AA Alclad one side 7075 アルミニウム合金
材料グループ:
非鉄合金 / アルミニウム合金
国 / 規格:
米国 / AA
データ更新
最新情報: 2019-03
更新の総数: 1
更新履歴
この材料には 58 件の特性データがありますが、現在表示されているのは一部のみです。
登録して、温度や条件ごとの詳細データを含む全ての材料特性データにアクセスしましょう。
全ての材料データを見る ›
無料登録・すぐにアクセス
無料登録・すぐにアクセス
AA Alclad one side 7075 物理的性質
温度
この材料には 58 件の特性データがありますが、現在表示されているのは一部のみです。
温度や条件ごとの詳細な物理データを閲覧
全ての材料データを見る ›
無料登録・すぐにアクセス
無料登録・すぐにアクセス
AA Alclad one side 7075 熱処理
- The times and temperatures are typical for various forms, sizes and methods of manufacture and may not exactly describe the optimum treatment for a specific item.
The nominal temperatures at which metal is heated (applies both for solution and precipitation heat treatment) should be attained as rapidly as possible and maintained ± 5°C of nominal during the time at temperature.
The time at precipitation heat treatment temperature will depend on time required for load to reach temperature. The times shown are based on rapid heating, with soaking time measured from the time the load reached within 5°C of the applicable temperature.
Material should be quenched from the solution heat-treating temperature as rapidly as possible and with minimum delay after removal from the furnace. Quenching is typically performed by immersion of wrought products in a cold water bath, although some forgings are quenched in hot-water. Quenching may be performed by alternative means such as total immersion in an aqueous polymer solution, liquefied gas, hot water, or boiling water, or by air blast or fog to minimize distortion provided samples from the material. The use of high-velocity high-volume jets of cold water is also effective for some materials.
The aging of aluminum alloy 7075 from any temper to the T73 or T76 temper series requires closer than normal controls on aging practice variables such as time, temperature, heating-up rates, etc., for any given item. In addition to the above, when re-aging material in the T6 temper series to the T73 or T76 temper series, the specific condition of the T6 temper material (such as its property level and other effect of processing variables) is extremely important and will affect the capability of the re-aged material to conform to the requirements specified for the applicable T73 or T76 temper series.
For sheet
With optimum ingot homogenization, heat treating temperatures as high as 500°C are sometimes acceptable.
Temper W: Solution heat treated at 480°C, quenched, naturally aged. With optimum ingot homogenization, heat treating temperatures as high as 500°C are sometimes acceptable.
Temper T6: Solution heat treated at 480°C, quenched, precipitation heat treated ta 120°C for 24 hours. An alternate two-stage treatment comprised of 4 hours at 95°C followed by 8 hours at 155°C also may be used.
Temper T73: Solution heat treated at 480°C, quenched, a two-stage treatment comprised of 6 to 8 hours at 105°C followed by a second-stage of 24-30 hours at 165°C. An alternate two-stage treatment comprised of 6-8 hours at 107°C followed by a second state of 14-18 hours at 168°C may be used providing a heating up of 14°C per hour is used.
Temper T76: Solution heat treated at 480°C, quenched, a two-stage treatment comprised of 3-30 hours at 121°C followed by 15-18 hours at 163°C. An alternate two-stage treatment of 8 hours at 99°C followed by 24-28 hours at 163°C may be used.
Temper T62: Solution heat treated at 480°C, quenched, precipitation heat treated ta 120°C for 24 hours. An alternate two-stage treatment comprised of 4 hours at 95°C followed by 8 hours at 155°C also may be used.
For plate
With optimum ingot homogenization, heat treating temperatures as high as 500°C are sometimes acceptable. For plate thickness over 4 inches and for rod diameters or bar thicknesses over four inches, a maximum temperature of 490°C is recommended to avoid eutectic melting.
Temper W51: Solution heat treated at 480°C, quenched, naturally aged. Stress-relieved by stretching is required to produce a specified amount of permanent set subsequent to solution heat treatment.
Temper W: Solution heat treated at 480°C, quenched, naturally aged.
Temper T651: Solution heat treated at 480°C, quenched, precipitation heat treated at 120°C for 24 hours. An alternate two-stage treatment comprised of 4 hours at 95°C followed by 8 hours at 155°C also may be used. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.
Temper T7351: Solution heat treated at 480°C, quenched, a two-stage treatment comprised of 6 to 8 hours at 105°C followed by a second-stage of 24-30 hours at 165°C. An alternate two-stage treatment comprised of 6-8 hours at 107°C followed by a second state of 14-18 hours at 168°C may be used providing a heating up of 14°C per hour is used. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.
Temper T7651: Solution heat treated at 480°C, quenched, a two-stage treatment comprised of 3-30 hours at 121°C followed by 15-18 hours at 163°C. An alternate two-stage treatment of 8 hours at 99°C followed by 24-28 hours at 163°C may be used. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.
Temper T62: Solution heat treated at 480°C, quenched, precipitation heat treated at 120°C for 24 hours. An alternate two-stage treatment comprised of 4 hours at 95°C followed by 8 hours at 155°C also may be used.
AA Alclad one side 7075 機械的特性
温度
AA Alclad one side 7075国際相当材
5件中5を表示しています。
材料
規格
国 / 製造業者
同等のカテゴリ
相当区分は、化学成分および機械的特性の比較に基づいています。実際の用途への適用にあたっては、必ず該当する規格要件に照らして適合性をご確認ください。
用途に最適な材料を選定 - デモを予約
- 5相互参照
- -成分
- 33機械的特性
- 3物理的特性
- 1熱処理
- -金属組織
- -被削性
- -応力-ひずみ
- -成形性
- -疲労
- -破壊
- -クリープ
- 14接合
- -コーティング
- -寸法
- -トライボロジ
- -腐食
- -時効
- -耐候性
- -照射
- 2総仕入先数