PROPRIETARY VP50IM 结构钢
材料组别:
黑色金属 / 结构钢
国家与地区/标准:
PROPRIETARY
数据更新
最新更新: 2022-01
更新总数: 1
更新历史
PROPRIETARY VP50IM 化学成分
化学元素
数值
单位
CAS 编号
化学元素
Al
数值
1.00
单位
%
CAS 编号
7429-90-5
化学元素
C
数值
0.15
单位
%
CAS 编号
7440-44-0
化学元素
Cu
数值
1.00
单位
%
CAS 编号
7440-50-8
Villares Metals, Product Data Sheets,
需要完整的材料性能数据吗？
查看完整材料数据 ›
需要注册 • 立即访问
需要注册 • 立即访问
PROPRIETARY VP50IM 物理性能
PROPRIETARY VP50IM 热处理
- Solubilization: Heat slowly and evenly to 400°C at a rate of 100°C/h. Then, at a maximum of 300°C/h, heat up to a solubilization temperature between 880/920°C, keep until completely homogenized and then cool in forced air. Cooling can also be carried out in oil suitable for quenching, stirred and heated at 40/70°C, until the part reaches a temperature of 100°C, then cooling in calm air to room temperature.
Stress Relief: Stress relief is not performed as applied to traditional steels; it occurs during the aging stage.
Aging: The heating cycle should be in steps every 100°C, with a soak time of 30 minutes for every 25mm of the thinnest thickness, to prevent machining stresses from causing distortions. T he aging temperature is 500°C. Time at temperature should be 6 hours. After aging, the piece must be cooled in calm air. If the part has been solubilized again, carry out aging only after reaching room temperature.
Nitriding: Nitride between 480 and 510°C, varying according to the process used, obtaining hardness of 600-650 HV in the nitrided layer. As they have coincident temperatures, it is not necessary to carry out the aging treatment when the matrix is nitrided, as long as the nitriding time is sufficient for aging.
PROPRIETARY VP50IM 机械性能
根据您的应用场景优化材料选择 - 预约演示
- -交叉引用
- 8化学成分
- 2机械性能
- 3物理性能
- 1热处理
- -金相组织
- -切削加工性能
- -应力-应变
- -成形性能
- -疲劳
- -断裂
- -爬行
- -焊接接头
- -涂层
- -尺寸
- -摩擦学
- -腐蚀
- -老化
- -耐候性
- -辐照
- 1供应商总数