PROPRIETARY BeyLos 2367 工具钢
材料组别:
黑色金属 / 工具钢
国家与地区/标准:
PROPRIETARY
数据更新
最新更新: 2014-01
更新总数: 1
更新历史
PROPRIETARY BeyLos 2367 化学成分
化学元素
数值
单位
CAS 编号
化学元素
C
数值
0.3400 – 0.4200
单位
%
CAS 编号
7440-44-0
化学元素
Cr
数值
4.8000 – 5.5000
单位
%
CAS 编号
7440-47-3
化学元素
Mn
数值
0.2000 – 0.5000
单位
%
CAS 编号
7439-96-5
Lucchini RS, Product Data Sheets,
需要完整的材料性能数据吗？
查看完整材料数据 ›
需要注册 • 立即访问
需要注册 • 立即访问
PROPRIETARY BeyLos 2367 物理性能
PROPRIETARY BeyLos 2367 热处理
- Normally supplied in the annealed condition with hardness values lower than 220 HB, if subjected to suitable hardening, it can reach a hardness of 52 HRc without affecting the toughness. Soft annealing: at 850°C, heating max 50°C/h, soaking time 120 min from when the temperature settles, cooling slow in the furnace. Stress relieving at 650°C, heating max 100°C/h, soaking time 120 min every 25 mm thickness, cooling slow in the furnace. If the suggested temperature is lower than the tempering temperature, the stress relieving temperature will be 50°C lower than the tempering temperature previously applied. Hardening: at 400°C (first pre-heating temperature), heating max 150 °C/h, soaking time 60 min every 25 mm thickness or when (Ts-Tc)<90°C; second pre-heating temperature at 600°C, heating max 150 °C/h, soaking time 45 min every 25 mm thickness or when (Ts-Tc)<90°C, third pre-heating temperature at 800°C, heating max 150 °C/h, soaking time 25 min every 25 mm thickness or when (Ts-Tc)<90°C. Austenising at 1050°C, heating > 150 °C/h, soaking time t=(x+39)/2 or 30min from when (Ts-Tc)<15°C, cooling in air, vacuum cooling, salt bath, water quench. First tempering temperature 580°C, soaking time t’=0,8x +120, cooling room temperature. Second tempering temperature set on the basis of the required mechanical properties, in any case higher than the temperature applied for the first temper, soaking time t’=0,8x +120, cooling room temperature. Third tempering temperature 30-50°C lower than the max temperature previously applied, soaking time t’=0,8x +180, cooling slow cooling in the furnace up to 250°C, then at room temperature.
PROPRIETARY BeyLos 2367 机械性能
PROPRIETARY BeyLos 2367 的全球近似对照材料
显示 5 条结果，共计 6 条。
材料牌号
标准
国家与地区 / 生产商
近似类型
近似对照材料反映了不同材料间化学成分的相似性和力学性能的相似性——请务必根据具体应用场景的适用标准和条件具体核实材料的适用性。
根据您的应用场景优化材料选择 - 预约演示
- 6交叉引用
- 6化学成分
- 10机械性能
- 11物理性能
- 1热处理
- -金相组织
- -切削加工性能
- -应力-应变
- -成形性能
- -疲劳
- -断裂
- -爬行
- -焊接接头
- -涂层
- -尺寸
- -摩擦学
- -腐蚀
- -老化
- -耐候性
- -辐照
- 4供应商总数