PROPRIETARY CPM CRU-WEAR 工具钢
材料组别:
黑色金属 / 工具钢
国家与地区/标准:
PROPRIETARY
数据更新
最新更新: 2025-10
更新总数: 4
更新历史
2017-11
2016-03
2015-08
PROPRIETARY CPM CRU-WEAR 化学成分
化学元素
数值
单位
CAS 编号
Crucible Industries LLC., Product Data Sheets,
需要完整的材料性能数据吗？
查看完整材料数据 ›
需要注册 • 立即访问
需要注册 • 立即访问
PROPRIETARY CPM CRU-WEAR 物理性能
PROPRIETARY CPM CRU-WEAR 热处理
- Annealed: Heat to 1550-1650°F (840-900°C), hold 2 hours, slow cool 50°F (28°C) per hour to 1200°F (650°C). Stress relieved: Annealed Parts: Heat to 1100-1300°F (595-705°C), hold 2 hours, then furnace cool or cool in still air. Hardened Parts: Heat to 25°F (15°C) below the original tempering temperature, hold 2 hours, then furnace cool or cool in still air. Hardened: Preheat: Heat to 1550-1600°F (840-870°C) Equalize. Austenitize: 1850-2050°F (1010-1120°C), Hold time at temperature 20-45 minutes. Quench: Air or positive pressure quench (2 bar minimum) to below 125°F (50°C). Temper: 900-1050°F (480-565°C). For the best combination of toughness and wear resistance, austenitize at 1950°F (1065°C). Temper 3 times at 1000°F (540°C).
- 退火： 加热至 840–900°C (1550–1650°F)，保持 2 小时，以 25°C (50°F)/小时的速度缓慢冷却至 650°C (1200°F)。
消除应力 退火零件：加热至 595–705°C (1100–1300°F)，保持 2 小时，然后炉冷或在静止空气中冷却。
硬化零件：加热至比原回火温度低 15°C (25°F)，保持 2 小时，然后炉冷或在静止空气中冷却。
硬化：通常使用两个炉子：一个炉子用于预热，第二个炉子用于奥氏体化。这确保了从预热温度到奥氏体化温度的转变相当迅速。
预热：加热至 840–870°C (1550–1600°F)，均温。
奥氏体化：1010–1120°C (1850–2050°F)，在温度下保持时间 20–45 分钟。
淬火：空气或正压淬火（最少 2 bar）至 50°C (125°F) 以下。如果可行，盐浴处理将确保给定硬化处理的最大可达到韧性。
回火： 480–565°C (900–1050°F)。双重回火是必须的，建议三重回火。回火之间冷却至室温。每次回火至少 2 小时，或对于超过 50 mm 厚的截面，每 25 mm 厚度至少 1 小时。
为获得韧性和耐磨性的最佳组合，在 1065°C (1950°F) 下奥氏体化。在 540°C (1000°F) 下回火 3 次。
PROPRIETARY CPM CRU-WEAR 机械性能
PROPRIETARY CPM CRU-WEAR 的全球近似对照材料
显示 1 条结果，共计 3 条。
材料牌号
标准
国家与地区 / 生产商
近似类型
近似对照材料反映了不同材料间化学成分的相似性和力学性能的相似性——请务必根据具体应用场景的适用标准和条件具体核实材料的适用性。
根据您的应用场景优化材料选择 - 预约演示
- 3交叉引用
- 10化学成分
- 22机械性能
- 7物理性能
- 2热处理
- -金相组织
- -切削加工性能
- -应力-应变
- -成形性能
- -疲劳
- -断裂
- -爬行
- -焊接接头
- -涂层
- -尺寸
- -摩擦学
- -腐蚀
- -老化
- -耐候性
- -辐照
- 3供应商总数