AA 7075 Alüminyum alaşım

Malzeme grubu: Demirdışı Alaşımlar / Alüminyum alaşım

Ülke/Standart: Amerika Birleşik Devletleri / AA

Belirleyici fiyat:

Veri güncellemeleri

Son Güncelleme: 2025-09

Toplam güncelleme sayısı: 22

Güncelleme Geçmişi

2025-08 2025-05 2024-10 2024-04 2024-03 2024-02 2024-01 2023-12 2023-03 2022-08 2020-10 2020-09 2020-08 2020-07 2019-06 2019-05 2016-11 2016-02 2015-03 2015-01 2014-06

Bu malzemenin 2931 özelliği vardır - burada yalnızca bir alt kümesi gösterilmektedir.

Sıcaklıklar ve koşullar genelinde ayrıntılı değerler de dahil olmak üzere tam malzeme özelliklerinin kilidini açın.

AA 7075 Kimyasal bileşim

Kriterler

Değer

Birim

CAS numarası

Kriterler

Değer

Remainder

Birim

CAS numarası

7429-90-5

Kriterler

Değer

0.18 – 0.28

Birim

CAS numarası

7440-47-3

Kriterler

Değer

1.2 – 2.0

Birim

CAS numarası

7440-50-8

Kriterler

Değer

val1

Birim

CAS numarası

7439-89-6

Kriterler

Değer

val1

Birim

CAS numarası

7439-95-4

Kriterler

Değer

val1

Birim

CAS numarası

7439-96-5

Kriterler

Other each

Değer

val1

Birim

CAS numarası

Kriterler

Other total

Değer

val1

Birim

CAS numarası

Kriterler

Değer

val1

Birim

CAS numarası

7440-21-3

Kriterler

Değer

val1

Birim

CAS numarası

7440-32-6

Kriterler

Ti+Zr

Değer

val1

Birim

CAS numarası

Kriterler

Değer

val1

Birim

CAS numarası

7440-66-6

International alloy designations and chemical composition limits for wrought aluminum and wrought aluminum alloys - Teal Sheets (2025), 2025

Tam malzeme performans verilerini mi arıyorsunuz?

AA 7075 Fiziksel özellikler

Sıcaklık

≤ 0°C 0 - 30°C 30 - 100°C 100 - 300°C ≥ 300°C

Özellik / Değer

Elastisite Modülü

69 — 79 GPa

Tüm ayrıntıların kilidini açın

Yoğunluk

val1 kg/dm³

Tüm ayrıntıların kilidini açın

Isı Kapasitesi

val1 J/(kg∙°C)

Tüm ayrıntıların kilidini açın

Isıl İletkenlik

val1 W/(m∙°C)

Tüm ayrıntıların kilidini açın

Elektriksel Direnç

val1 Ω∙mm²/m

Tüm ayrıntıların kilidini açın

Elektriksel İletkenlik

val1 S/m

Tüm ayrıntıların kilidini açın

Ergime Sıcaklığı

val1 °C

Tüm ayrıntıların kilidini açın

Poisson Katsayısı

val1

Tüm ayrıntıların kilidini açın

Kesme Katsayısı

val1 GPa

Tüm ayrıntıların kilidini açın

Isıl Genleşme Katsayısı (CTE)

val1 10^-6/°C

Tüm ayrıntıların kilidini açın

Bu malzemenin 2931 özelliği vardır - burada yalnızca bir alt kümesi gösterilmektedir.

Sıcaklık ve koşullar genelinde ayrıntılı fiziksel özellik değerlerinin kilidini açın.

AA 7075 Isıl İşlem

The times and temperatures are typical for various forms, sizes and methods of manufacture and may not exactly describe the optimum treatment for a specific item.

The nominal temperatures at which metal is heated (applies both for solution and precipitation heat treatment) should be attained as rapidly as possible and maintained ± 5°C of nominal during the time at temperature.

The time at precipitation heat treatment temperature will depend on time required for load to reach temperature. The times shown are based on rapid heating, with soaking time measured from the time the load reached within 5°C of the applicable temperature.

Material should be quenched from the solution heat-treating temperature as rapidly as possible and with minimum delay after removal from the furnace. Quenching is typically performed by immersion of wrought products in a cold water bath, although some forgings are quenched in hot-water. Quenching may be performed by alternative means such as total immersion in an aqueous polymer solution, liquefied gas, hot water, or boiling water, or by air blast or fog to minimize distortion provided samples from the material. The use of high-velocity high-volume jets of cold water is also effective for some materials.

The aging of aluminum alloy 7075 from any temper to the T73 or T76 temper series requires closer than normal controls on aging practice variables such as time, temperature, heating-up rates, etc., for any given item. In addition to the above, when re-aging material in the T6 temper series to the T73 or T76 temper series, the specific condition of the T6 temper material (such as its property level and other effect of processing variables) is extremely important and will affect the capability of the re-aged material to conform to the requirements specified for the applicable T73 or T76 temper series.

For sheet

With optimum ingot homogenization, heat treating temperatures as high as 500°C are sometimes acceptable.

Temper W: Solution heat treated at 480°C, quenched, naturally aged. With optimum ingot homogenization, heat treating temperatures as high as 500°C are sometimes acceptable.

Temper T6: Solution heat treated at 480°C, quenched, precipitation heat treated at 120°C for 24 hours. An alternate two-stage treatment comprised of 4 hours at 95°C followed by 8 hours at 155°C also may be used.

Temper T73: Solution heat treated at 480°C, quenched, a two-stage treatment comprised of 6 to 8 hours at 105°C followed by a second-stage of 24-30 hours at 165°C. An alternate two-stage treatment comprised of 6-8 hours at 107°C followed by a second state of 14-18 hours at 168°C may be used providing a heating up of 14°C per hour is used.

Temper T76: Solution heat treated at 480°C, quenched, a two-stage treatment comprised of 3-30 hours at 121°C followed by 15-18 hours at 163°C. An alternate two-stage treatment of 8 hours at 99°C followed by 24-28 hours at 163°C may be used.

Temper T62: Solution heat treated at 480°C, quenched, precipitation heat treated ta 120°C for 24 hours. An alternate two-stage treatment comprised of 4 hours at 95°C followed by 8 hours at 155°C also may be used.

For plate

With optimum ingot homogenization, heat treating temperatures as high as 500°C are sometimes acceptable. For plate thickness over 4 inches and for rod diameters or bar thicknesses over four inches, a maximum temperature of 490°C is recommended to avoid eutectic melting.

Temper W51: Solution heat treated at 480°C, quenched, naturally aged. Stress-relieved by stretching is required to produce a specified amount of permanent set subsequent to solution heat treatment.

Temper W: Solution heat treated at 480°C, quenched, naturally aged.

Temper T651: Solution heat treated at 480°C, quenched, precipitation heat treated at 120°C for 24 hours. An alternate two-stage treatment comprised of 4 hours at 95°C followed by 8 hours at 155°C also may be used. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

Temper T7351: Solution heat treated at 480°C, quenched, a two-stage treatment comprised of 6 to 8 hours at 105°C followed by a second-stage of 24-30 hours at 165°C. An alternate two-stage treatment comprised of 6-8 hours at 107°C followed by a second state of 14-18 hours at 168°C may be used providing a heating up of 14°C per hour is used. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

Temper T7651: Solution heat treated at 480°C, quenched, a two-stage treatment comprised of 3-30 hours at 121°C followed by 15-18 hours at 163°C. An alternate two-stage treatment of 8 hours at 99°C followed by 24-28 hours at 163°C may be used. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

Temper T62: Solution heat treated at 480°C, quenched, precipitation heat treated at 120°C for 24 hours. An alternate two-stage treatment comprised of 4 hours at 95°C followed by 8 hours at 155°C also may be used.

For rolled or cold finished wire, rod and bar

With optimum ingot homogenization, heat treating temperatures as high as 500°C are sometimes acceptable. For plate thickness over 4 inches and for rod diameters or bar thicknesses over four inches, a maximum temperature of 490°C is recommended to avoid eutectic melting.

Temper W: Solution heat treated at 490°C, quenched, naturally aged. Stress-relieved by stretching is required to produce a specified amount of permanent set subsequent to solution heat treatment.

Temper W51: Solution heat treated at 490°C, quenched, naturally aged. Stress-relieved by stretching is required to produce a specified amount of permanent set subsequent to solution heat treatment.

Temper T6: Solution heat treated at 490°C, quenched, precipitation heat treated at 120°C for 24 hours.

Temper T73: Solution heat treated at 490°C, quenched, a two-stage treatment comprised of 6 to 8 hours at 105°C followed by a second-stage of 8-10 hours at 175°C. An alternate two-stage treatment comprised of 6-8 hours at 107°C followed by a second state of 14-18 hours at 168°C may be used providing a heating up of 14°C per hour is used.

Temper T62: Solution heat treated at 490°C, quenched, precipitation heat treated at 120°C for 24 hours.

Temper T651: Solution heat treated at 490°C, quenched, precipitation heat treated at 120°C for 24 hours. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

Temper T7351: Solution heat treated at 490°C, quenched, a two-stage treatment comprised of 6 to 8 hours at 105°C followed by a second-stage of 8-10 hours at 175°C. An alternate two-stage treatment comprised of 6-8 hours at 107°C followed by a second state of 14-18 hours at 168°C may be used providing a heating up of 14°C per hour is used. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

For extruded rod, bar and profiles

Temper W: Solution heat treated at 465°C, quenched, naturally aged.

Temper W510: Solution heat treated at 465°C, quenched, naturally aged. Stress-relieved by stretching is required to produce a specified amount of permanent set subsequent to solution heat treatment.

Temper W511: Solution heat treated at 465°C, quenched, naturally aged. Stress-relieved by stretching is required to produce a specified amount of permanent set subsequent to solution heat treatment.

Temper T6: Solution heat treated at 465°C, quenched, precipitation heat treated at 120°C for 24 hours. An alternate three-stage treatment comprised of 5 hours at 100°C followed by 4 hours at 120°C followed by 4 hours at 150°C also may be used.

Temper T73: Solution heat treated at 465°C, quenched, a two-stage treatment comprised of 6 to 8 hours at 105°C followed by a second-stage of 6-8 hours at 175°C. An alternate two-stage treatment comprised of 6-8 hours at 107°C followed by a second state of 14-18 hours at 168°C may be used providing a heating up of 14°C per hour is used.

Temper T76: Solution heat treated at 465°C, quenched, a two-stage treatment comprised of 3-30 hours at 121°C followed by 15-18 hours at 163°C. An alternate two-stage treatment of 8 hours at 99°C followed by 24-28 hours at 163°C may be used.

Temper T62: Solution heat treated at 465°C, quenched, precipitation heat treated at 120°C for 24 hours. An alternate three-stage treatment comprised of 5 hours at 100°C followed by 4 hours at 120°C followed by 4 hours at 150°C also may be used.

Temper T6510: Solution heat treated at 465°C, quenched, precipitation heat treated at 120°C for 24 hours. An alternate three-stage treatment comprised of 5 hours at 100°C followed by 4 hours at 120°C followed by 4 hours at 150°C also may be used. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

Temper T73510: Solution heat treated at 465°C, quenched, a two-stage treatment comprised of 6 to 8 hours at 105°C followed by a second-stage of 6-8 hours at 175°C. An alternate two-stage treatment comprised of 6-8 hours at 107°C followed by a second state of 14-18 hours at 168°C may be used providing a heating up of 14°C per hour is used. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

Temper T76510: Solution heat treated at 465°C, quenched, a two-stage treatment comprised of 3-30 hours at 121°C followed by 15-18 hours at 163°C. An alternate two-stage treatment of 8 hours at 99°C followed by 24-28 hours at 163°C may be used. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

Temper T6511: Solution heat treated at 465°C, quenched, precipitation heat treated at 120°C for 24 hours. An alternate three-stage treatment comprised of 5 hours at 100°C followed by 4 hours at 120°C followed by 4 hours at 150°C also may be used. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

Temper T73511: Solution heat treated at 465°C, quenched, a two-stage treatment comprised of 6 to 8 hours at 105°C followed by a second-stage of 6-8 hours at 175°C. An alternate two-stage treatment comprised of 6-8 hours at 107°C followed by a second state of 14-18 hours at 168°C may be used providing a heating up of 14°C per hour is used. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

Temper T76511: Solution heat treated at 465°C, quenched, a two-stage treatment comprised of 3-30 hours at 121°C followed by 15-18 hours at 163°C. An alternate two-stage treatment of 8 hours at 99°C followed by 24-28 hours at 163°C may be used. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

For extruded tube

Temper W: Solution heat treated at 465°C, quenched, naturally aged.

Temper W510: Solution heat treated at 465°C, quenched, naturally aged. Stress-relieved by stretching is required to produce a specified amount of permanent set subsequent to solution heat treatment.

Temper W511: Solution heat treated at 465°C, quenched, naturally aged. Stress-relieved by stretching is required to produce a specified amount of permanent set subsequent to solution heat treatment.

Temper T6: Solution heat treated at 465°C, quenched, precipitation heat treated at 120°C for 24 hours. An alternate three-stage treatment comprised of 5 hours at 100°C followed by 4 hours at 120°C followed by 4 hours at 150°C also may be used.

Temper T73: Solution heat treated at 465°C, quenched, a two-stage treatment comprised of 6 to 8 hours at 105°C followed by a second-stage of 6-8 hours at 175°C. An alternate two-stage treatment comprised of 6-8 hours at 107°C followed by a second state of 14-18 hours at 168°C may be used providing a heating up of 14°C per hour is used.

Temper T62: Solution heat treated at 465°C, quenched, precipitation heat treated at 120°C for 24 hours. An alternate three-stage treatment comprised of 5 hours at 100°C followed by 4 hours at 120°C followed by 4 hours at 150°C also may be used.

Temper T6510: Solution heat treated at 465°C, quenched, precipitation heat treated at 120°C for 24 hours. An alternate three-stage treatment comprised of 5 hours at 100°C followed by 4 hours at 120°C followed by 4 hours at 150°C also may be used. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

Temper T73510: Solution heat treated at 465°C, quenched, a two-stage treatment comprised of 6 to 8 hours at 105°C followed by a second-stage of 6-8 hours at 175°C. An alternate two-stage treatment comprised of 6-8 hours at 107°C followed by a second state of 14-18 hours at 168°C may be used providing a heating up of 14°C per hour is used. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

Temper T6511: Solution heat treated at 465°C, quenched, precipitation heat treated at 120°C for 24 hours. An alternate three-stage treatment comprised of 5 hours at 100°C followed by 4 hours at 120°C followed by 4 hours at 150°C also may be used. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

Temper T73511: Solution heat treated at 465°C, quenched, a two-stage treatment comprised of 6 to 8 hours at 105°C followed by a second-stage of 6-8 hours at 175°C. An alternate two-stage treatment comprised of 6-8 hours at 107°C followed by a second state of 14-18 hours at 168°C may be used providing a heating up of 14°C per hour is used. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.

For drawn tube

Temper W: Solution heat treated at 465°C, quenched, naturally aged.

Temper T6: Solution heat treated at 465°C, quenched, precipitation heat treated at 120°C for 24 hours.

Temper T73: Solution heat treated at 465°C, quenched, a two-stage treatment comprised of 6 to 8 hours at 105°C followed by a second-stage of 6-8 hours at 175°C. An alternate two-stage treatment comprised of 6-8 hours at 107°C followed by a second state of 14-18 hours at 168°C may be used providing a heating up of 14°C per hour is used.

Temper T62: Solution heat treated at 465°C, quenched, precipitation heat treated at 120°C for 24 hours.

For die forgings

Temper W: Solution heat treated at 470°C, quenched in water at 60°C to 80°C, naturally aged.

Temper W52: Solution heat treated at 470°C, quenched in water at 60°C to 80°C, naturally aged. Stress-relieved by 1-5 percent cold reduction subsequent to solution heat treatment.

Temper T6: Solution heat treated at 470°C, quenched in water at 60°C to 80°C, precipitation heat treated at 120°C for 24 hours.

Temper T73: Solution heat treated at 470°C, quenched in water at 60°C to 80°C, a two-stage treatment comprised of 6 to 8 hours at 105°C followed by a second-stage of 8-10 hours at 175°C.

Temper T7352: Solution heat treated at 470°C, quenched in water at 60°C to 80°C, a two-stage treatment comprised of 6 to 8 hours at 105°C followed by a second-stage of 6-8 hours at 175°C. Stress-relieved by 1-5 percent cold reduction prior to precipitation heat treatment.

For hand forgings

Temper W: Solution heat treated at 470°C, quenched in water at 60°C to 80°C, naturally aged.

Temper W52: Solution heat treated at 470°C, quenched in water at 60°C to 80°C, naturally aged. Stress-relieved by 1-5 percent cold reduction subsequent to solution heat treatment.

Temper T6: Solution heat treated at 470°C, quenched in water at 60°C to 80°C, precipitation heat treated at 120°C for 24 hours.

Temper T73: Solution heat treated at 470°C, quenched in water at 60°C to 80°C, a two-stage treatment comprised of 6 to 8 hours at 105°C followed by a second-stage of 8-10 hours at 175°C.

Temper T652: Solution heat treated at 470°C, quenched in water at 60°C to 80°C, precipitation heat treated at 120°C for 24 hours. Stress-relieved by 1-5 percent cold reduction prior to precipitation heat treatment.

Temper T7352: Solution heat treated at 470°C, quenched in water at 60°C to 80°C, a two-stage treatment comprised of 6 to 8 hours at 105°C followed by a second-stage of 6-8 hours at 175°C. Stress-relieved by 1-5 percent cold reduction prior to precipitation heat treatment.

For rolled rings

Temper W: Solution heat treated at 470°C, quenched, naturally aged.

Temper T6: Solution heat treated at 470°C, quenched, precipitation heat treated at 120°C for 24 hours.

Annealing (O)

Heated at 415°C, held for 2-3 hours. This treatment is intended to remove the effects of solution heat treatment and includes cooling at an uncontrolled rate to 205°C or less, followed by reheating to 230°C for 4 hours. Treatment at 345°C, followed by uncontrolled cooling, may be used to remove the effects of cold work, or to partially remove the effects of heat treatment.

AA 7075 Mekanik özellikler

Sıcaklık

≤ 0°C 0 - 30°C 30 - 100°C 100 - 300°C ≥ 300°C

Özellik / Değer

Çekme Gerilimi

≥ 230 MPa

Tüm ayrıntıların kilidini açın

Brinell Sertliği (HB)

val1

Tüm ayrıntıların kilidini açın

Uzama, A

val1 %

Tüm ayrıntıların kilidini açın

Akma Dayanımı, Rp0.2

val1 MPa

Tüm ayrıntıların kilidini açın

Darbe Enerjisi

val1 J

Tüm ayrıntıların kilidini açın

Kesit Daralması

val1 %

Tüm ayrıntıların kilidini açın

Vickers Sertliği (HV)

val1

Tüm ayrıntıların kilidini açın

Doğru seçimi yapmak için eksiksiz mekanik özelliklere mi ihtiyacınız var?

Mukavemet, sertlik, yorulma ve daha fazlası hakkında eksiksiz verilere ulaşın.

AA 7075 Uluslararası eşdeğer malzemeler

296 sonuçtan 15 tanesi gösteriliyor.

Malzeme

Standart

Ülke / Üretici

Denklik Kategorisi

Malzeme

AlZnMgCu1,5

Standart

DIN

Ülke / Üretici

Almanya

Denklik Kategorisi

Resmi

Malzeme

3.4365

Standart

DIN

Ülke / Üretici

Almanya

Denklik Kategorisi

Resmi

Malzeme

A97075

Standart

UNS

Ülke / Üretici

Amerika Birleşik Devletleri

Denklik Kategorisi

Resmi

Malzeme

EN AW-7075

Standart

Ülke / Üretici

Avrupa Birliği

Denklik Kategorisi

Resmi

Malzeme

EN AW-7075

Standart

CSN

Ülke / Üretici

Çek Cumhuriyeti

Denklik Kategorisi

Resmi

Malzeme

EN AW-AlZn5,5MgCu

Standart

CSN

Ülke / Üretici

Çek Cumhuriyeti

Denklik Kategorisi

Resmi

Malzeme

EN AW-7075

Standart

DIN

Ülke / Üretici

Almanya

Denklik Kategorisi

Resmi

Malzeme

EN AW-AlZn5,5MgCu

Standart

DIN

Ülke / Üretici

Almanya

Denklik Kategorisi

Resmi

Malzeme

EN AW-AlZn5,5MgCu

Standart

Ülke / Üretici

Avrupa Birliği

Denklik Kategorisi

Resmi

Malzeme

1950

Standart

GOST

Ülke / Üretici

Rusya

Denklik Kategorisi

Resmi

Malzeme

V95

Standart

GOST

Ülke / Üretici

Rusya

Denklik Kategorisi

Resmi

Malzeme

AlZn5.5MgCu

Standart

ISO

Ülke / Üretici

Uluslararası

Denklik Kategorisi

Resmi

Malzeme

7075

Standart

ISO

Ülke / Üretici

Uluslararası

Denklik Kategorisi

Resmi

Malzeme

EN AW-7075

Standart

MSZ

Ülke / Üretici

Macaristan

Denklik Kategorisi

Resmi

Malzeme

EN AW-AlZn5,5MgCu

Standart

MSZ

Ülke / Üretici

Macaristan

Denklik Kategorisi

Resmi

Eşdeğerlik kategorileri, kimyasal bileşim ve mekanik özellik karşılaştırmalarını gösterir — uygulamanız için geçerli şartnameye göre uygunluğunu her zaman doğrulayın.

296 uluslararası eşdeğerin tam listesine mi ihtiyacınız var?

Standart, üretici ve eşdeğerlik kategorisine göre ayrıntılı eşleştirmeler ile tüm 296 eşdeğer kaliteleri görün.

Uygulamanız için en uygun olan malzeme seçiminizi optimize edin - Demo Rezervasyonu Yapın

Malzemeleri karşılaştırmak ve daha iyi kararlar almak mı istiyorsunuz?

Güvenilir malzeme verilerine erişin, seçenekleri karşılaştırın ve daha hızlı bir şekilde daha iyi kararlar alın.

Total Materia ile şunları yapabilirsiniz:

Gerçek mühendislik verilerine dayalı malzemeleri karşılaştırın

Standartlar arasında eşdeğer malzemeleri bulun

Belirli koşullarınız için performansı değerlendirin

Ulusal düzenlemelere uygunluğu kontrol edin

Belirli uygulamalarınız için nasıl çalıştığını görün

Rehberli Tura Katılın

296Çapraz Referanslar

23Bileşim
1079Mekanik Özellikler
225Fiziksel Özellikler
8Isıl İşlem
35Metalografi
1İşlenebilirlik

349Gerilme-Gerinim
21Şekillendirilebilirlik
262Yorulma
64Kırılma
7Sürünmek

4Bağlantılar
-Kaplamalar
-Boyutlar
1Triboloji

14Korozyon
406Yaşlanma
-Hava şartlarına dayanıklılık
2Radyasyon etkisi

134Toplam Tedarikçiler