PROPRIETARY Uddeholm Formvar 工具钢
材料组别:
黑色金属 / 工具钢
国家与地区/标准:
PROPRIETARY
数据更新
最新更新: 2020-08
更新总数: 2
更新历史
2016-04
PROPRIETARY Uddeholm Formvar 化学成分
化学元素
数值
单位
CAS 编号
Uddeholms AB, Product Data Sheets,
需要完整的材料性能数据吗？
查看完整材料数据 ›
需要注册 • 立即访问
需要注册 • 立即访问
PROPRIETARY Uddeholm Formvar 物理性能
PROPRIETARY Uddeholm Formvar 热处理
- Soft annealing: Protect the steel and heat through to 850°C (1560°F). Then cool in furnace at 10°C (20°F) per hour to 600°C (1110°F), then freely in air;
Stress relieving: After rough machining the tool should be heated through to 650°C (1200°F), holding time 2 hr. Cool slowly to 500°C (930°F), then freely in air;
Hardening: Preheating temperature: 600-900°C (1110-1650°F). Normally a minimum of two preheats, the first in the 600-650°C (1110-1200°F) range, and the second in the 820-850°C (1510-1560°F) range. When three preheats are used the second is carried out at 820°C (1510°F) and the third at 900°C (1650°F). Austenitizing temperature: 1000-1030°C (1830-1890°F);
Quenching: Recommended quenching media: High speed gas/circulating atmosphere, Vacuum (high speed gas with sufficient positive pressure). An interrupted quench at 320-450°C (610-840°F) is recommended where distortion control and quench cracking are a concern, Martempering bath, salt bath or fluidized bed at 450-550°C (840-1020°F), Martempering bath, salt bath or fluidized bed at 180-200°C (360-390°F), Warm oil, approx. 80°C (180°F). Temper the tool as soon as its temperature reaches 50-70°C (120-160°F);
Tempering: Temper minimum twice for forging and extrusion tools with intermediate cooling to room temperature. Holding time at temperature minimum 2 hr. Tempering in the range of 500-550°C (930-1020°F) for the intended final hardness will result in a lower toughness.
Gas nitriding at 510°C (950°F) for 10 h and depth of case 0.16 mm or 30 h and depth of case 0.22 mm. Plasma nitriding at 480°C (895°F) for 10 h and depth of case 0.15 mm. Nitrocarburizing in gas at 580°C (1075°F) for 2 h and depth of case 0.13 mm or in salt bath at 580°C (1075°C) for 1 h and depth of case 0.08mm - Austenitizing temperature 1025°C (1875°F). Holding time 30 minutes.
PROPRIETARY Uddeholm Formvar 机械性能
PROPRIETARY Uddeholm Formvar 的全球近似对照材料
显示 2 条结果，共计 2 条。
材料牌号
标准
国家与地区 / 生产商
近似类型
近似对照材料反映了不同材料间化学成分的相似性和力学性能的相似性——请务必根据具体应用场景的适用标准和条件具体核实材料的适用性。
根据您的应用场景优化材料选择 - 预约演示
- 2交叉引用
- 6化学成分
- 14机械性能
- 5物理性能
- 2热处理
- -金相组织
- -切削加工性能
- -应力-应变
- -成形性能
- -疲劳
- -断裂
- -爬行
- -焊接接头
- -涂层
- -尺寸
- -摩擦学
- -腐蚀
- -老化
- -耐候性
- -辐照
- 3供应商总数