AA 2014 Alüminyum alaşım

Malzeme grubu: Demirdışı Alaşımlar / Alüminyum alaşım

Ülke/Standart: Amerika Birleşik Devletleri / AA

Belirleyici fiyat:

Veri güncellemeleri

Son Güncelleme: 2025-09

Toplam güncelleme sayısı: 20

Güncelleme Geçmişi

2025-08 2025-05 2025-01 2024-10 2024-03 2020-09 2020-08 2020-07 2020-04 2019-04 2017-12 2017-11 2017-04 2016-11 2016-02 2015-03 2014-11 2014-06 2013-11

Bu malzemenin 3051 özelliği vardır - burada yalnızca bir alt kümesi gösterilmektedir.

Sıcaklıklar ve koşullar genelinde ayrıntılı değerler de dahil olmak üzere tam malzeme özelliklerinin kilidini açın.

AA 2014 Kimyasal bileşim

Kriterler

Değer

Birim

CAS numarası

Kriterler

Değer

Remainder

Birim

CAS numarası

7429-90-5

Kriterler

Değer

≤ 0.10

Birim

CAS numarası

7440-47-3

Kriterler

Değer

3.9 – 5.0

Birim

CAS numarası

7440-50-8

Kriterler

Değer

val1

Birim

CAS numarası

7439-89-6

Kriterler

Değer

val1

Birim

CAS numarası

7439-95-4

Kriterler

Değer

val1

Birim

CAS numarası

7439-96-5

Kriterler

Other each

Değer

val1

Birim

CAS numarası

Kriterler

Other total

Değer

val1

Birim

CAS numarası

Kriterler

Değer

val1

Birim

CAS numarası

7440-21-3

Kriterler

Değer

val1

Birim

CAS numarası

7440-32-6

Kriterler

Ti+Zr

Değer

val1

Birim

CAS numarası

Kriterler

Değer

val1

Birim

CAS numarası

7440-66-6

International alloy designations and chemical composition limits for wrought aluminum and wrought aluminum alloys - Teal Sheets (2025), 2025

Tam malzeme performans verilerini mi arıyorsunuz?

AA 2014 Fiziksel özellikler

Sıcaklık

≤ 0°C 0 - 30°C 30 - 100°C 100 - 300°C ≥ 300°C

Özellik / Değer

Elastisite Modülü

69 — 79 GPa

Tüm ayrıntıların kilidini açın

Yoğunluk

val1 kg/dm³

Tüm ayrıntıların kilidini açın

Isıl İletkenlik

val1 W/(m∙°C)

Tüm ayrıntıların kilidini açın

Elektriksel Direnç

val1 Ω∙mm²/m

Tüm ayrıntıların kilidini açın

Elektriksel İletkenlik

val1 S/m

Tüm ayrıntıların kilidini açın

Ergime Sıcaklığı

val1 °C

Tüm ayrıntıların kilidini açın

Poisson Katsayısı

val1

Tüm ayrıntıların kilidini açın

Isıl Genleşme Katsayısı (CTE)

val1 10^-6/°C

Tüm ayrıntıların kilidini açın

Bu malzemenin 3051 özelliği vardır - burada yalnızca bir alt kümesi gösterilmektedir.

Sıcaklık ve koşullar genelinde ayrıntılı fiziksel özellik değerlerinin kilidini açın.

AA 2014 Isıl İşlem

The times and temperatures are typical for various forms, sizes and methods of manufacture and may not exactly describe the optimum treatment for a specific item.

The nominal temperatures at which metal is heated (applies both for solution and precipitation heat treatment) should be attained as rapidly as possible and maintained ± 5°C of nominal during the time at temperature.

The time at precipitation heat treatment temperature will depend on time required for load to reach temperature. The times shown are based on rapid heating, with soaking time measured from the time the load reached within 5°C of the applicable temperature.

Material should be quenched from the solution heat-treating temperature as rapidly as possible and with minimum delay after removal from the furnace. Quenching is typically performed by immersion of wrought products in a cold water bath, although some forgings are quenched in hot-water. Quenching may be performed by alternative means such as total immersion in an aqueous polymer solution, liquefied gas, hot water, or boiling water, or by air blast or fog to minimize distortion provided samples from the material. The use of high-velocity high-volume jets of cold water is also effective for some materials.

For flat sheet

Temper T3: Solution heat treated at 500°C, quenched, naturally aged. Cold work subsequent to solution heat treatment is required to attain the specified mechanical properties for this temper.

Temper T42: Solution heat treated at 500°C, quenched, naturally aged.

Temper T62: Solution heat treated at 500°C, quenched, precipitation heat treated at 160°C for 18 hours.

For coiled sheet

Temper T4: Solution heat treated at 500°C, quenched, naturally aged.

Temper T42: Solution heat treated at 500°C, quenched, naturally aged.

Temper T6: Solution heat treated at 500°C, quenched, precipitation heat treated at 160°C for 18 hours.

Temper T62: Solution heat treated at 500°C, quenched, precipitation heat treated at 160°C for 18 hours.

For plate

Temper T451: Solution heat treated at 500°C, quenched, naturally aged. Stress-relieved by stretching is required to produce a specified amount of permanent set subsequent to solution heat treatment.

Temper T42: Solution heat treated at 500°C, quenched, naturally aged.

Temper T651: Solution heat treated at 500°C, quenched, precipitation heat treated at 160°C for 18 hours. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

Temper T62: Solution heat treated at 500°C, quenched, precipitation heat treated at 160°C for 18 hours.

For rolled or cold finished wire, rod and bar

Temper T4: Solution heat treated at 500°C, quenched, naturally aged.

Temper T451: Solution heat treated at 500°C, quenched, naturally aged. Stress-relieved by stretching is required to produce a specified amount of permanent set subsequent to solution heat treatment.

Temper T42: Solution heat treated at 500°C, quenched, naturally aged.

Temper T6: Solution heat treated at 500°C, quenched, precipitation heat treated at 160°C for 18 hours. An alternative treatment comprised of 8 hours at 175°C also may be used.

Temper T651: Solution heat treated at 500°C, quenched, precipitation heat treated at 160°C for 18 hours. An alternative treatment comprised of 8 hours at 175°C also may be used. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

Temper T62: Solution heat treated at 500°C, quenched, precipitation heat treated at 160°C for 18 hours. An alternative treatment comprised of 8 hours at 175°C also may be used.

For extruded wire, rod, bar, profiles and tube

Temper T4: Solution heat treated at 500°C, quenched, naturally aged.

Temper T4510: Solution heat treated at 500°C, quenched, naturally aged. Stress-relieved by stretching is required to produce a specified amount of permanent set subsequent to solution heat treatment.

Temper T4511: Solution heat treated at 500°C, quenched, naturally aged. Stress-relieved by stretching is required to produce a specified amount of permanent set subsequent to solution heat treatment.

Temper T42: Solution heat treated at 500°C, quenched, naturally aged.

Temper T6: Solution heat treated at 500°C, quenched, precipitation heat treated at 160°C for 18 hours. An alternative treatment comprised of 8 hours at 175°C also may be used.

Temper T6510: Solution heat treated at 500°C, quenched, precipitation heat treated at 160°C for 18 hours. An alternative treatment comprised of 8 hours at 175°C also may be used. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

Temper T6511: Solution heat treated at 500°C, quenched, precipitation heat treated at 160°C for 18 hours. An alternative treatment comprised of 8 hours at 175°C also may be used. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

Temper T62: Solution heat treated at 500°C, quenched, precipitation heat treated at 160°C for 18 hours. An alternative treatment comprised of 8 hours at 175°C also may be used.

For drawn tube

Temper T4: Solution heat treated at 500°C, quenched, naturally aged.

Temper T42: Solution heat treated at 500°C, quenched, naturally aged.

Temper T6: Solution heat treated at 500°C, quenched, precipitation heat treated at 160°C for 18 hours. An alternative treatment comprised of 8 hours at 175°C also may be used.

Temper T62: Solution heat treated at 500°C, quenched, precipitation heat treated at 160°C for 18 hours. An alternative treatment comprised of 8 hours at 175°C also may be used.

For die forgings

Temper T4: Solution heat treated at 500°C, quenched in water at 60°C to 80°C, naturally aged.

Temper T6: Solution heat treated at 500°C, quenched in water at 60°C to 80°C, precipitation heat treated at 170°C for 10 hours.

For hand forgings and rolled rings

Temper T4: Solution heat treated at 500°C, quenched, naturally aged. By definition, this temper designation is that which would apply after natural aging even though mechanical properties for this alloy-temper product have not been registered.

Temper T452: Solution heat treated at 500°C, quenched, naturally aged. Stress-relieved by 1-5 percent cold reduction subsequent to solution heat treatment. By definition, this temper designation is that which would apply after natural aging even though mechanical properties for this alloy-temper product have not been registered.

Temper T6: Solution heat treated at 500°C, quenched, precipitation heat treated at 170°C for 10 hours.

Temper T652: Solution heat treated at 500°C, quenched in water at 60°C to 80°C, precipitation heat treated at 170°C for 10 hours. Stress-relieved by 1-5 percent cold reduction prior to precipitation heat treatment.

Annealing (O)

Heated at 415°C, held for 2-3 hours. This treatment is intended to remove effects of solution heat treatment and include cooling at a rate of about 30°C per hour from the annealing temperature to 260°C. The rate of subsequent cooling is unimportant. Treatment at 345°C, followed by uncontrolled cooling, may be used to remove the effects of cold work, or to partially remove the effects of heat treatment.

AA 2014 Mekanik özellikler

Sıcaklık

≤ 0°C 0 - 30°C 30 - 100°C 100 - 300°C ≥ 300°C

Özellik / Değer

Çekme Gerilimi

≥ 178.1 MPa

Tüm ayrıntıların kilidini açın

Brinell Sertliği (HB)

val1

Tüm ayrıntıların kilidini açın

Uzama, A

val1 %

Tüm ayrıntıların kilidini açın

Akma Dayanımı, Rp0.2

val1 MPa

Tüm ayrıntıların kilidini açın

Kesit Daralması

val1 %

Tüm ayrıntıların kilidini açın

Doğru seçimi yapmak için eksiksiz mekanik özelliklere mi ihtiyacınız var?

Mukavemet, sertlik, yorulma ve daha fazlası hakkında eksiksiz verilere ulaşın.

AA 2014 Uluslararası eşdeğer malzemeler

339 sonuçtan 15 tanesi gösteriliyor.

Malzeme

Standart

Ülke / Üretici

Denklik Kategorisi

Malzeme

AlCuSiMn

Standart

DIN

Ülke / Üretici

Almanya

Denklik Kategorisi

Resmi

Malzeme

3.1255

Standart

DIN

Ülke / Üretici

Almanya

Denklik Kategorisi

Resmi

Malzeme

A92014

Standart

UNS

Ülke / Üretici

Amerika Birleşik Devletleri

Denklik Kategorisi

Resmi

Malzeme

EN AW-2014

Standart

Ülke / Üretici

Avrupa Birliği

Denklik Kategorisi

Resmi

Malzeme

EN AW-2014

Standart

AFNOR NF

Ülke / Üretici

Fransa

Denklik Kategorisi

Resmi

Malzeme

EN AW-Al Cu4SiMg

Standart

AFNOR NF

Ülke / Üretici

Fransa

Denklik Kategorisi

Resmi

Malzeme

EN AW-2014

Standart

ASRO

Ülke / Üretici

Romanya

Denklik Kategorisi

Resmi

Malzeme

EN AW-Al Cu4SiMg

Standart

ASRO

Ülke / Üretici

Romanya

Denklik Kategorisi

Resmi

Malzeme

EN AW-2014

Standart

BDS

Ülke / Üretici

Bulgaristan

Denklik Kategorisi

Resmi

Malzeme

EN AW-Al Cu4SiMg

Standart

Ülke / Üretici

Avrupa Birliği

Denklik Kategorisi

Resmi

Malzeme

AlCu4SiMg

Standart

ISO

Ülke / Üretici

Uluslararası

Denklik Kategorisi

Resmi

Malzeme

Al Cu4SiMg

Standart

Ülke / Üretici

İsveç

Denklik Kategorisi

Resmi

Malzeme

EN AW-Al Cu4SiMg

Standart

BDS

Ülke / Üretici

Bulgaristan

Denklik Kategorisi

Resmi

Malzeme

2014

Standart

ISO

Ülke / Üretici

Uluslararası

Denklik Kategorisi

Resmi

Malzeme

L-3130

Standart

UNE

Ülke / Üretici

İspanya

Denklik Kategorisi

Resmi

Eşdeğerlik kategorileri, kimyasal bileşim ve mekanik özellik karşılaştırmalarını gösterir — uygulamanız için geçerli şartnameye göre uygunluğunu her zaman doğrulayın.

339 uluslararası eşdeğerin tam listesine mi ihtiyacınız var?

Standart, üretici ve eşdeğerlik kategorisine göre ayrıntılı eşleştirmeler ile tüm 339 eşdeğer kaliteleri görün.

Uygulamanız için en uygun olan malzeme seçiminizi optimize edin - Demo Rezervasyonu Yapın

Malzemeleri karşılaştırmak ve daha iyi kararlar almak mı istiyorsunuz?

Güvenilir malzeme verilerine erişin, seçenekleri karşılaştırın ve daha hızlı bir şekilde daha iyi kararlar alın.

Total Materia ile şunları yapabilirsiniz:

Gerçek mühendislik verilerine dayalı malzemeleri karşılaştırın

Standartlar arasında eşdeğer malzemeleri bulun

Belirli koşullarınız için performansı değerlendirin

Ulusal düzenlemelere uygunluğu kontrol edin

Belirli uygulamalarınız için nasıl çalıştığını görün

Rehberli Tura Katılın

339Çapraz Referanslar

23Bileşim
1250Mekanik Özellikler
249Fiziksel Özellikler
2Isıl İşlem
5Metalografi
1İşlenebilirlik

328Gerilme-Gerinim
1Şekillendirilebilirlik
173Yorulma
25Kırılma
6Sürünmek

8Bağlantılar
-Kaplamalar
-Boyutlar
-Triboloji

6Korozyon
432Yaşlanma
-Hava şartlarına dayanıklılık
6Radyasyon etkisi

197Toplam Tedarikçiler