UNI 16MnCr5 Structural and constructional steels
Data updates
This material has 804 properties — only a subset is shown here.
Unlock full material properties, including detailed values across temperatures and conditions.
Free registration required • Instant access
UNI 16MnCr5 Chemical Composition
UNI 7846: 1978 / Finished products in hot rolled unalloyed or special hardening alloyed steel bars and rolls. Quality, requirements and tests
Looking for full material performance data?
Free registration required • Instant access
UNI 16MnCr5 Physical Properties
Temperature
This material has 804 properties — only a subset is shown here.
Unlock detailed physical values across temperatures and conditions.
Free registration required • Instant access
UNI 16MnCr5 Heat Treatments
- End quench test austenitizing at 900 ± 5°C (Time for austenitizing as a guide: 30 min minimum);
Carburizing at 880-980°C (The carburizing temperature depends on the chemical composition of the steel, the mass of the product and the carburizing medium. If the steels are direct hardened, in general, a temperature of 950°C is not exceeded. For special procedures, for example under vacuum, higher temperatures (for example 1020-1050°C) are not unusual);
Direct and simple hardening at 820-860°C (The kind of quenching agent depends on, for example the shape of the products, the cooling conditions and the amount of furnace filling. If the steels are direct hardened and if there is a danger of distortion, they should be quenched from a temperature between the core-hardening and case-hardening temperatures);
Double hardening: Core-hardening at 860-900°C and Case-hardening at 780-820°C;
Tempering at 150-200°C (Time for tempering as a guide: 1h minimum). - End quench test: Quench from 880°C. Carburizing: 880 to 980°C; NOTE: If steels are direct hardened, in general, a carburizing temperature of 950°C is not exceeded. For special procedures, for example under vacuum, higher temperatures (for example 1020 to 1050°C) are not unusual. Core hardening: 840 to 880°C; Case hardening: 780°C to 820°C; Tempering: 150 to 200°C (as a guide, for 1 hour minimum).
UNI 16MnCr5 Mechanical Properties
Temperature
Need complete mechanical properties to make the right choice?
Get complete data on strength, hardness, fatigue, and more.
Free registration required • Instant access
UNI 16MnCr5 International Equivalent Materials
Showing 15 of 269 results.
Equivalence categories reflect chemical-composition and mechanical-property comparison — always verify suitability against the governing specification for your application.
Need the full list of 269 international equivalents?
See all 269 equivalent grades with detailed mapping by standard, producer and equivalence category.
Free registration required • Instant access
Optimize material selection for your application - Book A Demo
- 269Cross References
- 76Composition
- 120Mechanical Properties
- 3Physical Properties
- 21Heat Treatment
- 3Metallography
- -Machinability
- 37Stress-Strain
- 37Formability
- 5Fatigue
- -Fracture
- -Creep
- 9Joints
- -Coatings
- 8Dimensions
- -Tribology
- -Corrosion
- -Ageing
- -Weatherability
- -Irradiation
- 216Total Suppliers