PROPRIETARY Uddeholm Vanadis 23 SuperClean 工具钢
材料组别:
黑色金属 / 工具钢
国家与地区/标准:
PROPRIETARY
数据更新
最新更新: 2021-01
更新总数: 4
更新历史
2017-07
2016-04
2015-06
PROPRIETARY Uddeholm Vanadis 23 SuperClean 化学成分
化学元素
数值
单位
CAS 编号
Uddeholms AB, Product Data Sheets,
需要完整的材料性能数据吗？
查看完整材料数据 ›
需要注册 • 立即访问
需要注册 • 立即访问
PROPRIETARY Uddeholm Vanadis 23 SuperClean 物理性能
PROPRIETARY Uddeholm Vanadis 23 SuperClean 热处理
- Soft annealing:
Protect the steel and heat through to 850-900°C (1560-1650°F). Then cool in the furnace at 10°C/h (20°F/h) to 700°C (1290°F), then freely in air;
Stress relieving:
After rough machining the tool should be heated through to 600-700°C (1110-1290°F), holding time 2 hr. Cool slowly to 500°C (930°F), then freely in air;
Hardening:
Preheating temperature: 450-500°C (840-930°F) and 850-900°C (1560-1650°F). Austenitizing temperature: 1050-1180°C (1920-2160°F) according to the desired final hardness;
Quenching media: Vacuum furnace with high speed gas at sufficient overpressure (2-5 bar), Martempering bath or fluidized bed at approx. 550°C (1020°F), Forced air/gas (Quenching should be continued until the temperature of the tool reaches approx. 50°C (120°F). The tool should then be tempered immediately; For applications where maximum toughness is required use a martempering bath or a furnace with sufficient overpressure.)
Tempering:
For cold work applications tempering should always be carried out at 560°C (1040°F) irrespective of the austenitizing temperature. Temper three times for one hour at full temperature. The tool should be cooled to room temperature between the tempers. The retained austenite content will be less than 1% after this tempering cycle.
Sub-zero treatment: For materials that require maximum dimensional stability, immediately after quenching the piece should be sub-zero treated -70 to -80°C (-95 to -110°F), soaking for 1-3 h and followed by tempering. - Austenitizing temperature 1080°C (1980°F). Holding time 30 minutes.
PROPRIETARY Uddeholm Vanadis 23 SuperClean 机械性能
PROPRIETARY Uddeholm Vanadis 23 SuperClean 国际等效材料
显示 15 / 68 条结果。
材料牌号
标准
国家与地区 / 生产商
近似类型
等效类别反映化学成分和机械性能的比较 — 请始终根据适用于您应用的相关规范验证适用性。
根据您的应用场景优化材料选择 - 预约演示
- 68交叉引用
- 5化学成分
- 7机械性能
- 21物理性能
- 2热处理
- -金相组织
- -切削加工性能
- -应力-应变
- -成形性能
- -疲劳
- -断裂
- -爬行
- -焊接接头
- -涂层
- -尺寸
- -摩擦学
- -腐蚀
- -老化
- -耐候性
- -辐照
- 50供应商总数