AA 6162 Aleaciones de aluminio

Grupo de materiales: Aleaciones No Ferrosas / Aleaciones de aluminio

País/Estándar: Estados Unidos / AA

Precio indicativo:

Actualizaciones de datos

Última actualización: 2019-04

Número total de actualizaciones: 1

Historial de actualizaciones

Este material cuenta con 65 propiedades — aquí solo se muestra una parte.

Accede a todas las propiedades del material, incluyendo valores detallados según temperatura y condiciones.

AA 6162 Composición química

Criterios

Valor

Unidad

Número CAS

Criterios

Valor

Resto.

Unidad

Número CAS

7429-90-5

Criterios

Valor

≤ 0.10

Unidad

Número CAS

7440-47-3

Criterios

Valor

≤ 0.20

Unidad

Número CAS

7440-50-8

Criterios

Valor

val1

Unidad

Número CAS

7439-89-6

Criterios

Valor

val1

Unidad

Número CAS

7439-95-4

Criterios

Valor

val1

Unidad

Número CAS

7439-96-5

Criterios

Other each

Valor

val1

Unidad

Número CAS

Criterios

Other total

Valor

val1

Unidad

Número CAS

Criterios

Valor

val1

Unidad

Número CAS

7440-21-3

Criterios

Valor

val1

Unidad

Número CAS

7440-32-6

Criterios

Valor

val1

Unidad

Número CAS

7440-66-6

International alloy designations and chemical composition limits for wrought aluminum and wrought aluminum alloys - Teal Sheets (2025), 2025

¿Buscas datos completos de desempeño de materiales?

AA 6162 Propiedades físicas

Temperatura

0 - 30°C

Propiedad/Valor

Módulo de elasticidad

69 — 79 GPa

Desbloquea todos los detalles

Densidad

2.6 — 2.9 kg/dm³

Desbloquea todos los detalles

Coeficiente de Poisson

0.33

Desbloquea todos los detalles

Este material cuenta con 65 propiedades — aquí solo se muestra una parte.

Consulta propiedades físicas detalladas en distintas temperaturas y condiciones.

AA 6162 Tratamiento Térmico

The times and temperatures are typical for various forms, sizes and methods of manufacture and may not exactly describe the optimum treatment for a specific item.

The nominal temperatures at which metal is heated (applies both for solution and precipitation heat treatment) should be attained as rapidly as possible and maintained ± 5°C of nominal during the time at temperature.

The time at precipitation heat treatment temperature will depend on time required for load to reach temperature. The times shown are based on rapid heating, with soaking time measured from the time the load reached within 5°C of the applicable temperature.

Material should be quenched from the solution heat-treating temperature as rapidly as possible and with minimum delay after removal from the furnace. Quenching is typically performed by immersion of wrought products in a cold water bath, although some forgings are quenched in hot-water. Quenching may be performed by alternative means such as total immersion in an aqueous polymer solution, liquefied gas, hot water, or boiling water, or by air blast or fog to minimize distortion provided samples from the material. The use of high-velocity high-volume jets of cold water is also effective for some materials.

For extruded rod, bar, profiles and tube

Temper T1: Quenched directly from the extrusion press, naturally aged. Some extrusions may be adequately quenched using a room temperature air blast. By definition, this temper designation is that which would apply after natural aging even though mechanical properties for this alloy-temper product have not been registered.

Temper T1510: Quenched directly from the extrusion press precipitation heat treated at 175°C for 8 hours. Some extrusions may be adequately quenched using a room temperature air blast. Stress-relieved by stretching is required to produce a specified amount of permanent set subsequent to solution heat treatment. By definition, this temper designation is that which would apply after natural aging even though mechanical properties for this alloy-temper product have not been registered.

Temper T1511: Quenched directly from the extrusion press precipitation heat treated at 175°C for 8 hours. Some extrusions may be adequately quenched using a room temperature air blast. Stress-relieved by stretching is required to produce a specified amount of permanent set subsequent to solution heat treatment. By definition, this temper designation is that which would apply after natural aging even though mechanical properties for this alloy-temper product have not been registered.

Temper T4: Solution heat treated at 525°C, quenched, naturally aged. By definition, this temper designation is that which would apply after natural aging even though mechanical properties for this alloy-temper product have not been registered.

Temper T4510: Solution heat treated at 525°C, quenched, naturally aged. Stress-relieved by stretching is required to produce a specified amount of permanent set subsequent to solution heat treatment. By definition, this temper designation is that which would apply after natural aging even though mechanical properties for this alloy-temper product have not been registered.

Temper T4511: Solution heat treated at 525°C, quenched, naturally aged. Stress-relieved by stretching is required to produce a specified amount of permanent set subsequent to solution heat treatment. By definition, this temper designation is that which would apply after natural aging even though mechanical properties for this alloy-temper product have not been registered.

Temper T5: Solution heat treated at 525°C, quenched, precipitation heat treated at 175°C for 8 hours.

Temper T5510: Solution heat treated at 525°C, quenched, precipitation heat treated at 175°C for 8 hours. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

Temper T5511: Solution heat treated at 525°C, quenched, precipitation heat treated at 175°C for 8 hours. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

Temper T6: Solution heat treated at 525°C, quenched, precipitation heat treated at 175°C for 8 hours.

Temper T6510: Solution heat treated at 525°C, quenched, precipitation heat treated at 175°C for 8 hours. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

Temper T6511: Solution heat treated at 525°C, quenched, precipitation heat treated at 175°C for 8 hours. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

AA 6162 Propiedades mecánicas

Temperatura

0 - 30°C

Propiedad/Valor

Resistencia a la Tracción

≥ 255 MPa

Desbloquea todos los detalles

Alargamiento, A

≥ 7 %

Desbloquea todos los detalles

Límite elástico, Rp0.2

≥ 235 MPa

Desbloquea todos los detalles

¿Buscas información completa sobre propiedades mecánicas para tomar la mejor decisión?

Obtén información completa sobre resistencia, dureza, fatiga y más.

AA 6162 Materiales Internacionales Equivalentes

Mostrando 11 de 11 resultados.

Material

Estándar

País / Productor

Categoría de Equivalencia

Material

A96162

Estándar

UNS

País / Productor

Estados Unidos

Categoría de Equivalencia

Oficial

Material

SB-241 6162

Estándar

ASME

País / Productor

Estados Unidos

Categoría de Equivalencia

Composición 100%

Material

6162

Estándar

ISO

País / Productor

Internacional

Categoría de Equivalencia

Oficial

Material

SB-221 6162

Estándar

ASME

País / Productor

Estados Unidos

Categoría de Equivalencia

Composición 100%

Material

B 221 6162

Estándar

ASTM

País / Productor

Estados Unidos

Categoría de Equivalencia

Composición 100%

Material

B 241 6162

Estándar

ASTM

País / Productor

Estados Unidos

Categoría de Equivalencia

Composición 100%

Material

6162

Estándar

País / Productor

China

Categoría de Equivalencia

Composición 100%

Material

6162

Estándar

País / Productor

India

Categoría de Equivalencia

Composición 100%

Material

6162

Estándar

NBR

País / Productor

Brasil

Categoría de Equivalencia

Composición 100%

Material

6162

Estándar

NMX

País / Productor

México

Categoría de Equivalencia

Composición 100%

Material

6162

Estándar

SAE

País / Productor

Estados Unidos

Categoría de Equivalencia

Composición 100%

Las categorías de equivalencia reflejan comparaciones de composición química y propiedades mecánicas; siempre verifique la idoneidad del material según la especificación aplicable a su aplicación.

¿Necesita la lista completa de los 11 internacionales equivalentes?

Consulte los grados 11 equivalentes con el detalle completo de correspondencias por norma, fabricante y categoría de equivalencia.

Optimiza la selección de materiales para tu aplicación - Reservar una demo

¿Buscas comparar materiales y tomar mejores decisiones?

Accede a datos confiables de materiales, compara opciones y decide con mayor rapidez.

Con Total Materia, puedes:

Comparar materiales basándote en datos reales de ingeniería

Encontrar materiales equivalentes entre distintas normas

Evaluar el desempeño según tus condiciones específicas

Verificar el cumplimiento con normativas internacionales

Descubre cómo funciona para tu aplicación específica

Realizar un Recorrido Guiado

11Referencias cruzadas

22Composición
27Propiedades mecánicas
4Propiedades físicas
1Tratamiento térmico
-Metalografía
-Maquinabilidad

-Esfuerzo-Deformación
-Conformabilidad
-Fatiga
-Fractura
-Bicho raro

-Uniones
-Revestimientos
-Dimensiones
-Tribología

-Corrosión
-Envejecimiento
-Resistencia a la intemperie
-Irradiación

-Proveedores Totales