CMT Welding: Part Two

概要:

Specifically aimed at the sheet metal industry, Cold Metal Transfer welding processes are a prospective set of methodologies where there is a deep requirement for control over welding distortions or deformations.
Traditionally a GMAW process, work on CMT technology has led to the possibility to apply these techniques to a conventional MIG/MAG processes meaning more possibilities to utilize its advantages as a cold welding technique.

The CMT (Cold Metal Transfer) process is a revolution in welding technology, with respect to both, welding equipment and welding applications. The CMT process is not only a completely new process, which is unknown until now, but it also opens a new field of application since it widens the limits of Gas Metal Arc Welding (GMAW), allowing the arc joining of steel to aluminium in a reproducible manner for the first time. There are materials and applications that cannot withstand the constant heat of a welding process. In order to avoid weld-pool drop-through, to be spatter-free, and to be amenable to metallurgical joining, they need lower temperatures. With CMT, this is now possible. The term “cold” has to be understood in terms of a welding process, but when set against the conventional MIG/MAG process, CMT is indeed a cold process.

As mentioned above, CMT can be described as a GMAW process where heat input is low as compared to the conventional dip arc process. The CMT-process is a dip arc process with a completely new method of the droplet detachment from the wire. In the conventional dip arc process the wire is moved forward until a short circuit occurs for welding happens (see Figure 1). At that moment, the welding current rises. Causing the short circuit to reopen and allowing the arc to ignite again. There are two main features of the MIG/MAG process: on the one hand the high short circuit current corresponds to a high heat input. On the other hands the short circuit opens in a rather uncontrolled manner, resulting in lots of spatters in the conventional dip arc process.



Figure 1: CMT arc sequence

Using the CMT method, 1mm thick DX54D+Z200 steel sheets were joined to 1.5mm thick AW5182-H111 sheets at Fronius International GmbH using 1.2mm diameter Al99.5 and AlSi3Mn1 filler wires, all parent materials being provided by Voest-Alpine Stahl GmbH. The optimized Voest-Alpine welding geometry (Figure 2) and optimized parameters for the CMT welding process were chosen (Table 1). The samples were clamped during the joining process in order to avoid distortion.

For optical (OM) and scanning electron (SEM) microscopy, specimens were cut, ground and polished until a specular surface was obtained. Specimen microstructure was characterized in the SEM using electron back scattering diffraction (EBSD).



Figure 2: (a) Sequence of CMT process stages and b) Geometry of the steel-aluminum CMT joint (detail from (a), right)



Table 1: Welding parameters

Where is: vS: Welding speed, vD: Wire feeding speed, I: Current, U: Voltage, f: Frequency.

Residual stress analysis was carried out using the instrument G3 at HASYLAB, DESY, Hamburg, Germany at 6.4 keV energy. Residual stresses in longitudinal (along the weld) and in transversal direction were determined by the sin method (Al311 and α-Fe200 reflections) at the top and bottom of a AW5182-H111 aluminum to DX54D+Z200 steel butt-joint with AlSi3Mn1 filler, in the center of the weld seam and along both the steel and aluminum sheets up to 80mm distance from the weld centerline (Figure 3). Face and bottom sides of the butt joint were electro-polished in order to access residual stresses in a depth of 100μm beneath the original surface. After electro-polishing residual stresses were determined in the weld seam, and in the aluminum and steel sheets up to a distance of 35mm from the weld seam. The diffraction elastic constants were calculated using Kröner’s model.



Figure 3: Scheme of stress measurement locations

Micrographs of the welded samples reveal different intermetallic phase morphologies (Figure 4) at the interface between the molten filler and the steel when using Al99.5 and AlSi3Mn1 filler materials. The chosen welding parameters ensured that the thickness of the intermetallic phase seam (IMP) in both welds with Al99.5 filler (IMP thickness about 3.5μm) and AlSi3Mn1 filler (IMP thickness about 2.5μm) was well below the 10μm limit, which often has been claimed to be critical with respect to weld toughness. The phases identified in the IMP of the weld with the Al99.5 filler are θ-phase Al3Fe (adjacent the filler) and η-phase Al5Fe2 (adjacent to the steel). The intermetallic phase seam in case of the AlSi3Mn1 filler contains also the θ-phase Al3Fe and the η-phase Al5Fe2 and additionally an Al(Fe,Mn)Si – phase.



Figure 4: SE-SEM micrograph showing the intermetallic phase seam (IMP) in welds with (a) Al99.5 filler and (b) AlSi3Mn1 filler

The residual stress distribution in longitudinal direction both at the top (Figure 5a) and the bottom side of the weld (Figure 5b) are characterized by compressive residual stresses within the steel plate parent material, which turn into tensile residual stresses in the heat affected zone with a steep gradient. The filler in the weld seam and the heat affected zone in the aluminum alloy are under tensile residual stresses, and the aluminum parent material contains balancing compressive residual stresses in longitudinal direction. The maximum value of the residual stresses in the aluminum alloy, on the top side of the weld near the weld seam, is as high as 100 MPa and, thus, about 2/3 of its yield strength. The residual stress distribution in transversal direction at the bottom side of the weld (Figure 6) is very similar to the residual stress distribution in longitudinal direction. The residual stress values encountered are slightly lower in transversal direction compared to the longitudinal direction.



Figure 5: Residual stress state along the longitudinal direction (↓) of a joint with AlSi3Mn1 aluminum filler on the surface and ~100μm beneath on (a) top and (b) bottom side



Figure 6: Residual stress state along the transversal direction (→) of a joint with AlSi3Mn1 aluminum filler on bottom side surface and ~100μm beneath it. [5] [4]


References

1. V. V. Ruiwale, A. A. Kadam, S. M. Kulkarni, M. S. Jadhao: A Review on Recent Trends in Robotic Welding, International Journal of Engineering Science and Innovative Technology (IJESIT) Volume 4, Issue 5, September 2015, ISSN: 2319-5967;

2. Motoman & CMT, Arc welding robot package MOTOPAC-WF400, YASKAWA, 2009-2010 YASKAWA ELECTRIC CORPORATION;

3. Il processo di saldatura CMT, Cold Metal Transfer, Arroweld Italia Spa, Distributore in esclusiva per LÍtalia dal 1993, Fronius, 2009;

4. L. Agudo Jácome: Influence of Alloying Elements on the Microstructure and Mechanical Properties of Steel-Aluminium-Joints Produced by Metal Arc Joining with Special Focus on the Intermetallic Phase Seam, PhD thesis, Ruhr-Universität Bochum, Bochum 2008, Fakultät für Maschinenbau der Ruhr-Universität Bochum, Bochum 2008, Accessed Oct 2017.

ナレッジベース検索

検索したい語句を入力:

検索方法

全文一致
キーワード

前方一致
要約

Total Materiaデータベースは世界の国々と広範な規格に関する数千種類の溶接に適した材料に関するデータを収録しております。

溶接に関する助言のほか必要に応じて、化学組成分、機械的特性、物理特性、炭素当量データなどの材料特性を御覧になれます。

高度な検索のページで材料グループのポップアップリストから’溶接フィラー材’を選び検索条件を決定します。さらに国/規格のフィールドを使い検索条件を絞ることもできます。

確定をクリックします。


選んだ材料の材料リストが表示されます。


結果リストで材料をクリックすると規格から導きだされるサブグループリストが表示されます。

そこから選んだ材料の特性を見る事ができさらにパワフルな相互参照表により類似材料、同等材料をみることもできます。


対象とする材料の特性データをクリックします。


Total Materiaデータベースをあなたにテスト評価を頂くために15万人以上の方が登録されている無料お試しコミュニティ-へ御招待致します。