Effect of Small Additions on Structure and Solder Properties: Part Two
By M.Kamal1 and E.S.Gouda2,3

요약:

This variation can be attributed to the change of the dissolving atoms in the Sn-matrix as substitutional solid solutions; which have different mobility due to the change of their atomic radii and the change of the axial ratio c/a that may hinder the motion of substitutional atoms from one site to another.

Internal Friction

Figure 4 shows the variation of internal friction values of the Sn-9Zn-1X (X = Ag, Bi, Cu, or Sb) rapidly solidified alloys. It shows that, the value of internal friction changes with the alloying elements. It increases to the maximum value when adding Ag, and decreases to the minimum value when adding Cu. This variation can be attributed to the change of the dissolving atoms in the Sn-matrix as substitutional solid solutions; which have different mobility due to the change of their atomic radii and the change of the axial ratio c/a that may hinder the motion of substitutional atoms from one site to another.



Figure 4: Internal friction of the Sn-9Zn-1X (x= 0, Ag, Bi, Cu or Sb) alloys

Hardness and Yield Strength

Figure 5 shows the variation of the Vickers hardness of Sn-9Zn-1X (X = 0, Ag, Bi, Cu, or Sb) rapidly solidified alloys with the corresponding values of the yield strength [14]. It shows the Vickers hardness value of Sn-9Zn is equal to 9.7 Kg/mm2. Adding both Ag and Cu increase this value to (15.8 and 12.6) Kgf/mm2, respectively. This increase can be attributed to the precipitation hardening mechanism of the intermetallic compounds which are formed in these alloys. The minimum values (5.7 and 5.5 Kgf/mm2) obtained with adding Bi and Sb, respectively can be attributed to the complete solubility of the two metals in Sn-matrix that may cause embrittlement in the Sn-matrix.



Figure 5: Hardness number of the Sn-9Zn-1X (x = 0, Ag, Bi, Cu or Sb) alloys

Electrical Resistivity

Table 3 shows the room temperature resistivity (ρo) of the Sn-9Zn-1X (X= 0, Ag, Bi, Cu, or Sb) rapidly solidified lead-free solder alloys. It shows that, the resistivity of the eutectic alloy is equal to 16.26 Ωcm. All additions to this alloy increase this value except the case of Bi that slightly decreases to 16.0 Ωcm. This decrease can be attributed to precipitation of the Zn phase, which has lower value of resistivity than that of the Sn-matrix. While, the higher values can be attributed to the formation of the intermetallic compounds which act as scattering centers for conduction electrons.

Figure 6 shows the temperature dependence of resistivity in the range of 300-420 K. It shows a slight increase of resistivity with temperature in the range of 300-360 K for all alloys followed by a fast increase in the range of 360-420 K. High temperatures may cause disturbance in the lattice order due to thermal vibration, then the probability of the electrons being scattered by phonons and by impurities are increased.

Also, as expected, the temperature of the solder joint can be as high as 300 K, the temperature coefficient of resistivity (TCR) denoted by the symbol (α) then becomes a property of interest. It was calculated from the relation;

α = slope/ρo

Ideally, the TCR should be as small as possible in this range of temperatures. The values of TCR of the Sn-9Zn-1X (X= 0, Ag, Bi, Cu, or Sb) are illustrated in Table 3. It indicates that, the value of Sn-9Zn is equal to 0.0097 K-1.

All additions to this alloy decrease this value and the minimum value (0.0039 K-1) is obtained in the case of adding Bi, which means the scattering by phonons becomes of less importance than that caused by crystal defects.

Alloy Resistivity
µΏcm
TCR
K-1
Sn-9Zn 16.2±0.2 0.0097
Sn-9Zn-1Ag 19.9±0.1 0.005
Sn-9Zn-1Bi 16.0±0.3 0.0039
Sn-9Zn-1Cu 19.1±0.2 0.0069
Sn-9Zn-1Sb 18.4±0.4 0.0071

Table 3: Electrical properties of the Sn-9Zn-1X (X=0, Ag, Bi, Cu, or Sb) alloys



Figure 6: Electrical resistivity of the Sn-9Zn-1X (X = 0, Ag, Bi, Cu or Sb) alloys versus temperature

Conclusion

The present paper aimed to investigate the structural changes and some physical properties of Sn-9Zn eutectic lead-free solder alloy with small additions of Ag, Bi, Cu and Sb as ternary additions.

The results showed that, adding Ag and Cu lead to form the intermetallic compounds Ag3Sn, AgZn, and Cu6Sn5, Cu5Zn8, respectively which act as hard inclusions in a soft matrix, then increase Vickers hardness values of these two alloys, while act as scattering centers for Conduction electrons, and also increase the electrical resistivity of these alloys.

Complete solubility of Bi and Sb in Sn-matrix were obtained, which may cause embrittlement of these alloys. The change of the dissolving atoms in Sn-matrix as substitutional solid solutions, which have different mobility's due to the change of their atomic radii, causes the change of internal friction of these alloys. Moreover, change of the axial ratio c/a may hinder the motion of substitutional atoms from one site to another. Also the connection between the Young's modulus and axial ratio of the Sn-matrix that was evident before was also confirmed here.


1 Metal Physics Lab., Psysics Department, Faculty of Science, Mansoura University, Egypt.
2 Department of Solid State Physiscs, Physiscs, Division, National Research Center, Dokki, Giza, Egypt.
3 Physiscs Department, Faculty of Science, Jazan University, Gizan, K.S.A.

기술 자료 검색

검색할 어구를 입력하십시오:

검색 범위

본문
키워드

머릿글
요약

이 문서는 전체 문서 중 일부분입니다. 이 주제에 대해 더 읽고 싶으시면 아래 링크를 클릭하시면 됩니다.

Total Materia는 용접용으로 적합한 다양한 국가와 규격 내 수천개의 재질에 대한 정보를 포함하고 있습니다.

재질의 화학적 조성, 기계적 특성, 물리적 특성, 탄소 등가 데이터와 용접용으로 재질 이용 시 필요한 정보 등의 전체적인 특성 정보들을 어디서든 검토하실 수 있습니다.

고급 검색을 이용하여, 검색 조건의 재질 리스트에서 '용접 필러 재료'를 선택합니다. 검색 범위 좀 더 줄이기를 원하신다면 국가/규격과 같은 다른 조건을 지정할 수 있습니다.

검색 버튼을 클릭합니다.


선택된 정보에 부합하는 일련의 재질이 검색됩니다.


결과 리스트에서 재질을 선택하시면, 일련의 규격 사양 소그룹이 나타납니다.

여기에서 선택한 재질의 특정 특성 데이터를 검토하실 수도 있고, 강력한 상호 참조 표를 이용하여 유사 재질이나 등가 재질을 검토하는 것 또한 가능합니다.


자세한 특성 데이터를 보시려면 특성 데이터 링크를 클릭하세요.


Total Materia 데이터베이스를 사용해 보실 수 있는 기회가 있습니다. 저희는 Total Materia 무료 체험을 통해 150,000명 이상의 사용자가 이용하고 있는 커뮤니티로 귀하를 초대합니다.