Sub-Liquidus Casting (SLC)

摘要:

Sub-Liquidus Casting is one of many known semi-solid metal technologies and holds great value offering grain refinement accompanied by proper control of melt temperature and cooling rate.
Some key advantages include improved tool life and time savings through quicker solidification.

Semi-solid metal (SSM) technology is different from the conventional forming processes which uses either solid or liquid metals as the starting material. This process deals with slurries, which in principle, can be produced in any material systems where liquid and solid phases coexist over a freezing range. The SSM process has advantages over other casting processes which are associated with less porosity and shrinkage voids, lower processing temperature and shorter time, less mold erosion, faster cycle time and longer die life.

Semisolid processing consists of two or three stages. First, a globular structure within the semisolid alloy is created. Then the semisolid slurry is used either directly for applications that require slurry (rheocasting) to form a component with near-net shape or be solidified as billets for later reheating during thixocasting.

There is a wide range of (SSM) processes patented or under investigation within research and development centers worldwide.

One of them is the Sub-Liquidus Casting (SLC) process. The process was developed by THT Presses Inc., USA, and explores a phenomenon of grain refinement accompanied by proper control of melt temperature and cooling rate.



Figure 1: 400t THT press machine

In fact, the successful process cycle can only be implemented if good grain refinement is achieved in the molten alloy supplied to the machine. The grain refined material is poured into the shot sleeve at temperatures just above liquidus and cooled to a semisolid state before transfer to the mold. For practical reasons, a superheat of 5–10°C is used to compensate for heat losses during alloy transfer from the furnace to the shot sleeve.

The slurry is developed within the shot sleeve, which means that no slurry processing equipment is required outside of the casting machine (Figure 2). For aluminum alloy A356 the temperature in the chamber before injection is between 570°C and 590°C. For proper grain refinement, fine rosettes transform into globules within seconds while coarse dendrites in poorly refined alloy would require more time to transform into globular features.

Although the machine features alone do not constitute the entire process, the specific features allow its proper implementation. They include large and shallow shot diameter and short stroke as well as a unique gate plate. The shot piston and sleeve wall temperatures are controlled to extract the heat primarily through the piston and less through the shot sleeve walls. The melt is transferred to the die cavity at very low velocity of the order of 1 m/s–2 m/s through a gate plate with multiple gates.



Figure 2: The concept of sub-liquidus casting (SLC) developed by THT Presses Inc.

The advantages and requirements of sub-liquidus casting (SLC) are summarized as follows:

SLC advantages:
1) Breakway gates
2) Less sensitive to:
• Microstructural effects on properties
• Metal flow in die cavity and entrapment of bubbles
• Directional solidification
3) Less thermal input to die (~50% less)
• Longer tool life (2-5 times)
• Quicker solidification

SLC Requirements:
1) Grain refinement
2) Melt temperature (in furnace)
3) Melt cooling in shot sleeve
4) Time to develop slurry structure
5) Melt flow into die cavity



Figure 3: Typical A356 alloy SLC microstructure (x100)


References

1. S. Nafizi: Effects of grain refining and modification on the microstructural evolution of semi-solid 356 alloy, University of Quebec at Chicoutimi, April 2006, Accessed Nov 2016

2. F.Czerwinski: Magnesium Injection Molding, Springer, 2008, ISBN-13: 978-0-387-72399-0 e-ISBN-13: 978-0-387-72528-4

3. A.Forn, M.T.Baile, S.Menargues, I.Espinosa: Corrosion resistance improve by hard anodize A356 aluminium alloy by subliquidus casting, OAI, 2008

4. Sub-Liquidus Casting: Process Concept and Product Properties, ss, Accessed Nov 2016

搜索钢材指南知识库

输入搜索词:

搜索项

全文
关键字

标题
摘要

The Total Materia database contains many thousands of casting materials across a large range of countries and standards.

Where available, full property information can be viewed for materials including chemical composition, mechanical properties, physical properties, advanced property data and much more.

Using the Advanced Search page, it is possible to search for materials by their key descriptive words detailed in the standard title by using the Standard Description function of Advanced Search.

It maybe that you need to further narrow the search criteria by using the other fields in the Advanced Search page e.g. Country/Standard.

Then click Submit.

solution img

A list of materials will then be generated for you to choose from.

solution img

After clicking a material from the resulting list, a list of subgroups derived from standard specifications appears.

From here it is possible to view specific property data for the selected material and also to view similar and equivalent materials in our powerful cross reference tables.

solution img

For example, by clicking on the chemical composition link on the subgroup page it is possible to view chemical composition data for the material.

solution img

For you’re a chance to take a test drive of the Total Materia database, we invite you to join a community of over 150,000 registered users through the Total Materia Free Demo.