The Metal Injection Molding (MIM) Process


The Metal Injection Molding process is characterized by high pressure injection of powdered metals and binders rather than the conventional gravity fed processes.
The main applications for this technique are to produce small and often more complex parts often ranging in weight from 0.5 to 150g.

Metal Injection Molding (MIM) is a powder metallurgy process. The difference between MIM and conventional powder metallurgy is that in MIM, metal powder along with binders is injected under high pressure into the die or mold cavity instead of flowing by gravity.

The metal powder used for this is finer than conventional powder with particle sizes typically of 20 µm in diameter being used. Generally, the powder mix contains a much higher percentage of binders and flow agents. Wherein, binders generally include various waxes and thermoplastics. The compounded material is injected with conventional plastic injection molding machines (slightly modified) into metal dies normally having one to eight cavities.

The molded component is called the green part. The binders are first driven off either by heating, by solvent extraction, or by a combination of both methods and approximately 80% of the binders are removed. Debinding time is directly related to wall thickness. After debinding, the part is called the brown part which is porous and fragile but size remains the same as at the time of molding. The brown parts are then sintered as done in conventional powder metallurgy.

This is carried out in a vacuum or inert-atmosphere furnace at a temperature of approximately 1300°C depending on the material used for processing. However, sintering temperatures are generally well below the melting point of the material. The entire cycle including debinding normally takes about 24 to 36 hours.

Typical characteristics and applications of metal injection-molded parts

As mentioned above, typical metal injection-molded parts are small and complex in nature. The process is more advantageous for more complex parts. In this process, high precision is possible to achieve. This method eliminates the constraint imposed by conventional powder metallurgy methods i.e. the side wall should be parallel. Very small size parts i.e. smaller than a golf ball in volume, weigh in the range of 0.5 to 150 g, and a wall thickness of less than 6.3 mm can be achieved using this method. It is possible to produce multi-functional parts with thin walls, sharp corners, undercuts, cross holes, screw threads, contours, gear segments, and similar features without secondary operations.

The densities of parts produced through this process are normally greater than those of conventional powder metallurgy parts, ranging between 95 and 99 % of theoretical maximum density.

Figure 1: The MIM process

Figure 2: Molding machine in a MIM Shop

기술 자료 검색

검색할 어구를 입력하십시오:

검색 범위



Total Materia는 수천개의 재질에 대한 기계적 특성 테이터가 포함되어 있으며, 데이터를 검토하는 것은 매우 쉽습니다.

데이터베이스는 다양한 특성 정보를 포함하고 있으며, 수 많은 재질의 항복 응력, 인장 응력과 연신율은 데이터를 쉽게 찾을 수 있을 것입니다.

신속 검색에 검색할 재질명을 입력합니다. 원하신다면 국가/규격을 지정하신 후 검색 버튼을 클릭합니다.

Total Materia 데이터베이스에서 검색된 관심 재질의 목록이 즉시 생성됩니다.
관심 재질을 클릭합니다.

소그룹 페이지에서, 선택된 재질의 기계적 특성 링크를 클릭하여 데이터를 검토합니다. 기계적 특성 데이터 기록의 개수는 링크 옆 괄호 안에 표시됩니다.

기계적 특성 데이터는 참조를 위해 선택한 모든 재질 정보와 함께 표시됩니다.

기계적 특성 데이터는 가능한 모든 조건과 처리 상태에 대해 표시됩니다.

또한 한 번의 클릭으로 귀하의 선택에 따라 단위 값을 메트릭(SI)과 앵글로 색슨 단위로 전환할 수도 있습니다.

Total Materia 데이터베이스를 사용해 보실 수 있는 기회가 있습니다. 저희는 Total Materia 무료 체험을 통해 150,000명 이상의 사용자가 이용하고 있는 커뮤니티로 귀하를 초대합니다.