PROPRIETARY Uddeholm Vanadis 60 SuperClean 工具钢
材料组别:
黑色金属 / 工具钢
国家与地区/标准:
PROPRIETARY
数据更新
最新更新: 2021-01
更新总数: 2
更新历史
2016-04
PROPRIETARY Uddeholm Vanadis 60 SuperClean 化学成分
化学元素
数值
单位
CAS 编号
Uddeholms AB, Product Data Sheets,
需要完整的材料性能数据吗？
查看完整材料数据 ›
需要注册 • 立即访问
需要注册 • 立即访问
PROPRIETARY Uddeholm Vanadis 60 SuperClean 物理性能
PROPRIETARY Uddeholm Vanadis 60 SuperClean 热处理
- Soft annealing:
Protect the steel and heat through to 850-900°C (1560-1650°F). Then cool in the furnace at 10°C/h (20°F/h) to 700°C (1290°F), then freely in air;
Stress relieving:
After rough machining the tool should be heated through to 600-700°C (1110-1290°F), holding time 2 hr. Cool slowly to 500°C (930°F), then freely in air;
Tempering:
Pre-heating temperature: 450-500°C (840-930°F) and 850-900°C (1560-1650°F).
Austenitizing temperature: 1100-1180°C (2010-2160°F), according to the desired final hardness. (The tool should be protected against decarburization and oxidation during hardening.
Quenching media:
Martempering bath at approx. 540°C (1000°F), Vacuum furnace with high speed gas at sufficient overpressure (Quenching should be continued until the temperature of the tool reaches approx. 25°C (77°F). The tool should then be tempered immediately; In order to obtain a high toughness, the cooling speed in the core should be at least 10°C/sec (20°F/sec). This is valid for cooling from the austenitizing temperature down to approx. 540°C (1000°F). After temperature equalization between the surface and core, the cooling rate of approx. 5°C/sec (10°F/sec) can be used.);
Tempering:
For cold work applications tempering should always be carried out at 560°C (1040°F) irrespective of the austenitizing temperature. Temper three times for one hour at full temperature. The tool should be cooled to room temperature between the tempers. The retained austenite content will be less than 1% after this tempering cycle.
Sub-zero treatment:
It should be treated immediately after quenching between -150 and -196°C (-238 and -321°F), although occasionally -70 to -80°C (-95 to -110°F) are used. - Austenitizing temperature 1150°C (1920°F). Holding time 10 minutes.
PROPRIETARY Uddeholm Vanadis 60 SuperClean 机械性能
PROPRIETARY Uddeholm Vanadis 60 SuperClean 的全球近似对照材料
显示 6 条结果，共计 7 条。
材料牌号
标准
国家与地区 / 生产商
近似类型
近似对照材料反映了不同材料间化学成分的相似性和力学性能的相似性——请务必根据具体应用场景的适用标准和条件具体核实材料的适用性。
根据您的应用场景优化材料选择 - 预约演示
- 7交叉引用
- 6化学成分
- 6机械性能
- 21物理性能
- 2热处理
- -金相组织
- -切削加工性能
- -应力-应变
- -成形性能
- -疲劳
- -断裂
- -爬行
- -焊接接头
- -涂层
- -尺寸
- -摩擦学
- -腐蚀
- -老化
- -耐候性
- -辐照
- 9供应商总数