PROPRIETARY Uddeholm Vanadis 10 SuperClean 工具钢
材料组别:
黑色金属 / 工具钢
国家与地区/标准:
PROPRIETARY
数据更新
最新更新: 2016-04
更新总数: 1
更新历史
PROPRIETARY Uddeholm Vanadis 10 SuperClean 化学成分
化学元素
数值
单位
CAS 编号
Uddeholms AB, Product Data Sheets,
需要完整的材料性能数据吗？
查看完整材料数据 ›
需要注册 • 立即访问
需要注册 • 立即访问
PROPRIETARY Uddeholm Vanadis 10 SuperClean 物理性能
PROPRIETARY Uddeholm Vanadis 10 SuperClean 热处理
- Soft annealing: Protect the steel and heat through to 900°C. Cool in the furnace at 10°C per hour to 750°C, then freely in air.
Stress relieving: After rough machining the tool should be heated through to 650°C, holding time 2 hr. Cool slowly to 500°C, then freely in air;
Hardening: Pre-heating temperature: 600-700°C, Austenitizing temperature: 1020-1100°C. Holding time: 30 minutes. (A holding time of less than 30 minutes will result in loss of hardness. The tool should be protected against decarburization and oxidation during hardening.);
Quenching media: Forced air/gas, Vacuum furnace (gas overpressure 2-5 bar), Martempering bath or fluidized bed at 500-550°C, Martempering bath or fluidized bed at 200-350°C whereby 350°C is preferred. (Temper the tool as soon as its temperature reaches 50-70°C; In order to obtain the optimum properties for the tool, the cooling rate should be as fast as is concomitant with acceptable distortion; Tools with sections > 50 mm should be quenched in forced air.
Quenching in still air will result in loss of hardness.);
Tempering: Choose the tempering temperature according to the hardness. Temper twice with intermediate cooling to room temperature. Lowest tempering temperature 180°C. Holding time at temperature minimum 2 hr. At a hardening temperature of 1100°C or higher it should be tempered at minimum 525°C in order to reduce the amount of retained austenite.
PROPRIETARY Uddeholm Vanadis 10 SuperClean 机械性能
根据您的应用场景优化材料选择 - 预约演示
- -交叉引用
- 6化学成分
- 1机械性能
- 12物理性能
- 3热处理
- -金相组织
- -切削加工性能
- -应力-应变
- -成形性能
- -疲劳
- -断裂
- -爬行
- -焊接接头
- -涂层
- -尺寸
- -摩擦学
- -腐蚀
- -老化
- -耐候性
- -辐照
- 5供应商总数