EBSD characterization of the path for small crack propagation. Random boundaries are shown as black lines twin boundaries are in red, other special boundaries are in yellow.



Procurar conhecimento básico

Colocar uma frase para procurar por:

Procurar por

Texto completo
Palavras chaves

Títulos
Resumo

Este artigo pertence a uma série de artigos. Você pode clicar nos links abaixo para ler mais sobre este tema.

Total Materia Extended Range inclui o maior banco de dados de fadiga e propriedades cíclicas para milhares de ligas de metal, tratamentos térmicos e condições de carga. Parâmetros de vida tanto de vida tensão e estresse são dadas, com propriedades monotônicas adicionados para a referência e parâmetros estatísticos e estimativas se for o caso.

Encontrar propriedades cíclicas no banco de dados é muito fácil e leva apenas alguns segundos.

Digite o material de interesse no campo de pesquisa rápida. Você pode, opcionalmente, limitar a sua pesquisa, especificando o país / padrão de escolha no campo designado e clique em Pesquisar.


Depois de selecionar o material de seu interesse, clique no link de dados para exibir dados de fadiga para o material selecionado. O número de conjuntos de dados disponíveis fadiga é exibido entre parênteses ao lado do link.


Porque as propriedades cíclicas da Total Materia Extended Range são neutras com as especificações padrão, você pode rever os dados de fadiga, clicando no link apropriado para qualquer um dos subgrupos. Os dados de vida de estresse são dados em um formato tabular, com gráficos se for o caso.


Referências explícitas às fontes de dados são apresentados para cada conjunto de dados. Por favor, veja o exemplo abaixo.


Para você é uma oportunidade de fazer um test drive na Total Materia, nós convidamos você a participar de uma comunidade de mais de 150.000 usuários registrados através da Total Materia Free Trial.