PROPRIETARY VP20ISOF 工具钢
材料组别:
黑色金属 / 工具钢
国家与地区/标准:
PROPRIETARY
数据更新
最新更新: 2022-01
更新总数: 1
更新历史
PROPRIETARY VP20ISOF 化学成分
化学元素
数值
单位
CAS 编号
化学元素
C
数值
0.36
单位
%
CAS 编号
7440-44-0
化学元素
Cr
数值
1.80
单位
%
CAS 编号
7440-47-3
化学元素
Mn
数值
1.60
单位
%
CAS 编号
7439-96-5
Villares Metals, Product Data Sheets,
需要完整的材料性能数据吗？
查看完整材料数据 ›
需要注册 • 立即访问
需要注册 • 立即访问
PROPRIETARY VP20ISOF 物理性能
PROPRIETARY VP20ISOF 热处理
- Annealing: Heat slowly and evenly to temperatures between 760 and 800°C, at a rate of 100ºC/h, keeping 1 hour for every 25 mm of the largest section of the piece. Slowly cool in an oven (30°C/h) to 600°C; then cool in calm air.
Stress Relief: Heating the molds slowly and evenly (100°C/h) up to 530°C, keeping 0.5 hour in temperature for each 25 mm of the largest section in the ask; regardless of the section, the time must not be less than 2 hours. After relief, cool in calm air.
Quenching: During quenching, the surface of the molds must be protected against decarburization and oxidation. Heat slowly and evenly at (100°C/h) up to 400°C and then at a maximum of 300°C/h until the austenitizing temperature, between 840 and 860°C. Keep at temperature until complete homogenization of the entire piece. Cooling must be carried out in oil suitable for quenching, stirred and heated between 40 and 70°C, until the mold temperature reaches 100°C. Then cool in calm air between 50 and 70°C.
Tempering: The tools must be tempered immediately after tempering, as soon as they reach 60°C. Make at least 2 tempers and between each temper the parts must cool slowly to room temperature. Tempering temperatures should be chosen as per desired hardness. The time of each tempering must be at least 2 hours. For pieces larger than 70 mm, the time must be calculated as a function of their dimension. Allow 1 hour for each mm of thickness.
Nitriding: Recommended when high levels of surface hardness and abrasion resistance are required. It must be carried out after quenching and tempering, as long as the nitriding temperature is at least 50°C lower than the temperature of the last tempering.
PROPRIETARY VP20ISOF 机械性能
根据您的应用场景优化材料选择 - 预约演示
- 1交叉引用
- 4化学成分
- 1机械性能
- 3物理性能
- 2热处理
- -金相组织
- -切削加工性能
- -应力-应变
- -成形性能
- -疲劳
- -断裂
- -爬行
- -焊接接头
- -涂层
- -尺寸
- -摩擦学
- -腐蚀
- -老化
- -耐候性
- -辐照
- 1供应商总数